Effects of Titanium Sputtering Current on Structure and Morphology of TiZrN Films Prepared by Reactive DC Magnetron Co-Sputtering
- 1 Department of Physics, Faculty of Science, King Mongkut’s University of Technology Thonburi, Bangkok, Thailand
- 2 Department of Physics, Faculty of Science, Burapha University, Chonburi, Thailand
- 3 Department of Physics, Faculty of Science, Burapha University, Chonburi, Thailand
- 4 Department of Physics, Faculty of Science, King Mongkut’s University of Technology Thonburi, Bangkok, Thailand; Thailand Center of Excellence in Physics, Commission on Higher Education, Ministry of Education, Bangkok, Thailand
Abstract
TiZrN films were deposited on unheated Si (100) substrates by reactive dc magnetron co-sputtering. Titanium and zirconium metals were used as sputtering targets. Ar and N 2 gas were used as sputtering gas and reactive gas, with the flow rates of 8 and 4 sccm, respectively. The Zr sputtering current was fixed at 0.6 A and Ti sputtering current varied from 0.6 to 1.2 A. The deposition time for all the deposited films was 60 min. The effects of Ti sputtering current on the structure and morphology of the films were investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM). It was found that all the prepared films were (Ti,Zr)N solid solution. Furthermore, the lattice parameter was found to decrease whereas the crystallite size, RMS roughness and film thickness increased with increasing Ti sputtering current. As a result, the crystallinity of the films increased what is in agreement with XRD results.
- K. Chu, P. W. Shum and Y. G. Chen, “Substrate Bias Effects on Mechanical and Tribological Properties of Substitutional Solid Solution (Ti,Al)N Films Prepared by Reactive Magnetron Sputtering,” Materials Science and Engineering B, Vol. 131, 2006, pp. 62-71. http://dx.doi.org/10.1016/j.mseb.2006.03.036
- R. Wuhrer and W. Y. Yeung, “Grain Refinement with Increasing Magnetron Discharge Power in Sputter Deposition of Nanostructured Titanium Nitride Coatings,” Scripta Materialia, Vol. 50, 2004, pp. 813-818. http://dx.doi.org/10.1016/j.scriptamat.2003.12.022
- K. H. Lee, C. H. Park, Y. S. Yoon and J. J. Lee, “Structure and Properties of (Ti1-xCrx)N Coatings Produced by the Ion-Plating Method,” Thin Solid Films, Vol. 385, 2001, pp. 167-173. http://dx.doi.org/10.1016/S0040-6090(00)01911-8
- G. S. Kim, B. S. Kim, S. Y. Lee and J. H. Hahn, “Structure and Mechanical Properties of Cr-Zr-N Films Synthesized by Closed Field Unbalanced Magnetron Sputtering with Vertical Magnetron Sources,” Surface & Coatings Technology, Vol. 200, 2005, pp. 1669-1675. http://dx.doi.org/10.1016/j.surfcoat.2005.08.101
- S. M. Aouadi, T. Maeruf, R. D. Twesten, D. M. Mihut and S. L. Rohde, “Physical and Mechanical Properties of Zirconium Nitride Thin Films,” Surface & Coatings Technology, Vol. 200, 2006, pp. 3411-3417. http://dx.doi.org/10.1016/j.surfcoat.2005.02.169
- H. Hasegawa, A. Kimura and T. Suzuki, “Microhardness and Structural Analysis of (TI,AI)N, (Ti,Cr)N, (Ti,Zr)N, and (TI,V)N, Films,” Journal of Vacuum Science & Technology A, Vol. 18, 2000, pp. 1038-1040. http://dx.doi.org/10.1116/1.582296
- P. W. Shum, K. Y. Li, Z. F. Zhou and Y. G. Shen, “Structural and Mechanical Properties of Titanium-Aluminium Nitride Films Deposited by Reactive Close-Field Unbalanced Magnetron Sputtering,” Surface & Coatings Technology, Vol. 185, 2004, pp. 245-253. http://dx.doi.org/10.1016/j.surfcoat.2003.12.011
- O. Knotek, W. D. Munz and T. Keyendecker, “Industrial Aeposition of Binary, Ternary, and Quarternary Nitrides of Titanium, Zirconium and Aluminum,” Journal of Vacuum Science & Technology A, Vol. 5, 1987, pp. 2173-2179. http://dx.doi.org/10.1116/1.574948
- N. Ichimiya, Y. Onishi and Y. Tanaka, “Properties and Cutting Performance of (Ti,V)N Coatings Prepared by Cathodic Arc Ion Patting,” Surface & Coatings Technology, Vol. 200, 2005, pp. 1377-1382. http://dx.doi.org/10.1016/j.surfcoat.2005.08.026
- T. Deeleard, S. Chaiyakun, A. Pokaipisit and P. Limsuwan, “Effects of Vanadium Content on Structure and Chemical State of TiVN Films and Prepared by Reactive DC Magnetron Co-Sputtering,” Materials Sciences and Application, Vol. 4, 2013, pp. 556-563. http://dx.doi.org/10.4236/msa.2013.49068