Research ArticleOpen AccessGoogle Scholar indexed
Growth of Carbon Nanotubes by Pyrolysis of Composite Film of Poly (Vinyl Alcohol) and Modified Fly Ash
- 1
- 2
Materials Sciences and Applications·Volume 03 (2012)·Pages 120–124·Published 17 February 2012·DOI10.4236/msa.2012.32019
Copy link · social · email
Abstract
We found carbon nanotube (CNT) materials by the pyrolysis of the composite film of poly (vinyl alcohol) (PVA) reinforced with modified fly ash (FA) at 500°C for 10 min under 2 L/min flow of nitrogen. Fly ash was treated with 2M sodium hydroxide and used with PVA to fabricate the composite film by aqua casting. CNT materials were analyzed using XPS, Raman, SEM and TEM. The admixtures of CNT materials and FA are a potential filler material for fabricating composites with polymer and metal. The process is an eco-friendly recycling paradigm for using value-added advanced products for the proper management of sustainable waste materials, plastic and FA.
KeywordsPoly (Vinly Alcohol)Modified Fly AshComposite and Carbon Nanotube
- M. Benito, Y. Maniette, Y. Aniette, E. Mogoza and T. M. Martnez, “Carbon Nanotubes Production by Catalytic Pyrolysis of Benzene,” Carbon, Vol. 36, No. 5-6, 1998, pp. 681-683. doi:10.1016/S0008-6223(98)00039-6
- T. Oku, K. Niihara and K. Suganuma, “Formation of Carbon Nanocapsules with SiC Nanoparticles Prepared by Polymer Pyrolysis,” Journal of Materials Chemistry, Vol. 8, No. 6, 1998, pp. 1323-1325. doi:10.1039/a801912f
- O. P. Krivoruchko, N. I. Maksimova, V. I. Zaikovskii and A. N. Salanov, “Study of Multiwalled Graphite Nanotubes and Filaments Formation from Carbonized Products of Polyvinyl Alcohol via Catalytic Graphitization at 600?C - 800?C in Nitrogen Atmosphere,” Carbon, Vol. 38, No. 7, 2000, pp. 1075-1082. doi:10.1016/S0008-6223(99)00225-0
- S. Wang, “Application of Solid Ash Based Catalysts in Heterogeneous Catalysis,” Environmental Science and Technology, Vol. 42, No. 19, 2008, pp. 7055-7063. doi:10.1021/es801312m
- D. C. D. Nath, S. Bandyopadhyay, A. Yu, D. Blackburn and C. White, “High Strength Bio Composite Films of Poly (Vinyl Alcohol) Reinforced with Chemically Modified-Fly Ash,” Journal of Materials Science, Vol. 45, No. 5, 2010, pp. 1354-1360. doi:10.1007/s10853-009-4091-6
- O. M. Dunens, K. J. Mackenzie and A. T. Harris, “Synthesis of Multiwalled Carbon Nanotubes on Fly Ash Derived Catalysts,” Environmental Science and Technology, Vol. 43, No. 20, 2009, pp. 7889-7894. doi:10.1021/es901779c
- J. P. Gorninski, D. C. D. Molin and C. S. Kazmierczak, “Study of the Modulus of Elasticity of Polymer Concrete Compounds and Comparative Assessment of Polymer Concrete and Portland Cement Concrete,” Cement & Concrete Research, Vol. 34, No. 11, 2004, pp. 2091-2095. doi:10.1016/j.cemconres.2004.03.012
- P. K. Rohatgi, N. Gupta and S. Alaraj, “Thermal Expansion of Aluminum-Fly Ash Cenosphere Composites Synthesized by Pressure Infiltration Technique,” Journal of Composite Materials, Vol. 40, No. 13, 2006, pp. 1163-1173. doi:10.1177/0021998305057379
- D. C. D. Nath and V. Sahajwalla, “Application of Fly Ash as a Catalyst for Synthesis of Carbon Nanotube Ribbons,” Journal of Hazardous Materials, Vol. 192, No. 2, 2011, pp. 691-697. doi:10.1016/j.jhazmat.2011.05.072
- J. E. Moulder, W. F. Stickle, P. E. Sobol and K. D. Bomben, “Handbook of X-Ray Photoelectron Spectroscopy,” Perkin Elmer Corporation, Waltham, 1992.
- A. A. Didik, V. I. Kodolov, A. Y. Volkov, E. G. Volkova and K. H. Hallmeier, “Low-Temperature Growth of Carbon Nanotubes,” Inorgnic Materials, Vol. 39, No. 6, 2003, pp. 583-587. doi:10.1023/A:1024045002419