Effect of Surface Treatment and Fiber Orientation on the Tensile and Morphological Properties of Banana Stem Fiber Reinforced Natural Rubber Composite
- 1 Department of Metallurgical & Materials Engineering, University of Nigeria, Nsukka, Nigeria
- 2 National Institute for Interdisciplinary Science and Technology (NIIST), CSIR, Trivandrum, India
- 3 Department of Metallurgical & Materials Engineering, University of Nigeria, Nsukka, Nigeria
- 4 Department of Metallurgical & Materials Engineering, University of Nigeria, Nsukka, Nigeria
Abstract
A mixture of NaOH and Na 2 SO 3 was used in modification of banana stem fibers (BSF). Unidirectional BSF reinforced natural rubber (NR) lamina composites were made using compression moulding method. The results of the tensile loading in 0°, 45° and 90° to the fiber directions of the composite with fiber mass fraction of 30% were studied. Surface modification of the BSF with a mixture of 4% NaOH and 2% Na 2 SO 3 increased the tensile strength and elastic modulus of the composite to 4.03 MPa and 147.34 MPa respectively from 3.12 MPa and 84.30 MPa of the untreated. Variation in properties due to fiber orintations was observed indicating a higher value of properties in the 0° fiber orientation than in 45° and 90° directions. The result of scanning electron microscope (SEM) micrographs of the surfaces of the fibers indicted an improvement in bonding of the fiber bundles prior to lamination with natural rubber as a result of surface treatment which resulted in its higher tensile strength.
- Maya, J.J. and Sabu, T. (2010) Cellulosic Fibril-Rubber Nanocomposite; Rubber Nanocopmosite: Prepartions, Properties and Applications. John Wiley & Sons Asia Plc Ltd, 197-209.
- Han, Y.H., Han, S.O., Cho, D. and Kim, H.-I. (2008) Dynamic Mechanical Properties of National Fiber/Polymer Composites—The Effect of Fiber Treatment with Electron Beam. Macromolecular Research, 16, 253-260. http://dx.doi.org/10.1007/BF03218861
- Pritchard, G. (2004) Two Technologies Merge: Wood Plastic Composite. Journal of Plastic Additives and Compounding, 48, 26-29.
- Satyanarayana, K.G., Pai, B.C., Sukumaran, K. and Pillai, S.G.K. (1990) Fabrication and Properties of Lignocellulosic Fiber—Incorporated Polyester Composites. Handbook of Ceramics and Composites, Vol. 1, Synthesis and Properties. Marcel Dekker Inc., New York, 339-384.
- Ticoalu, A., Aravinthan, T. and Cardona, F. (2010) Review of Current Developments in Natural Fiber Composites for Structural and Infrastructure Applications. Southern Region Engineering Conference, Toowoomba, 11-12 November.
- Fan, M. (2010) Characterization and Performance of Elementary Hemp Fiber: Factors Influencing Tensile Strength. Bioresources, 54, 2307-2322.
- Misra, M., Mohanty, A.K. and Drzal, L.T. (2002) Opportunities and Cchallenges in the Materials World. Plastic Impact on the Environment, Detroit, 13-14 February, 383-398.
- Oladele, I.O., Akinwekomi, A.D., Arobo, S. and Aladenika, A.K. (2009) Development of Fiber Reinforced Cementitious Composite for Ceiling Application. Journal of Minerals and Materials Characterization & Engineering, 8, 583-590.
- Esmeraldo, M.A., Gomes, A.C., Freitas, J.E.B., Fechine, P.B.A., Sombra, A.S.B., Corradini, E., Mele, G., Maffezzoli, A. and Mazzetto, S.E. (2010) Dwalf-Green Coconut Fibers: A Versatile Natural Renewable Raw Bioresource: Treatment, Morphology and Physico-Chemical Properties. Bioresources, 5, 2478-2501.
- Amer, A.A., Azza, E., Malash, G.F. and Nahla, A.T. (2007) Extensive Characterization of Raw Barley Straw and Study of the Effect of Steam Pretreatment. Journal of Applied Science Research, 3, 1336-1342.
- Dai, D. and Fan, M. (2010) Characteristics and Performance of Elementary Hemp Fiber. Materials Science and Applications, 1, 336-342. http://dx.doi.org/10.4236/msa.2010.16049
- Maleque, M.A., Belal, F.Y. and Sapuan, S.M. (2006) Mechanical Properties Study of Pseudo-Stem Banana Fiber Reinforced Epoxy Composites. The Arabian Journal of Science and Engineering, 32, 359-364.