Axial Tensile Testing of Single Fibres
- 1 Department of Aerospace Engineering, Indian Institute of Technology Kanpur, Kanpur Uttar Pradesh, India
- 2 Department of Aerospace Engineering, Indian Institute of Technology Kanpur, Kanpur Uttar Pradesh, India
- 3 Department of Aerospace Engineering, Indian Institute of Technology Kanpur, Kanpur Uttar Pradesh, India
Abstract
The mechanical and damage properties of single fibres used in fibrous composite have gained tremendous importance in recent years. These properties are used in determination of effective properties of composites by micromechanics. These are also used in the micromechanical damage modeling. Further, these properties are used as an indicator of the excellence of product by manufacturers. In the present study the axial tensile modulus, ultimate strength and failure strain of single fibres are determined for carbon and glass fibres. ASTM D3379-75 standard is followed and a number of fibers are tested for statistical analysis. The axial tensile moduli measured are 246.7 GPa and 93.3 GPa, respectively and strength are 3031.6 MPa and 2035.9 MPa, respectively for carbon and glass fibres. Further, the respective axial tensile failure strains are 0.0137 and 0.0224. The error in the measurement of axial modulus is below 8% while for axial tensile strength is below 1%.
- A. Jain, C. S. Upadhyay and P. M. Mohite, “Fibre Breaking Damage Model for Unidirectional Fibrous Composites Using Micromechanics,” 16th National Seminar on Aerospace Structures (NASAS), IIT Bombay, 2009.
- V. Murari, “Micromechanics Based Continuum Damage Model for Ply Failure in Unidirectional Composites,” Ph.D. Thesis, Department of Aerospace Engineering, Indian Institute of Technology Kanpur, Kanpur Uttar Pradesh, 2010.
- S. Biswas, “Micromechanics Based Damage Mesomodel for Unidirectional Fibrous Laminated Composite,” M. Tech. Thesis, Department of Aerospace Engineering, Indian Institute of Technology Kanpur, Kanpur Uttar Pradesh, 2011.
- ASTM D3379-75, “Standard Test Method for Tensile Strength and Young’s Modulus for High Modulus Single Filament Fibers,” ASTM Standards, 1975.
- Y. Yamashita, S. Kawabata, S. Okada and A. Tanaka, “Mechanical Characteristics of PBO Single Fiber,” 2003. www.mat.usp.ac.jp/polymer-composite/253.PDF
- D. Sinclair, “A Bending Method for Measurement of the Tensile Strength and Young’s Modulus of Glass Fibers,” Journal of Applied Physics, Vol. 21, No. 5, 1950, pp. 380-386. doi:+10.1063/1.1699670
- “Torayca Carbon Fibres Technical Information,” http://www.torayca.com/en/index.html
- I. P. Kumar, “Mechanical and Damage Characterization of Single Carbon and Glass Fibres,” M. Tech. Thesis, Department of Aerospace Engineering, Indian Institute of Technology Kanpur, Kanpur Uttar Pradesh, 2010, pp.
- D. Hartman, D. M. Miller and M. E. Greenwood, “High Strength Glass Fibers,” Moving Forward with 50 Years of Leadership in Advanced Materials, Vol. 39, 1994, pp. 415-426.
- P. D. Soden, M. J. Hinton and A. S. Kaddour, “Lamina Properties, Lay-Up Configurations and Loading Conditions for a Range of Fibre-Reinforced Composite Laminates,” Composite Science and Technology, Vol. 58, No. 7, 1998, pp. 1011-1022. doi:10.1016/S0266-3538(98)00078-5