Nitriding of Medium Carbon Ferromanganese Alloy in Gas Solid Reaction
- 1 Central Metallurgical Research & Development Institute, CMRDI P. O. Box 87 Helwan, Egypt
Abstract
Nitriding process of medium carbon ferromanganese was carried out in the solid state, on lab and bench scale at temperature range 1023-1323 K using different nitrogen and hydrogen pressures. The influence of H 2 /N 2 gas ratio, temperature and time on nitriding process of fine (-2 mm) medium carbon ferromanganese were investigated. Nitrogen content, in weight percent ranging from 2.1 to 9.7 could be obtained. The optimum temperature and time of nitriding process was found to be 1223 K and 21.6 ks respectively. The results showed that nitrogen content is mainly depending on time and temperature of nitriding process. The comparison between results of lab and bench scale, at optimum conditions, showed good coincidence. At optimum conditions; 1223 K, 21.6 ks and at 2/8 of H 2 /N 2 , nitrogen content of fine medium carbon ferromanganese was 9.5%.
- EUI-JUN KIM, BYUNG-DON YOU, and JONG-PAK “ nitrogen solubility in liquid manganese and ferromanganese alloys” Metallurgical and Materials transactions B, Aug. 2001, Vol. 32B, pp 659-668.
- D.S. Kozak and L.R Matricardi: Iron Steelmaker, 1981. Vol.8 (4), pp.28-31
- E. Schurmann, A. Ender, E. Hofiken, H. Litterscheld, and C.H. Schutzi Stov Eisen. 1993, vol 113, pp. 77-82
- W. Dresler: Can. Metall. Q. 1989, vol. 28, pp. 109-115.
- B. D. You, K.Y. Park, J.J. Pak, and J. W. Han: Mater., 1999, vol5, pp. 395-399.
- B. D. You J. W. Han and J.J. Pak: Steel Res. 2000, vol 71(1-2),pp.22-26.
- N. A. Gokcen The Mn-N System [J]. Bulletin of Alloy Phase Diagrams, 1990, 11(1), 33.
- C. Qiu, A F. Guillermet Predicative Approach to the Entropy of Manganese Nitrides and Calculation of the Mn-N Phase Diagram [J]. Z Metallkd, 1993, 84(1), 11.
- Metal phase diagram or binary phase diagram “ nitrogen and manganese”pp.573-578.
- Zhukov, I.I. – Zhurnal Russkogo Fiziko – Khimicheskogo Obshchestva, vol. 40; 457. 1908; vol.42;40. 1910; Izv. Sektora Fiziko-Khimicheskogo Analiza, 3(1): 14. 1926.
- M. P. Slavinskii, Fiziko-Khimicheskie svoistva elementrov (physicochemical properties of elements), p. 549.,-Metallurgizdat. 1952.
- Zwicker, U. –Zeitschr, Metallkunde, 1951, 42(9): 274.
- Zhang Jin-Zhu, XU Chu-Shao, Zhao Yue –Ping” Kinetics of nitrogen diffusion in granular manganese” Journal of iron and steel research, International. 2008, 15(1), pp. 85-88
- M. Hansen, K. Anderko Constitution of binary alloys[M], New York: McGraw Hill, 1958.
- F. Lihl, P. Ettmayer, Kutzelnigg A. The System Manganese Nitrogen [J]. Z Metallkd, 1962, 53,715.
- L. L. Quil, The chemistry and Metallurgy of Miscellaneous Materials; Thermodnamics. McGraw Hill Book Company, Inc. New York-Toronto-London. 1950.
- V. Grigoryan, L Belyanchikov and A. Stomakhin, “ theotetical principles of electric steelmaking” , 1979, Mir Publisher, Moscow.
- A. Vogel, A Textbook of Quantitative Inorganic Analysis Including Elementary Instrumental Analysis, Woolwich Polytechnic, London, 1992.
- A Ahmed, T. Mattar, A. Fathy, H. EL_Faramawy and M. Eissa. “ Solid state nitrogen of high and medium carbon ferromanganese”, Canadian Metallurgical Quarterly, 2006, No. 4,Vol. 45, pp. 493-498,