Corrosion Behaviour of Aluminium Engine Block in 3.5% NaCl Solution
- 1 Directorate of Advisory, Extension and Research Services Bangladesh University of Engineering and Technology, Dhaka, Bangladesh
- 2 Institute of Appropriate Technology Bangladesh University of Engineering and Technology, Dhaka, Bangladesh
Abstract
In the present work, the corrosion behavior of aluminium alloy engine block in 3.5% NaCl solution was studied. The work was carried out using conventional gravimetric measurements and complemented by scanning electron microscopy (SEM) and X-ray analyzer (EDX) investigations. The results obtained indicate that the main process the alloy undergoes, under the medium of exposure studied, is related to localized corrosion that takes place as a consequence of the process of alkalinization around the cathodic precipitates existing in the alloy. The alloy suffers a process of corrosion localized to the area surrounding the precipitates of the Al (Si, Mg) and Al-Mg, which resulted in hemispherical pits. This identification was confirmed by SEM and EDX analysis. No evidence was found of the formation of crystallographic pitting for exposure times up to 54 days. Gravimetric analysis confirmed that with varying exposure periods the weight loss of the alloy increases and the corrosion rate decreases with time.
- Evans, R.U. (1963) An Introduction to Metallic Corrosion. Edward Arnold Publishers, London.
- Smialowska, Z.S. (1986) Pitting Corrosion of Metals. NACE, Houston, TX.
- Mareus, P. and Oudart, J. (1995) Corrosion Mechanism in Theory and Practice. Marcel Dekker, New York.
- Sherif, E.M. (2012) Corrosion Behavior of Magnesium in Naturally Aerated Stagnant Seawater and 3.5% Sodium Chloride Solutions. Int. J. Electrochem. Sci., 7, 4235-4249.
- Aballe, A., Bethencourt, M., Botana, F.J., Cano, M.J. and Marcos, M. (2001) Localized Alkaline Corrosion of Alloy AA5083 in Neutral 3.5% NaCl Solution. Corrosion Science, 43, 1657-1674.
- Osorio, W.R., Cheung, N., Peixoto, L.C. and Garcia, A. (2009) Corrosion Resistance and Mechanical Properties of an Al 9wt%Si Alloy Treated by Laser Surface Remelting. International Journal of Electrochemical Science, 4, 820-831.
- Sherif, E.M. and Almajid, A.A. (2011) Corrosion of Magnesium/Manganese Alloy in Chloride Solutions and Its Inhibition by 5-(3-Aminophenyl)-tetrazoleInt. International Journal of Electrochem. Science, 6, 2131-2148.
- Chaudhury, S.K., Warke, V., Shankar, S. and Apelian, D. (2011) Localized Recrystallization in Cast Al-Si-Mg Alloy during Solution Heat Treatment: Dilatometric and Calorimetric Studies. Metallurgical and Materials Transactions A, 42A, 3160-3169.
- Davoodi, A. (2008) Mechanistic Studies of Localized Corrosion of Al Alloys by High Resolution in-Situ and ex-Situ Probing Techniques. Ph.D. Thesis, Universitetsservice US-AB, Stockholm.