Fabrication and Characterizations of Mechanical Properties of Al-4.5%Cu/10TiC Composite by <i>In-situ</i> Method
- 1 Department of Mechanical and Industrial Engineering, Indian Institute of Technology, Roorkee, India
- 2 Department of Mechanical and Industrial Engineering, Indian Institute of Technology, Roorkee, India
- 3 Department of Mechanical and Industrial Engineering, Indian Institute of Technology, Roorkee, India
Abstract
Addition of reinforcement such as TiC, SiC, Al 2 O 3 , TiO 2 , TiN, etc. to Aluminium matrix for enhancing the mechanical properties has been a well established fact. In-situ method of reinforcement of the Aluminium matrix with ceramic phase like Titanium Carbide (TiC) is well preferred over the Ex-situ method. In the present investigation, Al-Cu alloy (series of 2014 Aluminium alloy) was used as matrix and reinforced with TiC using In-situ process. The Metal Matrix Composite (MMC) material, Al-4.5%Cu/10%TiC developed exhibited higher yield strength, ultimate strength and hardness as compared to Al-4.5%Cu alloy. Percentage increase in yield and ultimate tensile strengths were reported to be about 15% and 24% respectively whereas Vickers hardness increased by about 35%. The higher values in hardness indicated that the TiC particles contributed to the increase of hardness of matrix. Fractured surface of the tensile specimen of the composite material indicated presence of dimpled surface, indicating thereby a ductile type of fracture. During the fabrication of composite, reaction products such as Al 3 Ti, Al 2 Cu and Al 3 C 4 were identified with various morphologies and sizes in metal matrix.
- P. K. Rohtagi, “Metal Matrix Composites,” Journal of Defence Science, Vol. 43, No. 4, 1993, pp. 323-349.
- D. B. Miracle, “Metal Matrix Composites from Science to Technological Significance,” Composites Science and Technology, Vol. 65, No. 15-16, 2005, pp. 2526-2540. doi:10.1016/j.compscitech.2005.05.027
- M. K. Surappa and P. K. Rohatgi, “Preparation and Prop- erties of Cast Aluminium-Ceramic Particle Composites,” Journal of Materials Science, Vol. 16, No. 4, 1981, pp. 883-993.
- A. Sato and R. Mehrabian, “Aluminium Matrix Composites: Fabrication and Properties,” Metallurgical Transactions B, Vol. 7, No. 3, 1976, pp. 443-451.
- J. Hashim “The Production of Cast Metal Matrix Composite by a Modified Stir Casting Method,” Journal Teknologi, Vol. 35, No. 35A, 2001, pp. 9-20.
- S. M. L. Nai and M. Gupta, “Influence of Stirring Speed in the Synthesis of Al/SiC Based Functionally Gradient Materials,” Composite Structures, Vol. 57, No. 1-4, 2002, pp. 227-233.
- J. Hashim, L. Looney and M. S. J. Hashmi, “Metal Matrix Composites: Production by the Stir Casting Method,” Journal of Materials Processing Technology, Vol. 92-93, 1999, pp 1-7.
- S. P. Balasivanandha, L. Karunamoorthy, S. Kathiresan and B. Mohan. “Influence of Stirring Speed and Stirring Time on Distribution of Particles in Cast Metal Matrix Composite,” Journal of Materials Processing Technology, Vol. 171, No. 2, 2006, pp. 268-273.
- I. Gotman and M. J. Koczak, “Fabrication of Al Matrix In-situ Composites via Self Propagating Synthesis,” Materials Science and Engineering, Vol. 187, No. A187, 1994, pp. 189-199.
- S. Sheivani and M. F. Nazafabadi, “In-situ Fabrication of Al-TiC Metal Matrix Composites by Reactive Slag Process,” Material and Design, Vol. 28, No. 8, 2007, pp. 2373-2378.
- B. P. Khrishnan, M. K. Surappa and P. K. Rohatgi, “A Direct Method to Prepare Cast Aluminium Alloy-Graphite Particle Composite,” Journal of Material Science, Vol. 16, No. 5, 1981, pp. 1209-1216.
- L. Peijie, E. G. Kandalova and V. I. Nikitin, “ In-situ Synthesis of Al-TiC in Aluminium Melt,” Materials Letters, Vol. 59, No. 19-20, 2005, pp. 2545-2548.
- T. V. Christry, N. Murugan and S. Kumar, “A Comparative Study on the Microstructures and Mechanical Properties of Al 6061 Alloy and the MMC Al6061/TiB2/12p,” Journal of Minerals and Materials Characterization and Engineering, Vol. 9, No. 1, 2010, pp 57-65.