The Effect of Time, Percent of Copper and Nickel on Naturally Aged Al-Cu-Ni Cast Alloys
- 1 Center for Autonomous Solar Power, State University of New York at Binghamton, Binghamton, NY 13850, USA
- 2 Clemson University International Center for Automotive Research (CU-ICAR), 4 Research Drive, Greenville, SC 29607, USA
- 3 Industrial Engineering Department, Jordan University of Science and Technology, P.O. Box 3030, Irbid 22110 Jordan
- 4 Industrial Engineering Department, Jordan University of Science and Technology, P.O. Box 3030, Irbid 22110 Jordan
Abstract
In this paper, the hardness property during natural age hardening phenomenon for aluminum based alloy has been studied. Different factors play role in aging hardening of aluminum. In this study, the chosen factors were percentages of copper and nickel in aluminum alloys. The specimens were manufactured using casting process, and then heat treatment was carried out for all produced samples together at 550 °C for 3 h before quenching in water. Finally, the specimens were left at room temperature for 936 hours (39days) to allow solute atoms to defuse and form coherent phases to allow the age hardening to take place. The results show that the hardness increased with time in the first 300 hour after the quenching time, and then it remained constant for the rest of the 936 hours. Furthermore, the hardness did not drop until the end of 936 hours which means the over-aging status was not achieved. To get full analysis of the natural aging, design of experiment technique was used to study the effect of %Cu, %Ni and aging time.
- A.M. Hassan, O.M. Bataineh, K.M. Abed. The effect of time and temperature on the precipitation behavior and hardness of Al–4 wt%Cu alloy using design of experiments. Journal of Materials Processing Technology 204 (2008): 343–349.
- ASM metals hand book, Properties and Selection: Nonferrous Alloys and Special-Purpose Materials 2 (1990): 169-487.
- ASM metals handbook, Properties and Selections: Nonferrous Alloys and Pure Metals, 10th Ed. 2 (1979): 2-81.
- W. Smith, J. Hashemi. Foundations of material science and engineering, Fourth Ed., McGraw-Hill International, New York, USA, 2006.
- H.D. Chapra, B.C. Muddle, I.J. Polmear. The structure of primary strengthening precipitates in an Al-1.5wt% Cu-4.0wt% Mg- 0.5wt% Ag alloy. Philosophical Magazine Letters 73 (1996): 351- 357.
- R.D. Askeland, P.P. Phulé. Materials science and engineering. Fourth Ed., Nelson, Toronto, Canada, 2003
- W.S. Miller, L. Zhuang, J. Bottema, A. J. Wittebrood, P. D. Smet, A. Haszler, A. Vieregge. Recent developments in aluminum alloys for the automotive industry. Materials Science and Engineering 280 (2000): 37–49.
- S. Szczepanik, T. Sleboda. The influence of hot deformation and heat treatment on the properties of P/M Al-Cu composites. Journal of Materials Processing Technology 60 (1996): 729-733.
- B.L. Ou, C. Shen. Effect of preaging on precipitation behavior in Aluminum alloy 6063 during high-temperature aging. Scandinavian Journal of Metallurgy 2004 (33): 105–112.
- N. Oneda, M. Shimura, Y. Takeuchi. The effect of preaging on the artificial precipitation-hardening of an Al-1.32wt% Mg2Si alloy. Journal of Light Metals 19 (1969): 41.
- I. Ozbek, A study on the re-solution heat treatment of AA 2618 aluminum alloy. Mater Character 58 (2007): 312–317.
- M.N. Desmukh, R. K. Pandey, A. K. Mukhopadhyay. Effect of aging treatments on the kinetics of fatigue crack growth in 7010 aluminum alloy. Materials Science and Engineering (2006): 318–326.
- M. Zeren. The effect of heat-treatment on aluminum-based piston alloys. Materials and Design 28 (2007): 2511-2517.
- P. Ouellet, F. H. Samuel. Investigation study of 356 and 319 Al alloys. Journal of Materials Science 34 (1999): 4671–4697.
- R. González-Martínez, J. G?ken, D. Letzig, K. Steinhoff, K. U. Kainer. Influence of aging on damping of the magnesium-aluminum-zinc Series. Journal of Alloys and Compounds 437 (1-2) (2007): 127-132.