Effect of Preheating Temperature on the Mechanical and Fracture Properties of Welded Pearlitic Rail Steels
- 1 Mechanical Engineering Department, Tuskegee University, Tuskegee, USA
- 2 Mechanical Engineering Department, Tuskegee University, Tuskegee, USA
- 3 Mechanical Engineering Department, Tuskegee University, Tuskegee, USA
- 4 Federal Railroad Administration, Washington DC, USA
Abstract
The effect of preheating temperature on the mechanical and fracture behavior, hardness, and the microstructure of slot welded pearlitic rail steel were studied. Railhead sections with slots were preheated to 200℃, 300℃, 350℃ and 400℃ before gas metal arc filling to simulate defects repair. Another sample, welded at room temperature (RT) with no preheat, was studied in comparison. The parent rail steel has ultimate strength, yield strength and strain to failure of 1146 MPa, 717 MPa and 9.3%, respectively. Optimum values of these properties for the welded rail steels were found to be 1023 MPa, 655 MPa and 4.7%, respectively, for the 200℃ preheat temperature. On this basis , the optimum weld efficiency was found to be 89.2%. The average apparent fracture toughness K I for the parent rail was 127 MPa.m 0.5 , while that for the optimum welded joint (200℃ preheat) was 116.5 MPa.m 0.5 . In addition, the average hardness values of the weld, fusion zone, and heat affected zone (HAZ) were 313.5, 332 and 313.6 HB, respectively, while that for parent rail steel was about 360 HB. Dominance of bainite and acicular ferrite phase in the weld mic rostructure was observed at 200℃ preheat.
- R. S. Funderburk, “Talking Your Weld’s Temperature,” Proceedings on North American Steel Construction Conference, Las Vegas, February 2000.
- BOC Library, AU: IPRM: 2007: Section 8: Consumable, pp. 326-329. http://www.bocworldofwelding.com.au/media/pdf/file/library/WOWLibrary-Preheating%20of%20materials-Consumables.pdf
- T. Kasuya and N. Yuriok, “Determination of Necessary Preheat Temperature to Avoid Cold Cracking under Varying Ambient Temperature,” ISIJ International, Vol. 35, No. 10, 1995, pp. 1183-1189. http://dx.doi.org/10.2355/isijinternational.35.1183
- L. Baughurst and G. Voznaks: “Welding Defects, Causes and Correction,” Australian Bulk Handling Review, 2009. http://www.bulkhandling.com.au/pdfs/26-28.pdf
- R. W. Hinton and R. K. Wiswesser: “Estimating Welding Preheat Requirements for Unknown Grades of Carbon and Low Alloy Steels,” Welding Journal, Vol. 87, 2008, pp. 273-278.
- S. Kou, “Welding Metallurgy,” 2nd Edition, John Wiley & Sons, Inc., Hoboken, 2003, pp. 232-239.
- H. K. D. H. Bhadeshia, “Reliability of Weld Microstructure and Property Calculations,” Welding Journal, Vol. 8, No. 9, 2004, pp. 237-243.
- W. W. Bose-Filho, A. L. M. Carvalho and M. Strangwood, “Effects of Alloying Elements on the Microstructure and Inclusion Formation in HSLA Multipass Welds,” Materials Characterization., Vol. 58, No. 1, 2007, pp. 29-39. http://dx.doi.org/10.1016/j.matchar.2006.03.004
- H. K. D. H. Bhadeshia, “The Microstructure of Submerged Arc-Weld Deposits for High-Strength Steels,” Journal of Materials Science, Vol. 24, No. 9, 1989, pp. 3180-3188. http://dx.doi.org/10.1007/BF01139039
- Y. Shia and Z. Han, “Effect of Weld Thermal Cycle on Microstructure and Fracture Toughness of Simulated Heat-Affected Zone for a 822 MPa Grade High Strength Low Alloy Steel,” Journal of Materials Processing Technology, Vol. 207, No. 1-3, 2008, pp. 30-39. http://dx.doi.org/10.1016/j.jmatprotec.2007.12.049
- R. S. Funderburk, “A Look at Heat Input,” Welding Innovation, Vol. 16, No. 1, 1999, pp. 8-11.
- E. M. El-Banna: “Effect of Preheat on Welding of Ductile Cast Iron,” Materials Letters, Vol. 41, No. 1, 1999, pp. 20-26. http://dx.doi.org/10.1016/S0167-577X(99)00098-1
- L. H. Hu, J. Huang, Z. G. Li and Y. X. Wu, “Effects of Preheating Temperature on Cold Cracks, Microstructures and Properties of High Power Laser Hybrid Welded 10Ni3CrMoV Steel,” Materials & Design, Vol. 32, 2011, pp. 1931-1939.