Study of Electroslag Remelted and Nitrogen Containing High Speed Tool Steel M41
- 1 Physics department, Faculty of Science, Al-Azhar University, Nasr City, Cairo, Egypt.
- 2 Steel Technology Department, Central Metallurgical Research and Development Institute (CMRDI), Cairo, Egypt
- 3 Steel Technology Department, Central Metallurgical Research and Development Institute (CMRDI), Cairo, Egypt
- 4 Physics department, Faculty of Science, Al-Azhar University, Nasr City, Cairo, Egypt.
Abstract
Mossbauer Effect (ME) spectra, microstructure and hardness of some alloyed and conventional AISI M41 high speed tool steel samples produced by induction furnace as well as after doing electro-slag refining (ESR) process under different slag compositions have been investigated. The obtained ME spectra for all samples could be analyzed to a singlet and three sextets. The appeared singlet in the conventional steel and that alloyed with nitrogen as well as two refined samples using electro-slag remelting 1 and 2 (ESR1, M41N and ESR2, M41N) can be attributed to γ–austenite phase, while the singlet that appeared in the refined sample 3 (ESR3, M41N) can be attributed to some iron nitride of the form ( ε-Fe 2 N). In the refined sample, which does not contain nitrogen, γ–austenite phase cannot be found and some α-Fe 2 O 3 was detected. The observed three sextets were attributed to three different magnetic martensite phases. It appeared also that some transformations in between the three martensite phases and between martensite and austenite take place, and all these changes were thoroughly discussed. It is interesting to state that the obtained ME results are in agreement with those obtained from optical microscopy and micro-hardness measurements.
- W. E. Duckworth and G. Hoyle, Electro-Slog Refining, British Iron and Steel Research Associations, London (1969) pp. 7-8.
- R. Ebner, H. Leither, F. Jeglitch, and D. aliskanoglu, Tooling in the Next Century, London, Austria (1999) pp. 3-24.
- Taha Mattar, Khaled M. Ibrahim, Ayman Fathy, and Hoda El Faramawy, Materials Characterization, 58 (2007) 407.
- M. R. Ghomashchi, Metall. Trans. A, 16A (1985) 2341.
- K. Kuo, J. Iron Steel Inst., 173 (1953) 363.
- U. Gomser, "Mossbauer Spectroscopy", Springer – Verlag – New York, Heidelberg Berlin (1975).
- Z. Homonnay, S Music, T. Nishida, N. S. Kopelev and A. Vertes,”Mossbauer Effect Spectroscopy of Sophisticated Oxides”, Akadememiai Kiado, Budapest, (1995).
- Sash Y. M., El-Gamal T., El-Salamoni M.A., and Denkar F." Improving solidification Patten of ESR ingots with energy saving" Steel Research 59, 1988, No.6.
- R. Wei, J. J. Vajo, J. N. Matossian, P. J. Wilbur, J. A. Davis, D. L. Williamson, G. A. Collins, Coat. Technol. 83 (1996) 235.
- C. Cordier-Robert, A. M. Kiauga and J. Foct, Mater. Sci. Forum 318 (1999) 333.
- S. D. de Souza, M. Olzon-Dionysio, E. J. Miola and C. O. Paiva-Santos, Surf. Coat. Technol. 184 (2004) 176.
- B. J. Griffiths, J. Tribol. 109 (1987) 525.
- Sangho Kim, Suk Yong kang,Sel. J. OH, Soon-Ju Kwon, Sunghak Lee, Joo Hag Kim, and Jun Hwa Hong., vol. 31A, (2000) 1107.
- L.H. Schwartz and K.J. Kim. Vol.7A, (1976) 1567.
- C. Cordier-Robert and J. Foct, ISIJ. International vol. 30 (1996) 759.
- Jerzy Narojczyk, Zbigniew Werner, Jerzy Piekozewski and Wladyslaw Szymczyk, Vacuum, 78 (2005) 229.
- L.C. Gontijo, R. Machado, E. J. Miola, L. C. Casteletti, N. G. Alcantara and P. A. P. Nascente, Materials Sci. and Engineering A, 431 (2006) 315.