Chemical and Mineralogical Characterization of Ghanaian Foundry Slags
- 1 Department of Materials Engineering, Kwame Nkrumah University of Science and Technology, Kumasi-Ghana
- 2 Department of Materials Engineering, Kwame Nkrumah University of Science and Technology, Kumasi-Ghana
- 3 Department of Materials Engineering, Kwame Nkrumah University of Science and Technology, Kumasi-Ghana
- 4 Department of Materials Engineering, Kwame Nkrumah University of Science and Technology, Kumasi-Ghana
- 5 Department of Geological Engineering, Kwame Nkrumah University of Science and Technology, Kumasi-Ghana
Abstract
The application of ferrous slags as aggregate, road bed materials, soil fertility conditioner and as clinker materials depend on their chemical and mineralogical characteristics. In order to assess the possibilities of using ferrous slags generated in Ghana, selected slag samples from some foundries have been characterized. A total of six bulk samples were collected from three different foundry shops to determine their chemical and mineralogical composition. The slag samples showed varied chemical and mineralogical characteristics. Differences are as a result of the differences in furnace charge, operation temperatures, grades of refractory furnace lining and melting additives. Calcium oxide (CaO) contents observed in all investigated samples were in combined form (i.e. not free CaO). The low amounts of calcium oxide in the slag samples limit their applications in the area of cement/aggregate production. Even though slags were found to be alkaline, for these slags to effectively neutralize the acidity of soil and improve its fertility, components such as CaO, SiO 2 , MgO and FeO in the slag must be improved. However, these slags could be used as road bed materials.
- Ghosh, S., Das, M., Chakrabarti, S., Ghatak, S. 2002, Development of ceramic tiles from common clay and blast furnace slag. Ceram Int. 28, 393–400.
- Osipov, V.A., Timofeeva, Z.G., Kurbatskii, M.N., Mironova, P.V., Ocheretnyuk, F.F. 1990, Blast furnace granulated slag in the production of building ceramics. Glass Ceram. 47, 228–230.
- Dana, K., Das, S.K., 2004, Partial substitution of feldspar by blast furnace slag in triaxial porcelain: Phase and microstructural evolution. J. Euro. Ceram. Soc. 24, 3833–3839.
- Karamanova, E., Avdeev, G., Karamanov, A., 2011, Ceramics from blast furnace slag, kaolin and quartz, J. Euro. Ceram. Soc. 31, 989–998.
- Nistor, L., Cioroi, M., 2007, Recycling possibilities of metallurgical slag, The Annals of Dunarea DeJos, University of Galati, Fascicle IX, Metallurgy and Materials Science (1), 78-82.
- Fidancevska, E., Vassilev, V., Hristova-Vasileva, T., Milosevski, M., 2009, On a possibility for application of industrial wastes of metallurgical slag and TV-glass, J. Univ. Chem. Technol. & Met. 44, 2, 189-196.
- Navarro, C., Diaz, M., Villa-Gacia, M.A., 2010, Physico-chemical characterization of steel slag. Study of its behavior under simulated environmental conditions. Environ. Sci. Technol. 44, 5383-5388.
- Adygezalov, S.A., Dvortsov, S.P., Shemonaeva, T.N., Strakhov, V.M., Surovtseva, I.V., 2011, Industrial production of coke briquets for cupola smelting of iron, Coke & Chemistry, 54 (1), 19-22.
- Diez, M.A., Alvarez, R., Barriocanal, C., 2002, Coal for metallurgical coke production: Prediction of coke quality and future requirements for coke making. Int. J. Coal Geol., Vol. 50, 289-412.
- Haley, D.G., 2004, The efficiency of coke producing quality iron from lower quality coke, www.asi-alloys.com/pdf/GeoHaleyCokePaper.pdf.
- Sarkar, R., Singh, N., Das, S.K., 2010, Utilization of steel melting electric arc furnace slag for development of vitreous ceramic tiles, Bull. Mater. Sci., 33 (3), 293–298.
- Skuza, Z., Kolmasiak, C., Prusak, R., 2009, Possibilities for the utilization of metallurgical slag in the conditions of polish economy, METABK, 48(2), 125-128.
- Barisi?, I., Dimter, S., Netinger, I., 2010, Possibilities of application of slag in road construction, Technical Gazette, 17 (4), 523-528.
- Sofili?, T., Rastov?an-Mioc, A., ?osi?, M., Merle1, V., Mio?, B., Sofili?, U., 2011, EAF steel slag application possibilities in Croatia asphalt mixture production: http://www.aidic.it/CISAP4/webpapers/16Sofilic.pdf.