Effect of Silane Coupling Agent on the Flexural Property of Glass Fiber Reinforced Composite Film
- 1 Department of Polymer Science & Engineering, Pusan National University, Busan, Korea
- 2 Department of Polymer Science & Engineering, Pusan National University, Busan, Korea
- 3 Department of Polymer Science & Engineering, Pusan National University, Busan, Korea
- 4 Department of Polymer Science & Engineering, Pusan National University, Busan, Korea
- 5 Department of Polymer Science & Engineering, Pusan National University, Busan, Korea
Abstract
Transparent glass fiber reinforced composites films ware fabricated by UV light induced chemical crosslinking of composite materials consisting of glass fiber and UV curable resin in film state. In order to apply film to flexible device, excellent flexural property is required, then the delamination should not occurred between glass fiber and UV curable resin when film is bent. To minimize delamination and improve the interfacial adhesion at interface between glass fiber and UV curable resin, the γ-aminopropyl triethoxy silane and γ-glycid oxypropyl trimethoxy silane were applied for the surface treatment of glass fibers. Silanization of glass fiber surface was checked by scanning electron microscopy and the degree of delamination of composite film was confirmed through the bending test, ASTEM290-96a, used by haze meter.
- Park, S.-J. and Jin, J.-S. (2001) Effect of Silane Coupling Agent on Interphase and Performance of Glass Fiber/Unsaturated Polyester Compoiste. Journal of Colloid and Interface Science, 242, 174-179. http://dx.doi.org/10.1006/jcis.2001.7788
- Ryu, S.C., Kim, J.W. and Park, L.S. (2009) Fabrication of Glass Fiber Reinforced Composite Film for Flexible Organic Light Emitting Diode Devices. Mol. Cryst. Liq. Cryst., 514, 331-343.
- Agrawal, R., Saxena, N.S., Sreekala, M.S. and Thomas, S. (2000) Effect of Treatment on the Thermal Conductivity and Thermal Iffusivity of Oil-Palm-Giber-Reinforced Phenolformaldehyde Composites. Journal of Polymer Science Part B: Polymer Physics, 38, 916-921. http://dx.doi.org/10.1002/(SICI)1099-0488(20000401)38:7 3.3.CO;2-S
- M?der, E. and Pisanova, E. (2000) Characterization and Design of Interphases in Glass Giber Reinforced Polyproplyene. Polymer Composites, 21, 361-368. http://dx.doi.org/10.1002/pc.10194?
- Elley-Bristow, D.M., Bellinger, M.A., Sauer, J.A. and Hara, M. (1999) Interfacial Bonding of Silica Glass Giber to Polystyrene Ionomers. Journal of Polymer Science Part B: Polymer Physics, 37, 2705-2710. http://dx.doi.org/10.1002/(SICI)1099-0488(19990915)37:18 3.0.CO;2-C
- Bayer, T., Eich-horn, K.-J., Grundke, K. and Jacobasch, H.-J. (1999) FTIR Spectroscopic Studies of Interfacial Reactions between Amino Functionalized Silicon Surfaces and Molten Maleic Anhydride Copolymers. Macromolecular Chemistry and Physics, 200, 852-857.
- Tragoonwichian, S., Yanumet, N. and Ishida, H. (2006) Effect of Fiber Surface Modification on the Mechanical Properties of Sisal Fiber-Reinforced Benzoxazine/Epoxy Composites Based on Aliphatic Diamine Benzoxazine. Journal of Applied Polymer Science, 106, 2925-2935. http://dx.doi.org/10.1002/app.25797
- Shibahara, S., Shimobe, Y. and Kuramoto, H. EP Patent NO.1477529A1.