Effects of Electrode Types on the Microstructure, Tensile and Hardness Properties of 304 L Austenitic Stainless Steel Heat-Affected Zone (HAZ)
- 1 Department of Minerals and Petroleum Resources Engineering, Federal Polytechnic, Ado Ekiti, Nigeria
- 2 Department of Mechanical Engineering, Federal Polytechnic, Ado Ekiti, Nigeria
- 3 Department of Metallurgical and Materials Engineering, Federal University of Technology, Akure, Nigeria
Abstract
Submerged arc welding (SAW) has been well utilised for the production of weld joints in 304 L ASS for various industrial application. However, effective performance of the material in service has been hampered by improper choice of electrode. Therefore, in this study, effects of different types of electrode on the microstructure and tensile property of type 304 L austenitic stainless steel heat-affected zone (HAZ) were studied. Chemical composition of the as-received sample was determined. A number of samples were cut from the as-received sample. Afterwards, two half were joined together with 308 L, 312 L and 316 electrodes at a controlled welding speed, current and voltage of 4.6 mm/s, 160 A and 30 V to produce a constant heat input of 626.09 J/mm. An automatic SAW machine with Model Type: DX3-301, and Frequency: 50 Hz was used. And based on ASTM standard, tensile and hardness samples were prepared from the as-received and HAZs. Tensile and hardness measurements were made. Also, specimens for microscopy studies were prepared from the HAZ and as-received samples. From the results, microstructures of the HAZs revealed varied volume fraction of austenite and ferrite phases and grain sizes, and at austenite and ferrite grain boundaries, chromium carbide formation and precipitation were observed. The weld joint produced with 308 L electrode revealed optimum UTS value and YS value of 475 and 325 respectively. While weld joint produced with 316 L electrode has superior ductility of value 41%. Irrespective of the types of electrode used, the as-received sample revealed superior tensile properties over the weld joints. Also, optimum hardness value of 45.7 HRA was obtained with 308 L. Hardness value of the as-received sample was higher than that of HAZ samples.
- Fowless, R.J. and Blake, S.E. (2008) Influence of Heat Input on Austenitic Stainless Steel Weld Properties. African Fusion, 1, 17-24.
- Lee, W.-S., Tzeng, F.-T. and Lin, C.-F. (2005) Mechanical Properties of 304L Stainless Steel SMAW Joints under Dynamic Impact Loading. Journal of Materials Science, 40, 439-484. https://doi.org/10.1007/s10853-005-1920-0
- El-Batahgy, A.M. (1997) Effect of Lazer Welding Parameters on Fusion Zone Shape and Solidification Structure of Austenitic Stainless Steels. Materials Letters, 32, 155-163. https://doi.org/10.1016/S0167-577X(97)00023-2
- Ramazan, Y. and Huseyin, U. (2002) Mechanical Properties of Austenitic Stainless Steels Welded by GMAW and GTAW. Journal of Marmara of Pure and Applied Sciences, 18, 97-113.
- Kolhe, K.P. and Datta, C.K. (2008) Prediction of Microstructure and Mechanical Properties of Multipass SAW. Journal of Materials Processing Technology, 197, 241-249. https://doi.org/10.1016/j.jmatprotec.2007.06.066
- Chandel, R.S., Seow, H.P. and Cheong, F.L. (1997) Effect of Increasing Deposition Rate on the Bead Geometry of Submerged Arc Welds. Journal of Materials Processing Technology, 72, 124-128. https://doi.org/10.1016/S0924-0136(97)00139-8
- Iordachescu, M., Ruiz-Hervias, J., Iordachescu, D., Valiente, A. and Caballero, L. (2010) Thermal Influence of Welding Process on Strength Overmatching of Thin Dissimiliar Joints. Welding in the World, 65, 201-209.
- Bipin, K.S. and Tewarl, S.P. (2010) A Review on Effect of Arc Welding Parameters on Mechanical Behavior of Ferrous Metals/Alloys. Internal Journal of Engineering Science and Technology, 2, 1425-1432.
- Peng, Y., Chen, W. and Xu, Z. (2001) Study of High Toughness Ferrite Wire for Submerged Arc Welding of Pipeline Steel. Materials Characterization, 47, 67-73. https://doi.org/10.1016/S1044-5803(01)00155-3
- Zhang, Z. and Farrar, R.A. (1997) Influence of Mn and Ni on the Microstructure and Toughness of C-Mn-Ni Weld Metals. Welding Journal, 76, S183-S196.
- Olaniran, O., Aribo, S. and Kutelu, B.J. (2010) Effect of Austempering Time on the Mechanical Properties of Austempered Ductile Iron. The Pacific Journal of Science and Technology, 11, 102-106.
- Sadeghian, M., Shamanian, M. and Shafyei, A. (2014) Effect of Heat Input Microstructure and Mechanical Properties of Dissimilar Joints between Super Duplex Stainless Steel and High Strength Low Alloy Steel. Materials and Design, 60, 678-684. https://doi.org/10.1016/j.matdes.2014.03.057