A TEM Study of Cobalt-Base Alloy Prototypes Fabricated by EBM
- 1
- 2
- 3
- 4
- 5
- 6
- 7
- 8
- 9
Abstract
A novel microstructural architecture consisting of Cr<sub>23</sub>C<sub>6</sub> carbide spatial columns was created in solid components of Co-26Cr-6Mo-0.2C fabricated from powder by additive manufacturing using electron beam melting. These columns of carbides extended in the build direction and are formed by the x-y rastering of the electron beam to pre-heat and melt powder layers using CAD models. These microstructural architectures are similar to rapidly solidified/unidirectionally solidified structures created by heat extraction in the direction perpendicular to the build plane. These columnar carbide architectures were observed by optical metallography and transmission electron microscopy (TEM) and compared with intrinsic stacking fault microstructures observed in annealed components. The TEM analysis allowed the details of the carbide crystal structure and corresponding cubic morphology to be observed.
- R. Roy, “Materials Science and Engineering in the United States,” The Pennsylvania State University Press, State College, 1970.
- Materials Science and Engineering for the 1990s, “Maintaining Competitiveness in the Age of Materials,” Na-tional Academy Press, Washington, 1989.
- G. A. Chadwick, “Eutectic Solidification,” In: T. J. Hughel, Ed., Liq-uids: Structure, Properties, Solid Interactions, Elsevier, New York, 1965, pp. 238-255.
- H. W. Weart and J. D. Mack, “Eutectic Solidification Structures,” Transactions of the Metal-lurgical Society of AIME, Vol. 212, 1958, pp. 664-671.
- R. W. Kraft, “Eutectic Solidification,” Journal of Metals, Vol. 8, No. 2, 1966, pp. 192-198.
- S. M. Gaytan, L. E. Murr, E. Martinez, J. L. Martinez, B. I. Machado, D. A. Ramirez, F. Medina, S. Collins and R. B. Wicker, “Comparisons of Micro-structures and Mechanical Properties for Solid and Mesh Co-balt-Base Alloy Prototypes Fabricated by Electron Beam Melt-ing,” Metallurgical and Materials Transactions A, Vol. 41, No. 12, 2010, pp. 3216-3227. doi:10.1007/s11661-010-0388-y
- A. Strondl, R. Fischer, G. Frommeyer and A.Schneider, “Investigations of MX and γ’/γ’’ precipitates in the Nickel-based Superalloy 718 Produced by Electron Beam Melting,” Materials Science and Engineering A, Vol. 480, No. 1-2, 2008, pp. 138-147. doi:10.1016/j.msea.2007.07.012
- C. T. Sims, N. S. Stoloff and W. C. Hagel, “Superalloys II,” John Wiley & Sons, New York, 1987.
- G. D. Janaki, “Microstructure and Wear Properties of LENS? Deposited Medical Grade CoCrMo,” Journal of Materials Science: Materials in Medicine, Vol. 19, No. 5, 2008, pp. 2105-2111. doi:10.1007/s10856-007-3078-6
- J. Cawley, J. E. P. Metcalf, A. H. Jones, T. J. Band and D. S. Skupien, “A Tri-bological Study of Cobalt Chromium Molybdenum Alloys Used in Metal-on-Metal Resurfacing Hip Arthroplasty,” Wear, Vol. 255, No. 7-12, 2003, pp. 999-1006. doi:10.1016/S0043-1648(03)00046-2
- L. E. Murr, E. V. Esquivel, S. A. Quinones, S. M. Gaytan, M. I. Lopez, E. Y. Martinez, F. Medina, D. H. Hernandez, E. Martinez, J. L. Mar-tinez, S. W. Stafford, D. K. Brown, T. Hoppe, W. Meyers, U. Lindhe and R. B. Wicker, “Microstructures and Mechanical Properties of Electron Beam-Rapid Manufactured Ti-6Al-4V Biomedical Prototypes Compared to Wrought Ti-6Al-4V,” Materials Characterization, Vol. 60, No. 2, 2009, pp. 96-105. doi:10.1016/j.matchar.2008.07.006