Structural and Electrical Characterization of GaN Thin Films on Si(100)
- 1
- 2
- 3
Abstract
The Gallium Nitride (GaN) layers grown on silicon substrates by electron beam evaporation technique. X- ray diffraction revealed that polycrystalline GaN was obtained indicating the enhance crystallinity of the films with annealing temperature at 600<sup>o</sup>C. Crystalline quality of the GaN films was determined by Scanning Electron Microscopy (SEM). The crystalline size increases with increasing annealing temperature. The fab- ricated MIS structures were characterized using Capacitance-Voltage (C-V) measurements, the capacitance remains nearly constant over a large range in higher negative as well as over a large range in higher positive gate voltages and Current-Voltage (I-V) measurements shows low forward and reverse current possibly due to high density defect formation in the thin layer of gallium nitride during its growth.The film is characterized by X-Ray photoelectron spectroscopy (XPS). The XPS spectra show that formation of pure GaN with- out presence of elemental gallium and Ga<sub>2</sub>O<sub>3</sub> in this film.
- S. C. Jain, M. Willander, J. Narayan and R. Van Over- straeten, “III-Nitride: Growth, Characterisation and Pro- perties,” Journal of Applied Physics, Vol. 87, No. 3, 2000, pp. 965-1006. doi:10.1063/1.371971
- J. W. Yang, A. Lunev, G. Simin, A. Chitnis, M. Shatalov, M. A. Khan, J. E. Van Nostrand and R. Gaska, “Selec- tive Area Deposited Blue GaN-InGaN Multiple-Quantum Well Light Emitting Diodes over Silicon Substrates,” Ap- plied Physics Letters, Vol. 76, No. 3, 2000, pp. 273-275. doi:10.1063/1.125745
- A. Dadgar, J. Christen, T. Riemann, S. Richter, J. Blaesing, A. Diez, A. Krost, A. Alam and M. Heuken, “Formation of Thin GaN Layer on Si(111) for Fabrication of High Temperature Metal Field Effect Transistors,” Applied Physics Letters, Vol. 78, No. 15, 2001, p. 2211. doi:10.1063/1.1362327
- J. W. Yang, C. J. Sun, Q. Chen, M. Z. Anwar, M. A. Khan, S. A. Nikishin, G. A. Seryogin, A. V. Qsinsky, L. Chernyak, H. Temkin, C. Hu and S. Mahajan, “High Quality GaN-InGaN Heterostructures Grown on Si(111) Substrates,” Applied Physics Letters, Vol. 69, No. 23, 1996, pp. 3566-3568. doi:10.1063/1.117247
- N. P. Kobayashi, J. T. Kobayashi, P. D. Dapkus, W. J. Choi, A. E. Bond, X. Zhang and D. H. Rich, “GaN Growth on Si(111) Substrate Using Oxidized AlAs as an Intermediate Layer,” Applied Physics Letters, Vol. 71, No. 24, 1997, pp. 3569-3571. doi:10.1063/1.120394
- L. Wang, X. Liu, Y. Zan, J. Wang, D. Wang, D. Lu and Z. Wang, “Wurtzite GaN Epitaxial Growth on a Si(001) SubStrate Using γ-Al2O3 as an Intermediate Layer,” Applied Physics Letters, Vol. 72, No. 1, 1998, pp. 109-111. doi:10.1063/1.120660
- P. W. Deelmann, R. N. Bicknell-Tassius, S. Nikishin, V. Kuryatkov and H. Temkin, “Low-Noise GaN Schottky Diodes on Si(111) by Molecular Beam Epitaxy,” Applied Physics Letters, Vol. 78, No. 15, 2001, p. 2172. doi:10.1063/1.1357448
- Y. Hiroyama and M. Tamura, “Effect of Very Thin SiC Layer on Heteroepitaxial Growth of Cubic GaN on Si (001),” Japanese Journal of Applied Physics, Vol. 37, 1998, pp. 630-632. doi:10.1143/JJAP.37.L630
- L. T. Romano, J. E. Northrup and M. A. O’Keefe, “In- version Domains in GaN Grown on Sapphire,” Applied Physics Letters, Vol. 69, No. 16, 1996, pp. 2394-2396. doi:10.1063/1.117648
- C. Stampfl, J. Neugebauer and C. Van de Walle, “Dop- ing of AlxGa1-xN Alloys,” Material Science Engineer- ing, Vol. 59, 1999, pp. 253-257.
- C. Wang and R. F. Davis, “Deposition of Highly Resistive, Undoped, and P-Type, Magnesium-Doped Gallium Nitride Films by Modified Gas Source Molecular Beam Epitaxy,” Applied Physics Letters, Vol. 63, No. 7, 1993, pp. 990-992. doi:10.1063/1.109816