Welding Effect at the Heat Affected Zone by Joining a Gray Cast Iron with Stainless Steel E308-16

Abstract

Different investigations of the union of dissimilar materials such as stainless steel and different castings have been carried out, but rapid cooling immediately after welding has not been considered, in this work it was investigated how rapid cooling affects the metallurgical microstructure and consequently the mechanical properties. The effect of welding parameters on the microstructure and mechanical properties of the joint between dissimilar metals, an E-308-16 austenitic stainless steel and Gray Cast Iron was also analyzed. Gray cast iron samples (GCI) were fabricated, welded and cooled. The main welding parameters studied in this work are the welding technique and the type of filler electrodes. Flux-coated electrode E-308-16 was applied for this different joint. An experimental study was carried out for the analysis of welded joints of similar and dissimilar steels. The microstructure of the welded joints was analyzed using an optical microscope, in the base metals, heat affected zone (HAZ) and filler metal. The mechanical properties of the welded joints were evaluated by Vickers microhardness and tensile strength tests. The hardness profile showed differences in hardness between the base metals, the heat affected zone and the filler metal. The metallurgical microstructures observed along the welded areas corresponded to the profile. The hardness differences determined the effect on the mechanical and metallurgical characteristics of the welded samples as a result of the cooling rate differences. This research work is important because it allows us to analyze the possibility of reworking pieces of dissimilar materials by welding or, failing that, to determine if this may or may not be possible.