In this paper, smooth specimens of three aluminum alloys: AA 2219-T8, AA 2519-T8 and AA 2624-T351, were subjected to the same level of uniaxial (tension/compression) fatigue loading to compare their fatigue responses. Fractographic investigations of the failed specimens after fatigue loading was also conducted using a scanning electron microscope. The fatigue test results showed considerable differences in the fatigue lives of the three investigated alloys with AA 2219-T8 having the shortest fatigue life and AA 2624-T351 the longest fatigue life. The fractographic analysis showed that coalescence of micropores, microvoids, particles cleavage and microcracks are the predominant features in the fracture surface of AA 2219-T8. The fracture surface features of AA 2519-T8 revealed higher resistance to fatigue cracks nucleation and growth when compared to AA 2219-T8. The features depicted mainly partly ductile and partly brittle fracture. The AA 2624-T351 fracture surface features revealed noteworthy ductile failure mechanism. The results suggest a strong correlation between the surface fractographic features and the fatigue lives of the alloys. It is also observed that in addition to the yield strengths and ultimate tensile strengths, the total strain energy densities (SED) may provide a reasonable indication of the relative fatigue performance of the three alloys. AA 2219-T8 had the lowest SED and the lowest fatigue life, while AA 2624-T351 had the highest SED and the highest fatigue life. Thus, AA 2624-T351 would be the most suitable materials for components subjected to fatigue loading.
KeywordsFatigue LifeAluminum AlloyStrain Energy DensityFractography
Strivatsan, T.S., Vasudevan, S., Park, L. and Lederich, R.J. (2008) The Quasi-Static Deformation and Final Fracture Behaviour of Aluminum Alloy 2219. Materials Science and Engineering: A, 497, 270-277. https://doi.org/10.1016/j.msea.2008.07.033
Alexopoulos, N.D., Migklis, E., Stylianos, A. and Myriounis, D.P. (2013) Fatigue Behaviour of the Aeronautical Al-Li (2198) Aluminum Alloy under Constant Amplitude Loading. International Journal of Fatigue, 56, 95-105. https://doi.org/10.1016/j.ijfatigue.2013.07.009
Guerin, M., Alexis, J., Andrieu, E., Blanc, C. and Odemer, G. (2015) Corrosion-Fatigue Lifetime of Aluminium-Copper-Lithium Alloy 2050 in Chloride Solution. Materials & Design, 87, 681-692. https://doi.org/10.1016/j.matdes.2015.08.003
Sayuti, M., Ahmed, A.D. and Handi, S.M. (2013) An Investigation of Optimum SiO2 Nanolubrication Parameters in End Milling of Aerospace Al6061-T6 Alloy. International Journal of Advanced Manufacturing Technology, 67, 833-849. https://doi.org/10.1007/s00170-012-4527-z
Li, H. and Lu, X. (2015) Springback and Tensile Strength of 2A97 Aluminium Alloy during Age Forming. Transactions of Nonferrous Metals Society of China, 25, 1043-1049. https://doi.org/10.1016/S1003-6326(15)63696-2
Bobbili, R., Madhu, V. and Gogia, A.K. (2016) Tensile Behaviour of Aluminium 7017 Alloy at Various Temperatures and strain Rates. Journal of Materials Research and Technology, 5, 190-197. https://doi.org/10.1016/j.jmrt.2015.12.002
Pourbahari, B. and Emamy, M. (2016) Effects of La Intermetallics on the Structure and Tensile Properties of Thin Section Gravity Die-Cast A 357 Al Alloy. Materials & Design, 94, 111-120. https://doi.org/10.1016/j.matdes.2016.01.039
Cadoni, E., Dotta, M., Forni, D. and Kaufmann, H. (2017) Tensile Behavior of Commercial Aluminium Alloys Used in Armour Applications at High Strain Rate. Procedia Engineering, 197, 168-175. https://doi.org/10.1016/j.proeng.2017.08.093
Graham, W.R., Hall, C.A. and Morales, M.V. (2014) The Potential of Future Aircraft Technology for Noise and Pollutant Emissions Reduction. Transport Policy, 34, 36-51. https://doi.org/10.1016/j.tranpol.2014.02.017
Tsai, W., Chang, Y., Li, S., Chei, H. and Chu, P. (2014) A Green Approach to the Weight Reduction of Aircraft Cabins. Journal of Air Transport Management, 40, 65-77. https://doi.org/10.1016/j.jairtraman.2014.06.004
Huang, R., Riddle, M., Graziano, D., Warren, J., Das, S., Nimbalkar, S., Cresko, J. and Masanet, E. (2016) Energy and Emissions Saving of Additive Manufacturing: The Case of Lightweight Aircraft Components. Journal of Cleaner Production, 135, 1559-1570. https://doi.org/10.1016/j.jclepro.2015.04.109
Bruekner, J.K. and Abreu, C. (2017) Airline Fuel Usage and Carbon Emissions: Determining Factors. Journal of Air Transport Management, 62, 10-17. https://doi.org/10.1016/j.jairtraman.2017.01.004
Xue, Y., Kadiri, H.E., Horsfemeyer, M.F., Jordan, J.B. and Weiland, H. (2007) Micromechanism of Multistage Fatigue Crack Growth in a High-Strength Aluminum Alloy. Acta Materialia, 55, 1975-1984. https://doi.org/10.1016/j.actamat.2006.11.009
Gupta, V.K. and Agnew, S.R. (2011) Fatigue Crack Surface Crystallography near Crack Initiating Particle Clusters in Precipitation Hardened Legacy and Modern Al-Zn-Mg-Cu Alloys. International Journal of Fatigue, 33, 1159-1174. https://doi.org/10.1016/j.ijfatigue.2011.01.018
Carpio, F.J., Araujo, D., Pacheco, F.J., Mendez, D., Garcia, A.J., Villar, M.P., Garcia, R., Jimenez, D. and Rubio, L. (2003) Fatigue Behaviour of Laser Machined Aluminium Alloy. Applied Surface Science, 208-209, 194-198. https://doi.org/10.1016/S0169-4332(02)01369-7
Desmukh, M.N., Pandey, R.K. and Mukhopadhyay, A.K. (2005) Fatigue Behavior of 7010 Aluminum Alloy Containing Scandium. Scripta Materialia, 52, 645-650. https://doi.org/10.1016/j.scriptamat.2004.11.018
Wang, Q.Y., Kawagoishi, N. and Chen, Q. (2006) Fatigue and Fracture Behaviour of Structural Al-Alloys up to Very Long Life Regimes. International Journal of Fatigue, 28, 1572-1576. https://doi.org/10.1016/j.ijfatigue.2005.09.017
Ceschini, L., Morri, A. and Sambogna, G. (2008) The Effect of Hot Isostatic Pressing on the Fatigue Behaviour of Sand-Cast A356-T6 and A204-T6 Aluminum Alloys. Journal of Materials Processing Technology, 204, 231-238. https://doi.org/10.1016/j.jmatprotec.2007.11.067
Sharma, V.M.J., Kumar, K.S., Rao, B.N. and Pathak, S.D. (2011) Fatigue Crack Growth of AA2219 under Different Aging Conditions. Materials Science and Engineering: A, 528, 4040-4049. https://doi.org/10.1016/j.msea.2011.01.055
Zheng, Z.Q., Cai, B., Zhai, T. and Li, S.C. (2011) The Behavior of Fatigue Crack Initiation and Propagation in AA2524-T34 Alloy. Materials Science and Engineering: A, 528, 2017-2022. https://doi.org/10.1016/j.msea.2010.10.085
Ma, Y.E., Zhao, Z., Liu, B. and Li, W. (2013) Mechanical Properties and Fatigue Crack Growth Rates in Friction Stir Welded Nugget of 2198-T8 Al-Li Alloy Joints. Materials Science and Engineering: A, 569, 41-47. https://doi.org/10.1016/j.msea.2013.01.044
Yan, L. and Fan, J. (2016) In-Situ SEM Study of Fatigue Crack Initiation and Propagation Behavior in 2524 Aluminum Alloy. Materials & Design, 110, 592-601. https://doi.org/10.1016/j.matdes.2016.08.004
Shou, W.B., Yi, D.Q., Liu, H.Q., Tang, C., Sheu, F.H. and Wang, B. (2016) Effect of Grain Size on the Fatigue Crack Growth Behavior of 2524-T3 Aluminum Alloy. Archives of Civil and Mechanical Engineering, 16, 304-312. https://doi.org/10.1016/j.acme.2016.01.004
Wu, W., Liu, Z., Bai, S., Li, F., Liu, M. and Wang, A. (2017) Anisotropy in Fatigue crack Propagation Behavior of Al-Cu-Li Alloy Thick Plate. Materials Characterization, 131, 440-449. https://doi.org/10.1016/j.matchar.2017.07.025
Ovono, D.O., Guillot, I. and Massinon, D. (2008) Study on Low-Cycle Fatigue Behaviours of the Aluminium Cast Alloys. Journal of Alloys and Compounds, 452, 425-431. https://doi.org/10.1016/j.jallcom.2006.11.052
Takahashi, Y., Shikama, T., Yoshihara, S., Aiupa, T. and Noguchi, H. (2012) Study on Dominant Mechanism of High-Cycle Fatigue Life in 6061-T6 Aluminum Alloy through Microanalyses of Microstructurally Small Cracks. Acta Materialia, 60, 2554-2567. https://doi.org/10.1016/j.actamat.2012.01.023
Sivaraj, P., Kanagarajau, D. and Balasubramanian, V. (2014) Fatigue Crack Growth Behaviour of Friction Stir Welded AA7075-T651 Aluminium Alloy Joints. Transactions of Nonferrous Metals Society of China, 24, 2459-2467. https://doi.org/10.1016/S1003-6326(14)63371-9
Aboulkair, N.T., Maskery, I., Tuck, C., Ashcraft, I. and Everitt, N.M. (2016) Improving the Fatigue Behaviour of Selectively Laser Melted Aluminium Alloy. Influence of Heat Treatment and Surface Quality. Materials & Design, 104, 174-182. https://doi.org/10.1016/j.matdes.2016.05.041
Szusta, J. and Sewryn, A. (2017) Experimental Study of the Low-Cycle Fatigue Life under Multiaxial Loading of Aluminum Alloy EN AW-2024-T3 at Elevated Temperatures. International Journal of Fatigue, 96, 28-42. https://doi.org/10.1016/j.ijfatigue.2016.11.009
Wang, J.T., Zhang, Y.K., Chen, J.F., Zhou, J.Y., Luo, K.Y., Tan, W.S., Sun, L.Y. and Lu, Y.L. (2017) Effect of Laser Shock Peening on the High-Temperature Fatigue Performance of 7075 Aluminum Alloy. Materials Science and Engineering: A, 704, 459-468. https://doi.org/10.1016/j.msea.2017.08.050
Strivatsa, T.S., Kolar, D. and Magnusen, P. (2002) The Cyclic Fatigue and Final Fracture Behaviour of Aluminum Alloy. Materials & Design, 23, 129-139. https://doi.org/10.1016/S0261-3069(01)00070-X
Giummarra, C., Bray, G.H. and Duquette, D.J. (2006) Fretting Fatigue in 2XXX Series Aerospace Aluminium Alloys. Tribology International, 39, 1206-1212. https://doi.org/10.1016/j.triboint.2006.02.010
Fersini, D. and Pirondi, A. (2007) Fatigue Behavior of Al2024-T3 Friction Stir Welded Lap Joints. Engineering Fracture Mechanics, 74, 468-480. https://doi.org/10.1016/j.engfracmech.2006.07.010
Malarvizhi, S., Raghukandan, K. and Viswanathan, N. (2008) Fatigue Behaviour of Post Weld Heat Treated Electron Beam Welded Aluminum Alloy Joints. Materials & Design, 29, 1562-1567. https://doi.org/10.1016/j.matdes.2007.11.005
Menzemer, C.C., Azzan, D. and Strivatsan, T.S. (2010) A Study of Fatigue and Fracture Response of Cantilevered Luminaire Structures Made from Aluminum Alloy 6063. Materials Science and Engineering: A, 527, 4680-4686. https://doi.org/10.1016/j.msea.2010.03.085
Priet, B., Odemer, G., Blanc, C., Giffard, K. and Arurault, L. (2016) Effect of New Sealing Treatments on Corrosion Fatigue Lifetime of Anodized 2024 Aluminium Alloy. Surface and Coatings Technology, 307, 206-219. https://doi.org/10.1016/j.surfcoat.2016.07.083
Fitzka, M. and Mayer, H. (2016) Constant and Variable Amplitude Fatigue Testing of Aluminum Alloy 2024-T351 with Ultrasonic and Servo-Hydraulic Equipment. International Journal of Fatigue, 91, 363-372. https://doi.org/10.1016/j.ijfatigue.2015.08.017
Skorupa, M., Machniewicz, T., Skorupa, A. and Korbel, A. (2016) Fatigue Life Predictions for Riveted Lap Joints. International Journal of Fatigue, 94, 41-57. https://doi.org/10.1016/j.ijfatigue.2016.09.007
Huang, Y., Li, H., Yang, X., Guan, Z., Li, Z. and Sun, Y. (2017) Improving the Fatigue Life of 2297-T87 Aluminum-Lithium Alloy Lugs by Cold Expansion, Interference Fitting, and their Combination. Journal of Materials Processing Technology, 249, 67-77. https://doi.org/10.1016/j.jmatprotec.2017.06.004
Xu, L., Yu, X., Hui, L. and Zhou S. (2017) Fatigue Prediction of Aviation Aluminium Alloy Based on Quantitative Pre-Corrosion Damage Analysis. Transactions of Nonferrous Metals Society of China, 27, 1353-1362. https://doi.org/10.1016/S1003-6326(17)60156-0
Hemmouche, L., Fares, C. and Belouchrani, M.A. (2013) Influence of Heat Treatment and Anodization on Fatigue Life of 2017A Alloy. Engineering Failure Analysis, 35, 554-561. https://doi.org/10.1016/j.engfailanal.2013.05.003
Hao, H., Ye, D. and Chen, C. (2014) Strain Ratio Effects on Low-Cycles Fatigue Behaviour and Deformation Microstructure of 2124-T851 Aluminum Alloy. Materials Science and Engineering: A, 605, 151-159. https://doi.org/10.1016/j.msea.2014.03.040
Fares, C., Hemmouche, L., Belouchrani, M.A., Amrouche, A., Chicot, D. and Puchi-Cabrera, E.S. (2015) Coupled Effects of Substrate Microstructure and Sulphuric Acid Anodizing on Fatigue Life of a 2017A Aluminum Alloy. Materials & Design, 86, 723-734. https://doi.org/10.1016/j.matdes.2015.07.120
Stanley, D., Twerbuch, J., Tan, T. and Anasori, B. (2016) Reconstruction of Fatigue Crack Growth in AA2024-T3 and AA2198-T8 Fastened Lap Joints. Theoretical and Applied Fracture Mechanics, 82, 33-50. https://doi.org/10.1016/j.tafmec.2015.06.006
Jayaraman, N., Prevey, P. and Mahoney, M. (2003) Fatigue Improvement of Aluminum Alloy FSW with Low Plasticity Burnishing. Proceedings of the 132nd TMS, San Diego, CA, 2-6 March 2003, 1-10.
Xu, W.F., Liu, J.H., Chen, D.L. and Luan, G.H. (2014) Low-Cycle Fatigue of a Friction Stir Welded 2219-T62 Aluminum Alloy at Different Welding Parameters and Cooling Conditions. International Journal of Advanced Manufacturing Technology, 74, 209-218. https://doi.org/10.1007/s00170-014-5988-z
ASTM E466-15 (2015) Standard Practice for Conducting Force Controlled Constant Amplitude Axial Fatigue Tests of Metallic Materials. ASTM International, West Conshohocken, PA.
ASTM E606/E606M-12 (2012) Standard Test Method for Strain-Controlled Fatigue Testing. ASTM International, West Conshohocken, PA.
Tang, K.K., Wu, H. and Berto, F. (2015) Fatigue Data Interpretation of 7075-T6 Al Sheets by Energy Density Factor in a Dual Scale Model. Theoretical and Applied Fracture Mechanics, 79, 98-104. https://doi.org/10.1016/j.tafmec.2015.06.012
Rambabu, P.R., Narasayya, C.V.A., Mohan, M.K. and Prasad, N.E. (2015) Mixed Mode (I/III) Fracture Behaviour of an Aerospace Grade Aluminium Alloy in Different Ageing Conditions. Materials Today: Proceedings, 2, 1741-1746. https://doi.org/10.1016/j.matpr.2015.07.008