Corrosion Behavior of 18/8 Stainless Steel and Nickel-Plated Low Carbon Steel in Cassava Fluid
- 1 Mechanical Engineering Department,University of Ibadan, Nigeria
- 2 Materials Science and Engineering Department,Obafemi Awolowo University, Nigeria
- 3 Materials Science and Engineering Department,Obafemi Awolowo University, Nigeria
- 4 Materials Science and Engineering Department,Obafemi Awolowo University, Nigeria
Abstract
This research work investigated the corrosion resistance of nickel- plated medium carbon steel and 18/8 stainless steel in cassava fluid (i.e. containing hydrogen cyanide). It simulated the effect of continuous use of the materials in a cyanide environment where corrosion products are left in place. Low carbon steel sample was nickel electroplated at 4V for 35 minutes. The plated sample, the unplated and the 18/8 stainless steel were then subjected to a cassava fluid environment for thirty days. The electrode potentials, in mV (SCE), were measured every day. Weight loss was determined at intervals of 5 days for duration of the exposure period. The result showed little corrosion attack on the nickel-plated steel on the fifth and tenth days which quickly dropped to zero by the 15 th day and remained at the passive state till the 20 th day when corrosion picked up again increasing steadily, linearly until the end of the test day. Corrosion of the 18/8 stainless steel was very low as well decreasing till the last day of the test. The pH of the cassava solution which initially was acidic because of the cyanide content in the cassava was observed to progress to neutrality within five days and to alkalinity at the end of the thirty days test (because of corrosion product contamination of the cyanide). Un-plated steel was found to be unsuitable for the fabrication of cassava processing machinery because of the very high corrosion rate. 18/8 stainless steel was found suitable for use in this environment. The renewed corrosion activity on nickel plated steel after the 20 th day (pH=12) of continuous use in cyanide environment makes it unsuitable for use.
- Adebiyi, K.A, Hammed, K.A, and Ajayi, E. O. (2003). Predictive model for evaluating corrosion rate of mild steel in six environments, LAUTECH Journal of Engineering and Technology. In Jekayinfa, S.O.(Eds),Effect of cassava fluid on corrosion performance of mild steel,Vol 52, No.5,pp.286-292.
- Jekayinfa S.O., Waheed M.A., Adebiyi K.A. and Adebiyi F.T. (2005); Effect of cassava fluid on corrosion performance of mild steel. Anti-Corrosion Methods and Materials, Volume 52, No. 5,pp.286-292.
- O.O. Oluwole, D.T. Oloruntoba and O. Awheme(2008)"Effect of zinc plating of low carbon steel on corrosion resistance in cocoa fluid environment" Materials and Design, Elsevier,29(6),1266-1274.
- O.O. Oluwole, D.T. Oloruntoba and O. Awheme(2008)"Effect of zinc plating of low carbon steel on corrosion resistance in cassava fluid environment” Corrosion Engineering Science and Technology, Institute of Materials, Minerals and Mining, UK,43(4),320-323.
- George Di Bari (1994): Nickel Plating, Surface Engineering, ASM International, Materials Park ASM Handbook, OH 44073 Volume 5, p 201.
- Oluwole.O.O , Oloruntoba D.T,and Ibironke.D.E(2007) ‘Effectiveness Of Nickel Coating On Manganese Steel In Seawater Environment’ Continuing Research
- Hibbert D.B. and JamesA.M.(1984); Dictionary of Electrochemistry, Macmillan Press, London.
- Kakani.S.L and Kakani.A(2004) ‘Materials Science’ New Age International Ltd., New Delhi., p. 381-383.
- Loto C.A. and Adesomo M.A. (1988); The corrosion of mild steel in maize juice, acidified maize juice and acetic acid environment, African Journal of Science and Technology Series A, Vol.7 No.1.