The Effect of Time, Percent of Copper and Nickel on the Natural Precipitation Hardness of Al – Cu – Ni Powder Metallurgy Alloys Using Design of Experiments
- 1 Department of Systems Science and Industrial Engineering, State University of New York at Binghamton, Binghamton, NY 13850, USA
- 2 Department of Automotive Engineering, Clemson University-International Center for Automotive Research (CU-ICAR), 4 Research Drive, Greenville, SC 29607, USA
- 3 Industrial Engineering Department, Jordan University of Science and Technology, P.O. Box 3030, Irbid 22110 Jordan
- 4 Industrial Engineering Department, Jordan University of Science and Technology, P.O. Box 3030, Irbid 22110 Jordan
Abstract
In this investigation, the effect of time, percentage of copper and nickel on the hardness property of aluminum based powder metallurgy alloys were studied. A full factorial analysis with four levels for each factor was used. The samples were produced using powder metallurgy process, and then subjected to natural aging where heat treatment was conducted for all samples together at 550°C for 3 hours before quenching in water. Then, the samples were left at room temperature for 936 hours (39 days) to allow traces atoms to diffuse and form coherent phases which increase the hardness. It was found that the hardness was firstly increased with time for about 300 hours after the quenching time, and then it tends to remain constant after that. However, the hardness drop at overage stage was not observed until the end of 936 hours. To get a full analysis of the natural aging we used design of experiment tool to study the effect of %Cu, %Ni and aging time on the hardness. The results showed that the hardness was influenced significantly by all considered factors and interactions between them.
- ASM Metals Hand book, Properties and Selection: Nonferrous Alloys and Special- Purpose Materials 2 (1990): 169-487.
- ASM Metals Handbook, vol. 2. Properties and Selections: Nonferrous Alloys and Pure Metals, 10th Ed.; 1979. p. 81–2.
- W. Smith, J. Hashemi, Foundations of Material Science and Engineering, Fourth Edition, McGraw-Hill International, 2006.
- H.D. Chapra. B.C. Muddle. I.J. Polmear. The structure of primary strengthening precipitates in an Al-1.5wt% Cu-4.0wt% Mg-0.5wt% Ag alloy. Philosophical magazine letters 1996, 73 (6) 351- 357.
- R.D. Askeland, P.P. Phulé. Materials science and engineering. 4th edition, 2003 Brooks/Cole.
- W.S. Miller, L. Zhuang, J. Bottema, A.J. Wittebrood. P. D. Smet, A, Haszler, A. Vieregge. Recent developments in aluminum alloys for the automotive industry. Materials Science and Engineering 280 (2000): 37–49.
- B.L. Ou, and Chin-Hui Shen. Effect of preaging on precipitation behavior in Aluminum alloy 6063 during high-temperature aging. Scandinavian Journal of Metallurgy 2004; 33: 105–112.
- N. Oneda, M. Shimura, Y. Takeuchi. The effect of preaging on the artificial precipitationhardening of an Al-1.32wt% Mg2Si alloy. Light Metal 19 (1969): 41.
- I. Ozbek. A study on the re-solution heat treatment of AA 2618 aluminum alloy. Materials Characterization 58 (2007): 312–317.
- M.N. Desmukh, R.K. Pandey, A.K. Mukhopadhyay. Effect of aging treatments on the kinetics of fatigue crack growth in 7010 aluminum alloy. Materials Science and Engineering (2006): 318–326.
- M. Zeren. The effect of heat-treatment on aluminum-based piston alloys. Materials and Design 28 (2007): 2511-2517.
- P. Ouellet, F.H. Samuel, J. Investigation study of 356 and 319 Al alloys. Journal of Material Science 34 (1999): 4671–4697.
- R. González-Martínez, J. Goken, D. Letzig, K. Steinhoff, K.U. Kainer. Influence of aging on damping of the magnesium-aluminum-zinc Series. Journal of alloys and compounds 437 (1-2) (2007): 127-132.
- A. M. Zahra, C.Y. Zahra, M. Dumont. Effects of Ag or Si on precipitation in the alloy Al-2.5 mass% Cu-1.5 mass% Mg. Philosophical Magazine, 2005, 85 (31) 3735–3754.
- S. Szczepanik, T. Sleboda, The influence of hot deformation and heat treatment on the properties of P/M Al-Cu composites. Journal of materials processing technology 60 (1996) 729-733.