Influence of Si and Ge Microalloying Additions and Plastic Deformation on Precipitation Processes in Al-Cu Based Alloys
- 1 División Física de Metales, Centro Atómico Bariloche, Comisión Nacional de Energía Atómica, San Carlos de Bariloche, Argentina
- 2 División Física de Metales, Centro Atómico Bariloche, Comisión Nacional de Energía Atómica, San Carlos de Bariloche, Argentina
Abstract
The combined effect of micro-alloying with Si and Ge and/or plastic deformation prior to ageing at 160°C on age hardening has been studied in an Al-2 at% Cu alloy. The results obtained indicate that the hardness response is faster and the peak hardness is higher when plastic deformation and micro-alloying are applied together than performing each procedure individually. Different amounts of deformation, ranging from 0% to 30% have been utilized. An optimum deformation degree for the hardening response has been established around 8% for the Al-Cu-Si-Ge alloy. Characterization by transmission electron microscopy (TEM) shows that the peak hardness is due to a complex microstructure that contained θ" disc shaped precipitates, rod-shaped Si-Ge precipitates and θ' plates that were heterogeneously nucleated on the Si-Ge particles. Pre-deformation has been found to stimulate the growth of the θ' plates due to enhanced diffusion along dislocation cores. Increasing deformation reduces the influence of the Si-Ge precipitates on heterogeneous nucleation, leading to reduced peak hardness and faster over-ageing.
- Polmear, I.J. and St. John, D. (2005) Light Alloys: From Traditional Alloys to Nanocrystals. 4th Edition, Butterworth-Heinemann, London.
- Hardy H.K. ,et al. (1951-1952)The Ageing Characteristics of Ternary Aluminium-Copper Alloys with Cadmium, Indium or Tin Journal of the Institute of Metals 80, 483-492.
- Hardy H.K. ,et al. (1950-1951)The Effect of Small Quantities of Cd, In, Sn, Sb, Tl, Pb or Bi on the Ageing Characteristics of Cast and Heat Treated Aluminium-4% Copper-0.15% Titanium Alloy Journal of the Institute of Metals 78, 169-194.
- Silcock, J.M., Heal, T.J. and Hardy, H.K. (1955) The Structural Ageing Characteristics of Ternary Aluminum-Copper Alloys with Cadmium, Indium, or Tin. Journal of the Institute of Metals, 84, 23-31.
- Ringer, S.P., Hono, K. and Sakurai, T. (1995) Nucleation and Growth of θ’ Precipitation in Sn Modified Al-Cu Alloys: APFIM/TEM Observations. Applied Surface Science, 87/88, 223-227. https://doi.org/10.1016/0169-4332(94)00514-1
- Polmear I.J. ,et al. (1964)The Effects of Small Additions of Silver on the Aging of Some Aluminium Alloys Transactions of the Metallurgical Society AIME 230, 1331-1331.
- Vietz, J.T. and Polmear, I.J. (1966) The Influence of Small Additions of Silver on the Ageing of Aluminium Alloys: Observations on Al-Cu-Mg Alloys. Journal of the Institute of Metals, 94, 410-419.
- Ringer, S.P., Sakurai, T. and Polmear, I.J. (1997) Origins of Hardening in Aged Al-Cu-Mg-(Ag) Alloys. Acta Materialia, 45, 3731-3744. https://doi.org/10.1016/S1359-6454(97)00039-6
- Chester, R.J. and Polmear, I.J. (1980) TEM Investigation of Precipitates in AlCuMgAg and AlCuMg Alloys. Micron, 11, 311-312.
- Knowles, K.M. and Stobbs, W.M. (1988) The Structure of {111} Age-Hardening Precipitates in Al-Cu-Mg-Ag Alloys. Acta Crystallographica B, 44, 207-227. https://doi.org/10.1107/S0108768187012308
- Muddle, B.C. and Polmear, I.J. (1989) The Precipitate Ω Phase in Al-Cu-Mg-Ag Alloys. Acta Metallurgica, 37, 777-789. https://doi.org/10.1016/0001-6160(89)90005-9
- Chopra, H.D., Liu, K.J., Muddle, B.C. and Polmear, I.J. (1995) The Structure of Metastable {111} Precipitates in an Al-2.5 wt% Cu-1.5 wt% Mg-0.5 wt% Ag Alloy. Philosophical Magazine Letters, 71, 319-324. https://doi.org/10.1080/09500839508241014
- Macchi, C., Tolley, A., Giovachini, R., Polmear, I.J. and Somoza, A. (2015) Influence of a Microalloying Addition of Ag on the Precipitation Kinetics of an Al-Cu-Mg Alloy with High Mg:Cu Ratio. Acta Materialia, 98, 275-287. https://doi.org/10.1016/j.actamat.2015.07.032