The cure characteristics and mechanical properties of natural rubber filled with pineapple leaf fibre (PLF) were studied at different filler contents and particle sizes. The PLF was characterized for filler properties while carbon black (N330) served as the reference filler. The natural rubber vulcanizates were compounded on a two-roll mill. Results showed that PLF (300 μm) filled natural rubber vulcanizates exhibited the highest maximum torque (T max ) (47.04 lb-in) at filler content, 10 phr among the filler particle sizes investigated. The minimum torque (T min ) of the vulcanizates generally increased with the increase in filler contents and particle sizes. The scorch times of the rubber vulcanizates did not vary with fibre content while the cure times of PLF (300 μm) filled rubber vulcanizates decreased with filler content. The tensile strength (TS) of PLF (150 μm) filled natural rubber vulcanizates generally increased with the increase in filler content whereas the tensile modulus of the rubber vulcanizates decreased steadily with increasing filler particle size at filler contents, 5 and 30 phr. The elongation at break (EB) of the rubber vulcanizates exhibited no general order of variation with filler content and particle size, and was generally greater than that of unfilled natural rubber. The flexural strength of the rubber vulcanizates increased with increasing filler particle size at filler contents, 20 and 40 phr. The addition of PLF and carbon black improved the compression strength of the rubber vulcanizates, and which for PLF (300 μm) and CB fillers generally increased with the increase in filler content. The study has demonstrated the enhancement of properties of natural rubber vulcanizates on incorporation of PLF into natural rubber, however, the property enhancements obtained were less than those recorded for CB filled natural rubber vulcanizates.
Osabohien, E. and Egboh, S.H.O. (2007) Cure Characteristics and Physico Mechanical Properties of Natural Rubber Filled with the Seed Shells of Cherry (Chrysophyllum albidum). Journal of Applied Science and Environment Management, 11, 43-48.
Bhatnagar, M.S. (2004) A Text Book of Polymer Chemistry and Technology. Vol. 2, Schand and Co. Ltd., New Delhi, 1-138.
Arroyo, M., Lopez-Manchado, M.A. and Herrero, B. (2003) Organo-Montmorillonite as Substitute for Carbon Black in Natural Rubber Compounds. Polymer Science Journal, 44, 2447-2453.
Ismail, H., Rozman, H.D., Jaffri, R.M. and MohdIshak, Z.A. (1997) Oil Palm Wood Flour Reinforced Epoxidized Natural Rubber Composites: Effects of Filler Content and Size. European Polymer Journal, 33, 1627-1632. https://doi.org/10.1016/S0014-3057(97)00020-7
Ansarifar, A., Shiah, S.F. and Bennett, M. (2005) Optimizing the Chemical Bonding between Silanised Silica Nanofiller and Natural Rubber and Assessing Its Effects on the Properties of the Rubber. International Journal of Adhesion and Adhesives, 26, 454-463. https://doi.org/10.1016/j.ijadhadh.2005.06.008
Kim, M., Kim, V., Chowdhury, S.R. and Kim, G. (2006) Melt-Compounded Butadiene Rubber Nanocomposites with Improved Mechanical Properties and Abraision Resistance. Journal of Applied Polymer Science, 102, 2062-2066. https://doi.org/10.1002/app.23738
Igwe, I.O. andEjim, A.A. (2011) Studies on Mechanical and End-Use Properties of Natural Rubber Filled with Snail Shell Powder. Journal of Materials Sciences and Application, 2, 801-809. https://doi.org/10.4236/msa.2011.27109
Zhang, H., Wang, Y., Zhang, L. and Yang, J. (2004) Preparation and Processing of Novel Polymer Materials. Journal of Applied Polymer Science, 97, 844-849. https://doi.org/10.1002/app.21797
Yang, J., Tian, M., Jia, Q., Zhang, L. and Li, X. (2006) Influence of Graphite Particle Size and Shape on the Properties of NBR. Journal of Applied Polymer Science, 102, 4007-4015. https://doi.org/10.1002/app.24844
Zhao, M. and Xiang, Y. (2004) Natural Rubber Vulcanizate Reinforced by Modified Coalshale-Based Fillers. Journal of Applied Polymer Science, 93, 1397-1400. https://doi.org/10.1002/app.20506
Imanah, J.E and Okieimen, F.E. (2004) Studies on the Mechanical Properties of Natural Rubber Reinforced with Agricultural By-Products. Proceedings of 27th International Conference of Chemical Society of Nigeria, Benin City, 317-322.
Chaiwat, R., Wasaphon, W., Apikiat, S. and Yapoporn, R. (2013) Congo Grass FibreExpoxidized Natural Rubber Composites. Advanced Materials and Resources, 7, 375-378.
Adeosun, B.F. (2002) Mechanical and Rheological Properties of Natural Rubber Composites Reinforced with Agricultural Wastes. Nigerian Journal of Polymer Science and Technology, 1, 58-62.
Imanah, J.E. (2003) Studies in the Utilization of Cocoa Pod Husk and Rubber Seed Shell as Fillers in Natural Rubber Compounds. Unpublished Ph.D. Thesis, Department of Chemistry, University of Benin, Nigeria, 61-310.
Ishak, Z.A.M. and Bakar, A.A. (1995) An Investigation on the Potential of Rice Husk Ash as Filler for Expoxidised Natural Rubber. European Polymer Journal, 31, 259-269. https://doi.org/10.1016/0014-3057(94)00156-1
Egwaikhide, A.P., Okieimen, F.E. and Lawal, U. (2013) Rheologoical and Mechanical Properties of Natural Rubber Compounds Filled with Carbonized Palm Kernel Husk and Carbon Black (N330). Science Journal of Chemistry, 1, 50-55. https://doi.org/10.11648/j.sjc.20130105.11
Okoh, B.E., Osabohien, E. and Egboh, S.H.O. (2014) The Reinforcing Potentials of Velvet Tamarind Seed Shell as Filler in Natural Rubber Compounds. International Journal of Biological and Chemical Sciences, 8, 2367-2376. https://doi.org/10.4314/ijbcs.v8i5.39
Eze, I.O. and Igwe, I.O. (2018) Comparison of Some Mechanical Properties of Injection and Extrusion Moulded Pineapple Leaf Powder Filled High Density Polyethylene. European Journal of Advances in Engineering and Technology, 5, 236-243.
Eze, I.O., Igwe, I.O., Nwanonenyi, S.C., Anyanwu, E.E., Ogbobe, O., Obasi, H.C., Ezeamaku, U.L. and Nwachukwu, I. (2017) Effects of Hydrogen Peroxide Treated Pineapple Leaf Powder on Mechanical Properties of High Density Polyethylene Composites. European Journal of Advances in Engineering and Technology, 4, 617-622.
Eze, I.O., Igwe, I.O., Ogbobe, O., Anyanwu, E.E. and Nwachukwu, I. (2016) Mechanical Properties of Pineapple Leaf Powder Filled High Density Polyethylene. International Journal of Engineering and Technologies, 9, 13-19. https://doi.org/10.18052/www.scipress.com/IJET.9.13
Lopattananon, N., Panawarangkul, K., Sahakaro, K. and Ellis, B. (2007) Performance of Pineapple Leaf Fibre-Natural Rubber Composites: The Effect of Fibre Surface Treatments. Journal of Applied Polymer Science, 102, 1974-1984. https://doi.org/10.1002/app.24584
Goering, H.K. and van Soest, P.J. (1970) Forage Fibre Analysis (Apparatus, Reagents, Procedures and Applicatiions) Agricultural Research Service. USDA, Washington DC.
Liyama, A. and Wallis, N. (1988) Analytical Methods in Wood Chemistry, Pulping and Papermaking. Journal of Science and Engineering, 6, 231-251.
Wang, B., Ponigrahi, S., Tabil, L., Crerar, W., Powell, T., Kolybaba, M. and Sokharisanj, S. (2003) Flax Fibre-Reinforced Thermoplastic Composites. CSAE/ASAE Annual International Meeting, Furgo, 3-4 October 2003.
Asore, E.J. (2000) An Introduction to Rubber Technology. Joseg Books Ltd., Benin City, 2-4.
Broonstra, B.B. (1984) Reinforcement by Fillers. In: Mortron, M., Ed., Rubber Technology, 2nd Edition, Van Nostrand Co., New York, 56-108.
Bledzki, A.K. and Gassan, J. (1999) Composites Reinforced with Cellulose Based Fibres. Progress in Polymer Science, 24, 221-274. https://doi.org/10.1016/S0079-6700(98)00018-5
Spinace, M.A.S., Lambert, C.S., Fermoselli, K.K.G. and Depaoli, M.A. (2009) Characterization of Lignocellulosic Curana Fibres. Carbohydrate Polymer, 77, 47-53. https://doi.org/10.1016/j.carbpol.2008.12.005
Khalil, A.H.P.S., Alwani, S.M. and Omar, M.A.K. (2006) Chemical Composition, Anatomy, Lignin Distribution and Cell Wall Structure of Malaysia Plant Waste Fibres. BioResourses, 1, 220-232.
Rahman, A. (2011) Study on Modified Pineapple Leaf Fibre. Journal of Textile and Apparel, Technology and Management, 7, 1-16.
Jacob, M., Thomas, S. and Varughese, K.T. (2004) Mechanical Properties of Sisal/Oil Palm Hybrid Fibre-Reinforced Natural Rubber Composites. Composite Science and Technology, 64, 955-965. https://doi.org/10.1016/S0266-3538(03)00261-6
Ismail, H., Shuhelmy, S. and Edyham, M.R. (2002) The Effects of a Sliane Coupling Agent on Curing Characteristics and Mechanical Properties of Bamboo Filled Natural Rubber Composites. European Polymer Journal, 38, 39-47. https://doi.org/10.1016/S0014-3057(01)00113-6
Iyasele, J.U. and Okieimen, F.E. (2004) Cure Characteristics and Rheological Properties of Melon Seed Shell Filled Natural Rubber. Proceedings of the 27th Internal Conference of Chemical Society of Nigeria, Benin City, 272-276.
Hepbum, C. and Blow, C.M. (1971) Rubber Technology and Manufacture. 3rd Edition, Butterworth Publishing, 188.
Rivin, D. (1963) Polymer—Filler Interaction in Rubber Reinforcement. Rubber Chemistry and Technology, 36, 729. https://doi.org/10.5254/1.3539604
Mohamed, N., Maditar, A., Ghazali, M.J., Muhd, D. and Azhari, C.H. (2008) The Effect of Filler on Epoxidized Natural Rubber—Alumina Nanoparticle Composites. European Journal of Science and Research, 24, 538-547.
Parkinson, D. (1957) Reinforcement of Rubbers. Lakeman and Co., London, 12.