Corrosion Behavior of Tin-Plated Carbon Steel and Aluminum in NaCl Solutions Using Electrochemical Impedance Spectroscopy
- 1 Department of Electrical Engineering Tuskegee University, Tuskegee, AL 36088, USA
- 2 Environmental Engineering Program, Department of Chemical Engineering Tuskegee University, Tuskegee, AL 36088, USA
- 3 Department of Electrical Engineering Tuskegee University, Tuskegee, AL 36088, USA
- 4 Department of Electrical Engineering Tuskegee University, Tuskegee, AL 36088, USA
Abstract
The corrosion behavior of both tin-plated carbon steel and aluminum (Al 1100) in NaCl solutions were studied using electrochemical impedance spectroscopy (EIS). The study objectives were to compare their corrosion behavior in concentrated brine solution, establish the equivalent electrical circuit diagrams of their corrosion phenomena, and consequently develop steady-state corrosion models for estimating the corrosion rates in the given solution. The steady-state corrosion rates for the tin-plated carbon steel increased significantly when the concentration of NaCl was increased from 1.0M to 1.5M. The increase in corrosion rate of the tin-plated steel is attributed to reduced charge transfer resistance due to the breakdown of the surface tin plating at high chloride concentrations. In contrast, there was little incremental change in the corrosion rates of aluminum when the NaCl concentration was increased from 1.0M to 1.5M. This is attributed to the known formation of a stable, passivating surface oxide film on aluminum which inhibits corrosion. The surface passivating film did not show any significant evidence of degradation with increase in chloride concentration. Using MATHLAB and the experimental corrosion rate data, a mathematical corrosion model was derived for the two samples to describe their steady-state corrosion in NaCl electrolyte solutions.
- Cottis, R. and Turgoose, S.. 1999. Electrochemical Impedance and Noise. Corrosion Testing Made Easy, (Syrett, B.C, Series Editor), NACE International, Houston, TX, 1999.
- Nigam, A.K., Balasubramaniam, R., Bhargava, S. and Baligidad, R.G. 2006. Electrochemical Impedance Spectroscopy and Cyclic Voltametry Study of carbon-Alloyed Iron Aluminides in Sulfuric Acid. Corrosion Science, 48, 1666-1678.
- J. Suay, E. Gimenez, T. Rodriguez, K.Habbib and J.J. Saura. 2003. Characterization of anodized and sealed aluminum by EIS. Corrosion Science, 45, 611-624.
- P. Yadav, A. Nishikata and T. Tsuru. 2004. Electrochemical impedance study on galvanized steel corrosion under cyclic wet-dry conditions-influence of time of wetness, Corrosion Science,46. 169-181.
- Soprano, M., Bennardo, A., and Gabetta, G. (1998). EIS Measurements on Burried Pipelines Cathodically Protected. Corrosion 98, paper #618, NACE International, Houston, TX., pp.618/1-618/14.
- Buchheit, R.G., Montes, L.P., Maestas, L.M., and Hinkebein, T.E. (1998). Corrosion Monitoring of Concrete-Lined Brine Service pipelines Using AC and DC Electrochemical Methods. Corrosion 98, paper #81, NACE International, Houston, TX., pp. 81/1-81/12.
- Wake, R. and Ezure, K (1991). Thinly Tin Coated Steel Sheets Having Excellent rust Resistance and weldability. US Patent # 4999258.
- Odegard, C. and Bronson, A. (1998). Evaluation of Pitting Corrosion with EIS for Alumina/Aluminum alloy Composites. Corrosion 98, paper #319, NACE International, Houston,TX., pp. 319/1-319/16.
- Umebayashi, R., Akao, N., Hara, N. and Sugomoto, K. (2003). Corrosion and Electrochemical Properties of Sn-8% Zn Alloy-Coated Steel in Methanol Containing Water,NaCl, and HCOOH. Journal of the Electrochemical Society, 150 (7), B295-B305.
- Masadeh, S. (2005). Electrochemical impedance spectroscopy of Epoxy-Coated Steel exposed to dead Sea Water. Journal of Minerals & Materials Characterization & Engineering, 4(2), 75-84.
- Barranco, V., Feliu, S. Jr., and Feliu, S. (2004). EIS Study of the Corrosion Behaviour of Zinc-based Coatings on Steel in Quiescent 3% Nacl Solution. Part 1: Directly Exposed Coatings. Corrosion Science, 46, 2203-2220.
- Tait, W.S. (1994). An Introduction to Electrochemical Corrosion Testing for Practicing Engineers and Scientists, PairODocs Publishers, Racine, Wisconsin 1994.