Cathodoluminescence (CL) Microscopy Application to Refractories and Slags
- 1 University of Missouri-Rolla Department of Ceramic Engineering Rolla, MO 65401
- 2 University of Missouri-Rolla Department of Ceramic Engineering Rolla, MO 65401
Abstract
Refractories are ceramic materials possessing high thermal shock properties and slag corrosion resistance, as well as creep resistance at high temperatures. They are used in large quantities in steel making furnaces, metal smelting vessels, and glass melting tanks, and are made from very refractory minerals such as lime, periclase, corundum, spinel, and zirconia. Slags are residual vitreous materials generated during steel refining processes. They cover a wide range of compositions and may contain pure oxides, silicates, and sulfides as well as fluoride phases, depending on the melting and smelting processes. These minerals exhibit spectacular cathodoluminescence color when bombarded with electrons. Cathodoluminescence (CL) microscopy, therefore, is a very effective technique for the characterization of refractory corrosion by slags. Studies in this paper include: (1) reaction of fluorine containing mold slags with ZrO 2 -C nozzle refractories, promoting crystallization of cuspidine [Ca 4 Si 2 O 7 (F,OH) 2 ], (2) corrosion of fusion cast refractories and formation of glass defects in TV panel glassmaking furnaces, and (3) densification of spinel-based castable in steel melting induction furnace.
- Lee, W. E. and Moore, R. E., 1998, "Evolution of in Situ Refractories in the 20th Century," Journal of American Ceramic Society, Vol. 81, No. 6, pp. 1385-1410.
- Lee, W. E. and Rainforth, W. M., 1994, Ceramic Microstructures: Property, Control by Processing. Chapman and Hall, London, UK.
- Refractories Handbook, The Technical Association of Refractories, Japan, 1998.
- Semler, C., 2000, U. S. Demand for Refractories to Reach $2.8 Billion Through 2003, Ceramic Industry, Vol. 150, No. 9, pp.45-46.
- Seward, T. P., 1997, Some aspect of oxy- fuel glass melting, Glass Technology, Vol. 38, No. 5, pp. 150-151.
- Crites, M. D., Karakus, M., Schlesinger, M. E., Somerville, M. A., and Sun, S., 2000a, "Interaction of Chrome-Free Refractories with Copper Smelting and Converting Slags," Canadian Metallurgical Quarterly, Vol. 39, No. 2, pp. 129-134.
- Crites, M. D., Karakus, M., Schlesinger, M. E., Somerville, M. A., and Sun, S., 2000b, "Refractory Interaction with Calcium Ferrite Slags," Interceram, Vol. 49, No. 2, pp. 88-91.
- Schlesinger, M. E., Karakus, M., Crites, M. D., Sommerville, M. A., and Sun, S., 1997, "Chrome-Free Refractories for Copper Production Furnaces," UNITECR'97, Proceedings of Unified International Technical Conference on Refractories, M. A. Stett, editor, American Ceramic Society, Westerville, pp. 1703-1709.
- Karakus, M., Smith, J. D., and Moore, R. E., 2000a, "Cathodoluminescence Mineralogy of Used MgO-C Bricks in Basic Oxygen Furnaces," Veitsch-Radex Rundschau, 1/2000, pp. 24-32.
- Wereszczak, A, Wang, H., Karakus, M., Curtis, W., Aume, V., and VerDow, D., 2000, "Postmortem Analyses of Salvaged Conventional Silica Bricks from Glass Production Furnaces," Glass Science and Technology (Glasstechnische Berichte), Vol. 73, No. 6, pp. 165-174.
- R. E. Moore, M. Velez, M. Karakus, W. L. Headrick, "Oxyfuel Firing Effects on Refractories," in Fundamentals of Refractory Technology, pp. 223-233, edited by J. P. Bennett and J. D. Smith, Ceramic Transactions, Vol. 125, The American Ceramic Society, Westerville, Ohio, 2001.
- Karakus, M. and Moore, R. E., 1998, "Seeking Solution to Glass Defects from Refractory Corrosion," The Glass Researcher, Bulletin of Glass Science and Engineering, Vol. 7, No. 2, pp. 13-14, 17.
- Karakus, M. and Moore, R. E., 1996b, " Post-Mortem Study of Glass Melting Furnace Refractories," Corrosion of Materials by Molten Glass, Ceramic Transactions, Vol. 78, G. A. Pecoraro, J. C. Marra, and J. T. Wenzel, eds., American Ceramic Society, Westerville, pp. 179-191.