Making Ferronickel from Laterite Nickel Ore by Coal-Based Self-Reduction and High Temperature Melting Process

Abstract

Based on the process of coal-based self-reduction and melting separation at high temperature, it was investigated that the effect of process factors on the reduction of iron and nickel oxide, the metal yield and the nickel content in ferronickel about the laterite nickel ore, was from Philippines and contented low nickel, high iron and aluminum. The results showed that if the C/O mole ratio was not higher than 0.5 and the reduction temperature was kept as 1200°C and then increased up to 1500°C, the metal could not separate from molten slag for the A series of experiments, which were only added CaF₂. However, when the C/O ratio was added up to 0.6 - 0.8, the metal could separate well from the slag, and the yields of Fe and Ni increased gradually. But the nickel content in the metal declined from 1.79% to 1.34%. When the C/O ratio increased to 1.2, and the temperature of melting products obtained at 1200°C and rose to 1550°C, the separation of metal from slag could not be realized in B group of tests, which were only added hydrated lime. However, when both of CaF₂ and hydrated lime were added, the metal could separate from slag in C group. In order to increase the content of nickel in the metal, it is necessary to restrain the reduction of iron oxide. When the C/O mole ratio is 0.6, the nickel content of metal could be 1.79%, which was higher than the theoretical ratio 1.65% of Ni/(Ni + Fe) of the latcritic nickel ore, but the yield of nickle was only 71.3%.