Supported tritonX100 polyaniline nano-porous electrically active film has been fabricated successfully onto indium-tin-oxide conducting probe using electrochemical polymerization process. The doping of TX-100 in the polymeric network of PANI was suggested using cyclic voltammeter, UV-vis spectroscopy, and Fourier Transform Infrared spectroscopy. The change in the surface morphology of PANI thin film due to incorporation of tritonX-100 was investigated using Atomic Forced Microscopy and porosity has been confirmed scanning electron microscopy, respectively. The surface morphology, uniformly disperse hexagonal close packing of TX-100 in PANI matrices due to the incorporation of TX-100 in polymeric network of PANI was confirmed by Atomic Force Microscopy. The electrical conductivity of PANI-TX-100 increases from 1.06 x 10<sup>-2</sup> S/cm<sup>-1</sup> to 4.95 x 10<sup>-2</sup> S/cm<sup>-1</sup> as the amount of TX-100 increases during the polymerization. The change in the morphology and electrical conductivity of PANI due to incorporation of TX-100 prove as a promising material for the sensing application.
KeywordsElectrochemical PolymerizationNon ionic surfactantConducting PolyanilineAtomic Force MicroscopyScanning Tunneling Microscopy.
H. Yamamaoto, M. Oshima, T. Hosaka and I. Isa, “Solid Electrolytic Capacitors Using an Aluminum Alloy Elec-trode and Conducting Polymers,” Synthetic Metals, Vol. 104, No. 1, 1999, pp. 33-38. doi:10.1016/S0379-6779(99)00003-X
K. S. Ryu, K. M. Kim, S. G. Kang, G. J. Lee, J. Joo and S. H. Chang, “Electrochemical and Physical Characteriza-tion of Lithium Ionic Salt Doped Polyaniline as a Poly-mer Electrode of Lithium Secondary Battery,” Synthetic Metals, Vol. 110, No. 3, 2000, pp. 213-217. doi:10.1016/S0379-6779(99)00288-X
A. Talei, J. Y. Lee, Y. K. Lee, J. Jang, J. A. Romagnoli, T. Taguchi and E. Maeder, “Dynamic Sensing Using Intel-ligent Composite: An Investigation to Development of New Ph Sensors and Electrochromic Devices,” Thin Solid Films, Vol. 363, No. 1-2, 2000, pp. 163-166. doi:10.1016/S0040-6090(99)00987-6
A. Kumar, D. M. Welsh, M. C. Morvant, F. Piroux, K. A. Abboud and J. R. Reynolds, “Conducting Poly (3,4-alkylenedioxythiophene) Derivatives as Fast Elec-trochromics with High-Contrast Ratios,” Chemistry of Materials, Vol. 10, No. 3, 1998, pp. 896-902. doi:10.1021/cm9706614
J. C. Scott, S. A. Carter, S. Karg and M. Angelopoulos, “Polymeric Anodes for Organic Light-Emitting Diodes,” Synthetic Metals, Vol. 85, No. 1-3, 1997, pp. 1197-1200. doi:10.1016/S0379-6779(97)80207-X
Y. T. Shin, S. W. Shin, J. Shin, K. Lee and M. Cha, “Pulsed Laser Deposition of a Thin Conjugated-Polymer Film,” Thin Solid Films, Vol. 360, No. 1-2, 2000, pp. 13-16. doi:10.1016/S0040-6090(99)00962-1
B. Wessling and J. Posdorfer, “Corrosion Prevention with an Organic Metal (polyaniline): Corrosion Test Results,” Electrochimica Acta, Vol. 44, No. 12, 1999, pp. 2139-2147. doi:10.1016/S0013-4686(98)00322-3
R. Khan and M. Dhayal, “Chitosan/Polyaniline Hybrid Conducting Biopolymer Base Impedimetric Immunosen-sor to Detect Ochratoxin-A,” Biosensors & Bioelectron-ics, Vol. 24, No. 6, 2009, pp. 1700-1705. doi:10.1016/j.bios.2008.08.046
A. A. Ansari, R. Khan, K. N. Sood and B. D. Malhotra, “Polyaniline-Cerium Oxide Nanocomposite for Hydrogen Peroxide Sensor,” Journal of Nanoscience & Nanotech-nology, Vol. 9, No. 8, 2009, pp. 4679-4685. doi:10.1166/jnn.2009.1085
A. Kaushik, R. Khan, V. Gupta, B. D. Malhotra and S. P. Singh, “Hybrid Cross Linked Polyaniline-WO3 Nano-composite Thin Films for NOx Gas Sensing,” Journal of Nanoscience & Nanotechnology, Vol. 9, 2009, pp. 1792-1796. doi:10.1166/jnn.2009.417
A. Kaushik, J. Kumar, M. K. Tiwari, R. Khan, B. D. Malhotra, V. Gupta and S. P. Singh, “Fabrication and Characterization of Polyaniline—ZnO Hybrid Nano-composite Thin Films,” Journal of Nanoscience & Nanotechnology, Vol. 8, No. 4, 2008, pp. 1757-1761. doi:10.1166/jnn.2008.006
B. Wesseling, “Electrical Properties of Pyrrole and Its Copolymers,” Synthetic Metals, Vol. 4, No. 2, 1991, pp. 119-130.
Y. Z. Zheng, K. Levon, T. Taka, J. Laasko and J. E. Osterholm, “Doping-induced Layered Structure in N-alkylated Polyanilines,” Polymer Journal, Vol. 28, No. 5, 1996, pp. 412-418. doi:10.1295/polymj.28.412
Y. Cao, P. Smith, A. J. Heeger, PCT, Patent Application WO 92/2291, Vol. 91, 1992.
Y. Xia, A. G. MacDiarmid and A. J. Epstein, “Camphorsulfonic Acid Fully Doped Polyaniline Emeraldine Salt: In situ Observation of Electronic and Conformational Changes Induced by Organic Vapors by an Ultraviolet/Visible/Near-Infrared Spectroscopic Method,” Macromolecules, Vol. 27, No. 24, 1994, pp. 7212-7214. doi:10.1021/ma00102a033
A. G. MacDiarmid and A. J. Epstein, “The Concept of Secondary Doping as Applied to Polyaniline,” Synthetic Metals, Vol. 65, 1994, pp. 103-116. doi:10.1016/0379-6779(94)90171-6
A. G. MacDiarmid, Y. N. Xia and J. M. Wiesinger, U.S. Patent 5, 773, 568 (1998).
A. G. MacDiarmid and A. J. Epstein, “Secondary Doping in Polyaniline” Synthetic Metals, Vol. 69, No. 1-3, 1995, pp. 85-92. doi:10.1016/0379-6779(94)02374-8
S. P. Armes and M. Aldissi, “Novel Colloidal Dispersons of Polyaniline,” Journal of the Chemical Society, Chemi-cal Communication, Vol. 2, 1989, pp. 88-89. doi:10.1039/c39890000088
N. Kohut-Svelko, S. Reynaud and J. Francois, “Synthesis and Characterization of Polyaniline Prepared in the Presence of Nonionic Surfactants in an aqueous dispersion,” Synthetic Metals, Vol. 150, No. 2, 2005, pp. 107-114. doi:10.1016/j.synthmet.2004.12.022
P. J. Kinlen, J. Liu, Y. Ding, C. R. Graham and E. E. Remsen, “Emulsion Polymerization Process for Organi-cally Soluble and Electrically Conducting Polyaniline,” Macromolecules, Vol. 31, No. 6, 1998, pp. 1735-1744. doi:10.1021/ma971430l
S. Palaniappan, “Preparation of Polyaniline-Sulfate Salt by Emulsion and Aqueous-Polymerization Pathway Without Using-Protonic Acid,” Polymers for Advanced Technologies, Vol. 13, No. 1, 2002, pp. 54-59. doi:10.1002/pat.154
H. Xia and Q. Wang, “Synthesis and Characterization of Conductive Polyaniline Nanoparticles Through Ul- trasonic Assisted Inverse Microemulsion Poly-me- rization,” Journal of Nanoparticle Research, Vol. 3, No. , 2001, pp. 401-441.
P. S. Rao, S. Subrahmanya and D. N. Sathyanarayana, “Inverse Emulsion Polymerization: A New Route For the Synthesis of Conducting Polyaniline,” Synthetic Metals, Vol. 128, No. 3, 2002, pp. 311-316. doi:10.1016/S0379-6779(02)00016-4
P.S. Rao, D.N. Sathyanarayana and S. Palaniappan, “Po-lymerization of Aniline in an Organic Peroxide System by the Inverted Emulsion Process,” Macromolecules, Vol. 35, No. 13, 2002, pp. 4988-4996. doi:10.1021/ma0114638
D. W. C. Andrew, E. A. O’ Rear and B. P. Grady, “Ad-sorbed Surfactants as Templates for the Synthesis of Morphologically Controlled Polyaniline and Polypyrrole Nanostructures on Flat Surfaces: From Spheres to Wires to Flat Films,” Journal of the American Chemical Society, Vol. 125, No. 48, 2003, pp. 14793-14800. doi:10.1021/ja0365983
J. P. Rabe, “Self-assembly of Single Macromolecules at Surfaces,” Current Opinion in Colloid & Interface Sci-ence, Vol. 3, No. 1, 1998, pp. 27-31. doi:10.1016/S1359-0294(98)80038-1
D. Ichinohe, T. Aria and H. Kise, “Synthesis of Soluble Polyaniline in Reversed Micellar Systems,” Synthetic Metals, Vol. 84, No. 1-3, 1997, pp. 75-76. doi:10.1016/S0379-6779(96)03843-X
D. Kim, J. Choi, J-Y Kim, Y-K Han and D. Sohn, “Size Control of Polyaniline Nanoparticle by Polymer Surfactant, Macromolecules, Vol. 35, No. 13, 2002, pp. 5314-5316. doi:10.1021/ma020162a
M. Omastova, M. Trchova, J. Kovarova and J. Stejskal, “Synthesis and Structural Study of Polypyrroles Prepared in the Presence of Surfactants,” Synthetic Metals, Vol. 138, No. 3, 2003, pp. 447-455. doi:10.1016/S0379-6779(02)00498-8
Z. Zhang, Z. Wei and M. Wan, “Nanostructures of Polyaniline Doped with Inorganic Acids,” Mcromo- lecules, Vol. 35, No. 15, 2002, pp. 5937-5942.
A. N. Galatanu, I. S. Chrorrakis, D. F. Anghel and A. Khan, “Ternary Phase Diagram of the Triton X-100/ Poly(acrylic acid)/Water System,” Langmuir, Vol. 16, No. 11, 2000, pp. 4922-4928. doi:10.1021/la991668y
R. J. Robson and E. A. Dennis, “The Size, Shape, and Hydration of Nonionic Surfactant Micelles Triton X-100,” The Journal of Physical Chemistry, Vol. 81, No. 11, 1977, pp. 1075-1077. doi:10.1021/j100526a010
C. Tanford, Y. Nozaki and M. F. Rhode, “Size and Shape of Globular Micelles Formed in Aqueous Solution by N-Alkyl Polyoxyethylene Ethers,” The Journal of Physi-cal Chemistry, Vol. 81, No. 18, 1977, pp. 1555-1560. doi:10.1021/j100531a007
A. A. Ribeiro and E. A. Dennis, “Proton Magnetic Reso-nance Relaxation Studies on The Structure of Mixed Mi-celles of Triton X-100 and Dimy- ristoylphosphatidyl-choline,” Biochemistry, Vol. 14, No. 17, 1975, pp. 3746-3755. doi:10.1021/bi00688a005
T. C. Girija and M. V. Sangarranarayanan, “Poly- aniline-Based Nickel Electrodes For Electrochemical Supercapacitors—Influence of Triton X-100,” Journal of Power Sources, Vol. 159, No. 2, 2006, pp. 1519-1526. doi:10.1016/j.jpowsour.2005.11.078
N. Arsalani, M. Khavei and A.A. Entezami, “Synthesis and Characterization of Novel NSubstituted Polyaniline by Triton X-100,” Iranian Polymer Journal, Vol. 12, No. 3, 2003, pp. 237-242.
L.T. Cai, S.B. Yao and S.M. Zhou, “Surfactant effects on the polyaniline film,” Synthetic Metals, Vol. 88, No. 3, 1997, pp. 209-212. doi:10.1016/S0379-6779(97)03852-6
K.R. Prasad and N. Munichandraiah, “Potentiodynamic Deposition of Polyaniline on Non-Platinum Metals and Characterization,” Synthetic Metals, Vol. 123, No. 3, 2001, pp. 459-468. doi:10.1016/S0379-6779(01)00334-4
J.C. Cooper and E.A.H. Hall, “Electrochemical Response of an Enzyme-Loaded Polyaniline Film,” Biosens & Bio-electronics, Vol. 7, No. 7, 1992, pp. 473-485.