A PQAS-containing glass-ionomer cement for improved antibacterial function
- 1
- 2
- 3
- 4
- 5
Abstract
The novel non-leachable poly (quaternary ammonium salt) (PQAS)-containing antibacterial glass- ionomer cement has been developed. Compressive strength (CS) and S. mutans viability were used as tools for strength and antibacterial activity evaluations, respectively. All the specimens were conditioned in distilled water at 37?C prior to testing. Commercial glass-ionomer cement Fuji II LC was used as control. With PQAS addition, the studied cements showed a reduction in CS with 25-95% for Fuji II LC and 13-78% for the experimental cement and a reduction in S. mutans viability with 40-79% for Fuji II LC and 40-91% for the experimental cement. The experimental cement showed less CS reduction and higher antibacterial activity as compared to Fuji II LC. The long-term aging study indicates that the cements are permanently antibacterial with no PQAS leaching. It appears that the experimental cement is a clinically attractive dental restorative that can be potentially used for long- lasting restorations due to its high mechanical strength and permanent antibacterial function.
- Mjor, I.A., Dahl, J.E. and Moorhead, J.E. (2002) Placement and replacement of restorations in primary teeth. Acta Odontologica Scandinavica, 60(1), 25-28.
- Forss, H. and Widstrom, E. (2004) Reasons for restorative therapy and longevity of restorations in adults. Acta Odontologica Scandinavica, 62(2), 82-86.
- Manhart, J., Godoy, F.G. and Hickel, R. (2002) Direct posterior restorations: clinical results and new developments. Dental Clinics of North America, 46(2), 303-339.
- Deligeorgi, V., Mjor, I.A. and Wilson, N.H. (2001) An overview of reasons for the placement and replacement of restorations. Primary Dental Care: Journal of the Faculty of General Dental Practitioners, 8(1), 5-11.
- Craig, R.G. and Power, J.M. (2002) Restorative dental materials. 11th Edition, Mosby-Year Book, Inc., St. Louis.
- Wiegand, A., Buchalla, W. and Attin, T. (2007) Review on fluoride-releasing restorative materials—Fluoride release and uptake characteristics, antibacterial activity and influence on caries formation. Dental Materials, 23(3), 343-362.
- Osinaga, P.W., Grande, R.H., Ballester, R.Y., Simionato, M.R., Rodrigues, C.R.D. and Muench, A. (2003) Zinc sulfate addition to glass-ionomer-based cements: Influence on physical and antibacterial properties, zinc and fluoride release. Dental Materials, 19(3), 212-217.
- Takahashi, Y., Imazato, S., Kaneshiro, A.V., Ebisu, S., Frencken, J.E. and Tay, F.R. (2006) Antibacterial effects and physical properties of glass-ionomer cements containing chlorhexidine for the ART approach. Dental Materials, 22(7), 647-652.
- Yamamoto, K., Ohashi, S., Aono, M., Kokybu, T., Yamada, I. and Yamauchi, J. (1996) Antibacterial activity of silver ions implanted in SiO2 filler on oral streptococci. Dental Materials, 12(4), 227-229.
- Syafiuddin, T., Hisamitsu, H., Toko, T., Igarashi, T., Goto, N., Fujishima, A. and Miyazaki, T. (1997) In vitro inhibition of caries around a resin composite restoration containing antibacterial filler. Biomaterials, 18(15), 1051- 1057.
- Gottenbos, B., Mei, H.C., Klatter, F., Nieuwenhuis, P. and Busscher, H.J. (2002) In vitro and in vivo antimicrobial activity of covalently coupled quaternary ammonium silane coatings on silicone rubber. Biomaterials, 23(6), 1417-1423.
- Thebault, P., Givenchy, E.T., Levy, R., Vandenberghe, Y., Guittard, F. and Geribaldi, S. (2009) Preparation and antimicrobial behavior of quaternary ammonium thiol derivatives able to be grafted on metal surfaces. European Journal of Medicinal Chemistry, 44(2), 717-724.