Crystal Growth and Nucleation in Glasses in the Lithium Silicate System

Abstract

The crystal growth and nucleation in glasses in the lithium silicate system have been investigated. Phase separation in ultimately homogenized glasses of the lithium silicate system xLi 2 O · (100 ﹣ x)SiO 2 (where x = 23.4, 26.0, 29.1, and 33.5 mol% Li 2 O) has been studied. The glasses of these compositions have been homogenized using the previously established special temperature-time conditions, which make it possible to provide a maximum dehydration and removal of bubbles from the glass melt. The parameters of nucleation and growth of phase separated in homogeneities and homogeneous crystal nucleation have been determined. The absolute values of the stationary nucleation rates I st of lithium disilicate crystals in the 23.4Li 2 O · 76.6SiO 2 , 26Li 2 O · 74SiO 2 and 29.1Li 2 O · 70.9SiO 2 glasses with the compositions lying in the metastable phase separation region have been compared with the corresponding rates I st for the glass of the stoichiometric lithium disilicate composition 33.51Li 2 O · 66.5SiO 2 . It has been found that the crystal growth rate has a tendency toward a monotonic increase with an increase in the temperature, whereas the dependences of the crystal growth rate on the time of low temperature heat treatment exhibit an oscillatory behavior with a monotonic decrease in the absolute value of oscillations. The character of crystallization in glasses with the compositions lying in the phase separation region of the Li 2 O-SiO 2 system is compared with that in the glass of the stoichiometric lithium disilicate composition. The conclusion has been made that the phase separation weakly affects the nucleation parameters of the lithium disilicate and has a strong effect on the crystal growth.