The purpose of this research was to study the effect of Argon inert gas on the laser welding quality of Co-Cr and Ni-Cr base metal alloys, which are widely used as Fixed Prosthodontics alloys in Dental Laboratories. A total of 36 specimens were manufactured (18 of Ni-Cr alloy and 18 of Co-Cr alloy). The specimens were then divided into 3 subgroups (6 specimens each): control; argon-welded; and non-Argon welded. The specimens were cut, laser welded, radiographed and finally tested under tensile strength testing, followed by examination using Scanning Electron Microscopy. The tensile strength of welded specimens was lower than the strength of non-welded specimens, however this difference was not found to be statistically significant. The material factor (Co-Cr alloy or Ni-Cr alloy) has a statistically significant effect on the tensile strength, while the presence or not of the inert gas, as well as the combination of the two factors do not have a statistically significant effect. The laser welding process applied in daily practice (separation of specimen, formation of two cones in contact, aggregation of two cones, filling of the remaining gap by welding) is considered satisfactory in terms of weld strength. The factor of the material, as an independent factor, affects the tensile strength to a statistically significant degree, in contrast to the factor of the presence of inert gas which does not affect to a statistically significant degree.
Hero, H., Syverud, M., Gjonnes, J. and Horst, J.A. (1984) Ductility and Structure of Some Cobalt-Base Dental Casting Alloys. Biomat, 5, 201-208. https://doi.org/10.1016/0142-9612(84)90016-4
Asgar, K. and Peyton, F.A. (1961) Effect of Microstructure on the Physical Properties of Cobalt-Base Alloys. Journal of Dental Research, 40, 63-72. https://doi.org/10.1177/00220345610400012501
Asgar, K. and Peyton, F.A. (1961) Effect of Casting Conditions on Some Mechanical Properties of Cobalt-Base Alloys. Journal of Dental Research, 40, 73-86. https://doi.org/10.1177/00220345610400012601
Brown, D., Braden, M., Miller, M., Causton, B.E., Prosser, H.J., Combe, E.C., et al. (1981) Dental Materials, 1979 Literature Review Part I. Journal of Dentistry, 9, 177-209. https://doi.org/10.1016/0300-5712(81)90056-7
Nikellis, I., Levi, A. and Zinelis, S. (2005) Effect of Soldering on the Metal-Ceramic Bond Strength of an Ni-Cr Base Alloy. Journal of Prosthetic Dentistry, 94, 435-439. https://doi.org/10.1016/j.prosdent.2005.09.012
Angelini, E., Bonino, P. and Pezzoli, M. (1988) Corrosion Resistance of Solder Joints for Removable Partial Dentures. Dental Materials, 4, 255-260. https://doi.org/10.1016/S0109-5641(88)80019-8
Gordon, T.E. and Smith, D.L. (1970) Laser Welding of Prostheses—An Initial Report. Journal of Prosthetic Dentistry, 24, 472-476. https://doi.org/10.1016/0022-3913(70)90087-9
da Silva Barbosa, J., de Lima, E.D., de Melo, J.B.C.A., Batista, A.U.D., Neto, J.P.S. and da Silva, H.F.V. (2021) Fractographic Analysis of Two Fractured Removable Partial Denture Metal Frameworks. Research, Society and Development, 10, 1-9. https://doi.org/10.33448/rsd-v10i10.18370
Kelly, J.R. and Rose, T.C. (1983) Nonprecious Alloys for Use in Fixed Prosthodontics, a Literature Review. Journal of Prosthetic Dentistry, 49, 363-370. https://doi.org/10.1016/0022-3913(83)90279-2
Wataha, J.C. (2002) Alloys for Prosthodontic Restorations. Journal of Prosthetic Dentistry, 87, 351-363. https://doi.org/10.1067/mpr.2002.123817
Tartari, A., Clark, R.K.F., Juszczyk, A.S. and Radford, D.R. (2010) Tensile Strength of Laser Welded Cobalt-Chromium Alloy with and without an Argon Atmosphere. European Journal of Prosthodontics and Restorative Dentistry, 18, 60-65.
Bertrard, C., Le Petitcorps, Y., Albingre, L. and Dupuis, V. (2001) The Laser Welding Technique Applied to the Non Precious Dental Alloys Procedure and Results. British Dental Journal, 190, 255-257. https://doi.org/10.1038/sj.bdj.4800942a
Pop, D., Negrutiu, M., Sinescu, C., Demian, C., Todea, C., Rominu, M. and Balabuc, C. (2007) Different Types of Laser Welding in Dental Technology. TMJ, 57, 184-186.
NaBadalung, D.P. and Nicholls, J.I. (1998) Laser Welding of a Cobalt-Chromium Removable Partial Denture Alloy. Journal of Prosthetic Dentistry, 79, 285-290. https://doi.org/10.1016/S0022-3913(98)70239-2
Lee, J.H., Choi, S.K. and Hong, M.H. (2015) The Metallurgical Characteristics of Non-Precious Alloys Using Nd, YAG Laser Welding. BioMed Research, 19, 1-10. https://doi.org/10.1186/s40824-015-0047-x
Watanabe, I. and Topham, D.S. (2006) Laser Welding of Cast Titanium and Dental Alloys Using Argon Shielding. Journal of Prosthodontics, 15, 102-107. https://doi.org/10.1111/j.1532-849X.2006.00082.x
Rezaei, S.M., Heidarifar, H., Arezodar, F., Azary, A. and Mokhtaryhoee, S. (2011) Influence of Connector Width on the Stress Distribution of Posterior Bridges Under Loading. Journal of Dentistry, 8, 67-74.
Reimann, L., Zmudzski, J. and Dobranski, L.A. (2015) Strength Analysis of a Three-Unit Dental Bridge Framework with the Finite Element Method. Acta of Bioengineering and Biomechanics, 17, 51-59.
Morris, H.F., Asgar, K., Rowe, A.P. and Nasjleti, C.E. (1979) The Influence of Heat Treatments on Several Types of Base-Metal Removable Partial Denture Alloys. Journal of Prosthetic Dentistry, 41, 388-395. https://doi.org/10.1016/0022-3913(79)90034-9
Dharmar, S., Rathnasamy, R.J. and Swaminathan, T.N. (1993) Radiographic and Metallographic Evaluation of Porosity Defects and Grain Structure of Cast Chromium Cobalt Removable Partial Dentures. Journal of Prosthetic Dentistry, 69, 369-373. https://doi.org/10.1016/0022-3913(93)90182-N
Lewis, A.J. (1978) Radiographic Evaluation of Porosities in Removable Partial Denture Castings. Journal of Prosthetic Dentistry, 39, 278-281. https://doi.org/10.1016/S0022-3913(78)80095-X
Lewis, A.J. (1978) Failure of Removable Partial Denture Castings during Service. Journal of Prosthetic Dentistry, 39, 147-149. https://doi.org/10.1016/S0022-3913(78)80011-0
Van Noort, R. and Lamb, D.J. (1984) A Scanning Electron Microscope Study of Co-Cr Partial Dentures Fractured in Service. Journal of Dentistry, 12, 122-126. https://doi.org/10.1016/0300-5712(84)90045-9
Elarbi, E.A., Ismail, Y.H., Azarbal, M. and Saini, T.S. (1985) Radiographic Detection of Porosities in Removable Partial Denture Castings. Journal of Prosthetic Dentistry, 54, 674-677. https://doi.org/10.1016/0022-3913(85)90248-3
Lewis, A.J. (1975) Microporosity in Casting Alloys. Australian Dental Journal, 20, 161-166. https://doi.org/10.1111/j.1834-7819.1975.tb04361.x
Eisenburger, M. and Addy, M. (2002) Radiological Examination of Dental Castings—A Review of the Method and Comparisons of the Equipment. Journal of Oral Rehabilitation, 29, 609-614. https://doi.org/10.1046/j.1365-2842.2002.00938.x
Wictorin, L., Julin, P. and Mollersten, L. (1979) Roentgenological Detection of Casting Defects in Cobalt-Chromium Alloy Frameworks. Journal of Oral Rehabilitation, 6, 137-146. https://doi.org/10.1111/j.1365-2842.1979.tb01273.x
Morris, H., Farah, J.W., Craig, R.G. and Hood, J.A. (1976) Stress Distribution within Circumferential Clasp Arms. Journal of Oral Rehabilitation, 3, 387-394. https://doi.org/10.1111/j.1365-2842.1976.tb01453.x
Srimaneepong, V., Yoneyama, T., Kobayashi, E., Doi, H. and Hanawa, T. (2008) Comparative Study on Torsional Strength, Ductility and Fracture Characteristics of Laser-Welded α + β Ti-6Al-7Nb Alloy, CP Titanium and Co-Cr Alloy Dental Castings. Dental Materials, 24, 839-845. https://doi.org/10.1016/j.dental.2007.10.002
Zupancic, R., Legat, A. and Funduk, N. (2006) Tensile Strength and Corrosion Resistance of Brazed and Laser-Welded Cobalt-Chromium Alloy Joints. Journal of Prosthetic Dentistry, 96, 273-282. https://doi.org/10.1016/j.prosdent.2006.08.006
Bertrand, C., Le Petitcorps, Y., Albingre, L. and Dupuis, V. (2001) The Laser Welding Technique Applied to the Non Precious Dental Alloys Procedure and Results. British Dental Journal, 190, 255-257. https://doi.org/10.1038/sj.bdj.4800942
Asgar, K. and Allan, F.C. (1968) Microstructure and Physical Properties of Alloys for Partial Denture Castings. Journal of Dental Research, 47, 189-197. https://doi.org/10.1177/00220345680470020201
Baba, N., Watanabe, I., Liu, J. and Atsuta, M. (2004) Mechanical Strength of Laser-Welded Cobalt-Chromium Alloy. Journal of Biomedical Materials Research, 69, 121-124. https://doi.org/10.1002/jbm.b.10082
Han, S.K. and Margolin, H. (1989) Void Formation, Void Growth and Tensile Fracture of Plain Carbon Steel and a Dual-Phase Steel. Materials Science and Engineering A, 112, 133-141. https://doi.org/10.1016/0921-5093(89)90352-3
Bertrand, C., Le Petitcorps, Y., Albingre, L. and Dupuis, V. (2004) Optimization of Operator and Physical Parameters for Laser Welding of Dental Materials. British Dental Journal, 196, 413-418. https://doi.org/10.1038/sj.bdj.4811138
Luthy, H., Marinello, C.P., Reclaru, L. and Scharer, P. (1996) Corrosion Considerations in the Brazing Repair of Cobalt-Based Partial Dentures. Journal of Prosthetic Dentistry, 75, 515-524. https://doi.org/10.1016/S0022-3913(96)90456-4
Kokolis, J., Chakmakchi, M., Theocharopoulos, A., Prombonas, A. and Zinelis, S. (2015) Mechanical and Interfacial Characterization of Laser Welded Co-Cr Alloy with Different Joint Configurations. The Journal of Advanced Prosthodontics, 7, 39-46. https://doi.org/10.4047/jap.2015.7.1.39
Al Jabbari, Y.S., Koutsoukis, T., Barmpagadaki, X., El-Danaf Ehab, A., Fournelle, R.A. and Zinelis, S. (2015) Effect of Nd, YAG Laser Parameters on the Netration Depth of a Representative Ni-Cr Dental Casting Alloy. Journal of Lasers in Medical Sciences, 30, 909-914. https://doi.org/10.1007/s10103-013-1502-3