Mechanical Properties of Fly Ash Filled High Density Polyethylene
- 1 Department of Polymer Engineering and Technology, Institute of Chemical Technology,Mumbai University, Mumbai 400019, India
- 2 Department of Polymer Engineering and Technology, Institute of Chemical Technology,Mumbai University, Mumbai 400019, India
Abstract
Effect of fly ash as filler in mechanical properties of HDPE is described in this study. Three different particle size of fly ash was used. Concentration of fly ash was varied up to 40 % by weight. The composites were prepared using twin screw extruder and then test specimens were prepared by injection molding. Tensile, flexural and impact properties were tested. The microstructure was investigated through scanning electron microscopy (SEM) of the fractured samples. Both tensile and flexural strengths and moduli were found to increase with fly ash addition. Tensile elongation drastically reduced at fly ash concentration greater than 10%. With increasing fly ash concentration impact resistance decreased up to about 15% fly ash concentration and then did not reduce significantly on further addition. Composites with smallest size fly ash particles proved to be better in enhancing strength and relative elongation. Modulus and impact resistance did not seem to depend much on particle size.
- Hodd, K. A.; Davies, L. C. B.; Sothern, G. R. Proceedings Second International Conference on Ash Technology and Marketing, London, September 1984, 647-51.
- Plowan, C.; Shaw, N. C. Proceedings Second International Conference on Ash Technology and Marketing, London, September 1984, 663-70.
- O’Keeffe, J. Proceedings Second International Conference on Ash Technology and Marketing, London, September 1984, 653-62.
- Huang X.; Hwang J. Y.; Gillis J. M.; Proceedings 12th International Symposium on Coal Combustion by-product Management and Use, 1997, 22.
- Guhanathan S.; Devi M. S.; Murugeshan V.; Journal of Applied Polymer Science, 2000, 82, 1755-1760.
- Alkan C.; Arslan M.; Cici M.; Kaya M.; Aksoy M. Resourses, Conservation and Recycling, 1995, 13, 147-154.
- Bose S.; Mahanwar P. A.; Journal of Minerals and Materials Characterization and Engineering, 2004, 3, 2, 65-72.
- Hundiwale D. G.; Kapadi U. R.; Desai M. C.; Patil A. G.; Bidkar S. H.; Polymer-Plastics Technology and Engineering, 2004, 43, 3, 615-630.
- Wypych G. Handbook of Fillers, 2nd ed.; Chem Tec Publishing, Toronto, 2000; Chap. 2.
- Pukanszky, B.; Fekete, E.; Tudos, F. Makromol. Chem. Macromol. Symp., 1989, 28, 165.