Structure and Properties of Sn-9Zn Lead-Free Solder Alloy with Heat Treatment
- 1
- 2
- 3
- 4
- 5
Abstract
The Sn-9Zn lead-free solder alloy was prepared by conventional casting technique then cold-rolled into long sheets of 1 mm thickness and 3 mm width. It was annealed at 80, 120 and 160°C for 60 min to investigate the effect of isochronal heat treatment on structure and mechanical properties of the cold rolled Sn-9Zn alloy. The results showed that, the crystallite size and lattice strain have opposite behavior with increasing annealing temperature due to recovery and recrystalization processes associated with the heat treatment process. Vickers micro-hardness number increases continuously from 155 to 180 MPa with increasing annealing temperature. Ultimate tensile strength (UTS) was also calculated. It was found that, it is equal to 61.4 MPa for the non annealed sample and slightly decreases to 60.5 and 58.2 MPa for samples annealed at 80 and 120°C, respectively. While, increases to 65.4 MPa for the sample annealed at 160°C. Also, ductility increases with increasing annealing temperature in opposite manor with the UTS. The new method for Micro-creep behavior as well as the creep rate calculated by this method has been characterized at room temperature.
- M. Kamal and E. S. Gouda, “Effect of rapid solidification on structure and properties of some lead-free solder alloy,” Materials and Manufacturing Processes, Vol. 21, pp. 736-740, 2006.
- E. S. Gouda, E. Ahmed and F. Saad Allah, “Electrical and mechanical properties of Sn-5wt.%Sb alloy with annealing temperature,” European Physical Journal: Applied Physics, Vol. 45, pp. 10901-10905, 2009.
- E. S. Gouda, “Effect of cooling rate on structure and creep behavior of Sn-0.7 Cu-0.5 Zn lead-free solder alloy,” European Physical Journal: Applied Physics, Vol. 48, pp. 20902-20906, 2009.
- R. Islam, B. Wu, M. Alam, Y. Chan and W. Jillek, “Investigations on microhardness of Sn-Zn based lead-free solder alloys as replacement of Sn-Pb solder,” Alloys and Compounds, Vol. 392, pp. 149-158, 2005.
- M. Kamal, M. Meikhail, A. Elbediwi and E. S. Gouda, “Study of structural changes and properties of Sn-9Zn lead free solder alloy with addition of different alloying elements,” Radiation Effects and Defects in Solids, Vol. 160, pp. 45-49, 2005.
- J. Zhao, L. Qi, X. Wang and L. Wang, “Influence of Bi on microstructures evolution and mechanical properties in Sn-Ag-Cu lead-free solder,” Alloys and Compounds, Vol. 375, pp. 196, 2004.
- M. Kamal and E. S. Gouda, “Enhancement of solder properties of Sn-9Zn lead-free solder alloy,” Crystal Research and Technology, Vol. 41, No. 12, pp. 1210-1213, 2006.
- C. M. Wu, D. Q. Yu, C. M. T. Law and L. Wang, “ The properties of Sn-9Zn lead-free solder alloys doped with trace rare earth elements,” Electronic Materials, Vol. 31, pp. 921-927, 2002.
- T. El-Ashram and R. Shalaby, “Effect of rapid solidification and small additions of Zn and Bi on structure and properties of Sn-Cu eutectic alloy,” Electronic Materials, Vol. 34, pp. 212-215, 2005.
- B. E. Warren, “X-Ray diffraction,” Addison Wesley, Reading, MA, 1969.
- M. Brown, “Introduction to thermal analysis,” Wiley, New York, pp. 33-35, 1986.
- W. Wendlandt, “Thermal analysis,” Wiley, New York, pp. 271-274, 1986.
- O. Uzuna, T. Karaaslan, M. Gogebakan and M. Keskin, “Hardness and microstructural characteristics of rapidly solidified Al-8-16 wt.%Si alloys,” Alloys and Compounds, Vol. 376, pp. 149, 2004.
- M. Kamal, E. S. Gouda and L. Marei, “Effect of Bi addition on hardness and micro creep behavior of Sn-3.5Ag rapidly solidified alloy,” Crystal Research and Technology, Vol. 44, No. 12, pp. 1308-1812, 2009.