Microstructural Evolution of Cast Hyper-Eutectic Al-18% Si Alloy during Cyclic Semi-Solid Heat Treatment
- 1 College of Engineering, University of Hail, Hail, Saudi Arabia
- 2 Casting Technology Lab., Central Metallurgical Research and Development Institute (CMRDI), Cairo, Egypt
Abstract
The cyclic semi-solid heat treatment represents a promising technique for improving microstructure and mechanical properties of a wide range of metallic alloys. In the current research the influence of cyclic semi-solid heat treatment on microstructure of Al-18% Si alloy containing 0.8% Fe has been studied. All specimens were heated in an electrically heated resistance furnace with heating rate of 10°C·min -1 to 585°C. For a complete one cycle heat treatment (5 min heating time), samples after 5 min holding at 585°C were cooled to a temperature of 550°C in still air cooling and the samples were taken out immediately for water quenching. It was found that heat treatment cycles should be limited to 3 cycles or less in order to maintain fine grain size and globular structure without agglomeration and coalescence. Cyclic semi-solid heat treatment changes morphology of iron-rich intermetallics phases to be plate-like and fine plate iron-rich intermetallics phases, in stead of needle-like iron-rich intermetallics phases that are observed in as-cast samples. Cyclic heating shows a relatively higher hardness for all heating cycles compared with as-cast one due to its finer and globular structure. Cyclic semi-solid heat treatment technique results in lower coarsening rate constant compared with isothermal heat treatment one due to coarsening discontinuous effect.
- He, K., Yu, F., Zhao, D. and Zuo, L. (2012) Characterization of Precipitates in a Hot-Deformed Hypereutectic Al-Si Alloy. Journal of Alloys and Compounds, 539, 74-81. http://dx.doi.org/10.1016/j.jallcom.2012.06.051
- Chen, M. and Alpas, A.T. (2008) Ultra-Mild Wear of a Hypereutectic Al-18.5 wt.% Si Alloy. Wear, 265, 186-195. http://dx.doi.org/10.1016/j.wear.2007.10.002
- Ott, R.D., Blue, C.A., Santella, M.L. and Blau, P.J. (2001) The Influence of a Heat Treatment on the Tribological Performance of a High Wear Resistant High Si Al-Si Alloy Weld Overlay. Wear, 251, 868-874. http://dx.doi.org/10.1016/S0043-1648(01)00744-X
- Stefanescu, D.M. (2008) ASM Handbook. ASM International, USA, V15 Casting.
- Fathy, N. (2013) Microstructural Evolution of Hyper-Eutectic Al-18% Si Alloy during Semi-Solid Isothermal Heat Treatment. Proceedings of the International Conference on Research in Science, Engineering and Technology, Kuala Lumpur, 13-14 November 2013.
- Abouei, V., Shabestari, S.G. and Saghafian, H. (2010) Dry Sliding Wear Behaviour of Hypereutectic Al-Si Piston Alloys Containing Iron-Rich Intermetallics. Materials Characterization, 61, 1089-1096. http://dx.doi.org/10.1016/j.matchar.2010.07.001
- Shabestari, S.G. and Gruzleski, J.E. (1994) The Effect of Solidification Condition and Chemistry on the Formation and Morpholgy of Complex Intermetallic Compounds in Aluminum-Silicon Alloys. International Journal of Cast Metals Research, 6, 217-224.
- Belov, N.A. and Aksenov, A.A. (2002) Iron in Aluminum Alloys. Impurity and Alloying Element. Taylor and Francis, New York.
- Ashtari, P., Tezuka, H. and Sato, T. (2005) Modification of Fe-Containing Intermetallic Compounds by K Addition to Fe-Rich AA319 Aluminum Alloys. Scripta Materialia, 53, 937-942. http://dx.doi.org/10.1016/j.scriptamat.2005.06.022
- Shabestari, S.G. (2004) The Effect of Iron and Manganese on the Formation of Intermetallic Compounds in Al-Si Alloys. Materials Science and Engineering: A, 383, 289-298. http://dx.doi.org/10.1016/S0921-5093(04)00832-9
- Wang, N., Zhou, Z. and Lu, G. (2012) Microstructural Evolution of 6061 Alloy during Isothermal Heat Treatment. Journal of Materials Science and Technology, 27, 8-14. http://dx.doi.org/10.1016/S1005-0302(11)60018-2
- Atkinson, H.V. and Liu, D. (2010) Coarsening Rate of Microstructure in Semi-Solid Aluminum Alloys. Transactions of Nonferrous Metals Society of China, 20, 1672-1676. http://dx.doi.org/10.1016/S1003-6326(09)60356-3