Effect of Aqueous Extracts of Bitter Leaf Powder on the Corrosion Inhibition of Al-Si Alloy in 0.5 M Caustic Soda Solution
- 1 National Metallurgical Development Centre, P.M.B. 2116, Jos, Plateau State, Nigeria
- 2 National Metallurgical Development Centre, P.M.B. 2116, Jos, Plateau State, Nigeria
- 3 National Metallurgical Development Centre, P.M.B. 2116, Jos, Plateau State, Nigeria
- 4 National Metallurgical Development Centre, P.M.B. 2116, Jos, Plateau State, Nigeria
- 5 National Metallurgical Development Centre, P.M.B. 2116, Jos, Plateau State, Nigeria
- 6 National Metallurgical Development Centre, P.M.B. 2116, Jos, Plateau State, Nigeria
- 7 Department of Metallurgical and Materials Engineering, Ahmadu Bello University, Zaria, Nigeria
Abstract
The effect of bitter leaf ( Vernonia amygdalina ) extract as an inhibitor for aluminium silicon alloy in 0.5 M solution of caustic soda using weight loss method has been investigated. The alloy of composition 9% Si and 91% Al was sand cast at the Foundry Shop of the National Metallurgical Development Centre, Jos, Nigeria. The cast alloy was cut and machined to corrosion coupons and immersed into 0.5 M NaOH solution containing varying inhibitor concentrations (0.1%, 0.2%, 0.3%, 0.5% v/v) within a period of fifteen days. From the result, it was found that the adsorption of Vernonia amygdalina reduced the corrosion rate of this group of alloy in the alkaline medium. The inhibitive action of this plant extract was explained using inhibition efficiency and degree of surface coverage. The most suitable inhibitor concentration was found to be 0.5% with inhibition efficiency of 87%. The mechanism of inhibition is by physical adsorption and the adsorbed molecules of the inhibitor lies on the surface of the alloy blocking the active corrosion sites on the alloy, hence, giving the alloy a higher corrosion resistance in the studied environment.
- Fontana, M.G., (1987); Corrosion Engineering, Third Edition, MC Graw-Hill Book Company, Printed and Bound by B and Joe Enterprise Ltd. Singapore, pp 143-160.
- Kuznetsov, Y.I., (2004); Russia Academy of Science and Turpion Ltd., Chemical Reviews, 73:75.
- Ebenso, E.E., (2003); Corrosion Inhibition Studies of some Plant Extracts 0n Aluminium in Acidic Medium; Journal of Mater. Chem. Phys. vol. 79, pp 58-62.
- Adeyemi, O.O., (2006); Effect of Temperature and Concentration on Protective Action of 5 Membered Heterocycles on Acid Corrosion of Brass; Journal of Corr. Science and Technology, published by NICA, Nigeria, vol. 3, pp 40-45.
- Oguize, E.E., Okolue, B.N., Ogukwe, C.E., Onuchukwu, A.I., (2004); Studies on the Inhibitive Action of Methylene Blue Dye on Aluminium Corrosion in KOH Solution; Journal of Corrosion Science and Technology, NICA, Nigeria, vol. 1, pp 88-91.
- Chetouani, A., Hanmouti, B., Benkaddour, M., (2004); Pigment and Resin, 33:26.
- Loto, C.A., Muhammed, A.I., (2005); The Effect of Cashew Juice Extract on the Corrosion Inhibition of Mild Steel in HCl, Corrosion Prevention and Control Journal, vol. 52 (1) 3, pp 13-22.
- Okafor, P.C., (2007); Eco Friendly Corrosion Inhibitors: Inhibitive Action of Ethanol extracts of Garcinia Kola for the Corrosion of Mild Steel in H2SO4 Solution; Pigment Resin Technology, vol. 36, pp 5-8.
- Davis, G.D., Fraunhofer, J.A., Krebs, L.A., Dacres, C.M., (2001); TheUse of Tobacco Extracts as Corrosion Inhibitor; CORROSION 2001 Paper, no. 58, Houston, Texas, NACE.
- Loto, C.A., (1998); The Effect of Bitterleaf Extracts on Corrosion of Mild Steel in 0.5M HCl and H2SO4 Solutions, Nigeria Corrosion Journal International, vol. 1, pp 19-20.
- Loto, C.A., Loto, R.T., Popoola, A.P.I., (2011); International Journal of the Physical Sciences, vol. 6(9), pp. 2249-2257.
- Loto, C.A., (2003); The Effect of Bitterleaf on the Inhibition of Mild Steel in HCl and H2SO4; Corrosion Prevention and Control Journal, vol. 50 (1) 3, pp 43-49.
- Avwiri, G.O., Igho, F.O., (2003), “Inhibitive Action of Vernonia Amygdalina on the Corrosion of Aluminium Alloys in Acidic Media”. Materials Letters, Vol. 57, issues 22-23, pp. 3705-3711.
- Idenyi, N.E., Neife, S.I., (2005); The Corrosion Behaviour of Recrystallized Mild Steel in various Tetraoxosulphate (VI) Acid Concentration; Journal of Corr. Science and Technology, NICA, Nigeria, vol. 1, pp 9-16.