The aim of this study is to use Cocoa Cortex Ash (CCA) as alternative fluxing agent to manufacture vitrified ceramics at low temperatures from alluvial clay. Specimens of mixtures including clay and CCA (0%, 10%, 20% and 30% by mass) were used and fired respectively at 1050 ° C and 1100 ° C. X-ray diffraction and scanning electron microscopy were carried out. γ -alumine, mullite, akermanite, anorthite and grossular are new crystalline phases formed. Also, technological properties were determined on fired specimens as a function of CCA mass percentage. The results showed that firing shrinkage increased up to 8.5% for specimens with 10% by mass of CCA, then lessened up to 2% for specimens with 30% by mass of CCA. When fired at 1100 ° C, the specimens that initially contained 10% by mass of CCA allowed the formation of compact bodies with water absorption of 2% and flexural strength of 32 MPa. Hence, mixed at low percentage with poorly fluxing kaolinite clay, CCA can be used successfully as flux for the production of vitrified ceramics such as stoneware at low temperatures. The mixture of CCA with kaolinitic clay also promotes the formation of mullite and anorthite at low temperature.
Boch, P. and Niepce, J.C. (2006) Ceramic Materials. ISTE Limited, France. https://doi.org/10.1002/9780470612415
Njoya, D., Hajjaji, M., Baçaoui, A. and Njopwouo, D. (2010) Microstructural Characterization and Influence of Manufacturing Parameters on Technological Properties of Vitreous Ceramics Materials. Materials Characterization, 61, 289-295. https://doi.org/10.1016/j.matchar.2009.12.009
Lemougna, P.N., Melo, U.C., Kamseu, E. and Tchamba, A.B. (2011) Laterit Based Stabilized Product for Sustainable Building Application in Tropical Countries. Review and Prospect for the Case of Cameroon. Sustainability, 3, 293-305. https://doi.org/10.3390/su3010293
Permana, K.W.S., Paramarta, I.B.A. and Sumadiyasa, A.S.M. (2019) Stoneware Ceramic Synthesis with Iron Sand as a Filler Material. Journal of Materials Science and Chemical Engineering, 7, 42-51. https://doi.org/10.4236/msce.2019.78006
Touolak, B.T. and Nya, F.T. (2014) More Value of Maroua Clay in the Formulation of Ceramic Products (Terracotta, Earthenware, Stoneware, Porcelain). Advances in Materials Physics and Chemistry, 4, 284-299. https://doi.org/10.4236/ampc.2014.412031
Staneva, N. and Kasabov, I. (1996) Influence of Electrolyte on the Casting Properties of Porcelain Slips. Interceram, 45, 12-15.
Ergul, S., Akyildiz, M. and Karamanov, A. (2007) Ceramic Material from Basaltic Tuffs. Industrial Ceramics, 27, 1-7.
Esposito, L., Salem, A., Tucci, A., Gualtieri, A. and Jazayeri, S.H. (2005) The Use of Nepheline Syenite in a Body Mix for Porcelain Stoneware Tiles. Ceramics International, 31, 233-240. https://doi.org/10.1016/j.ceramint.2004.05.006
Das, S.K., Dana, K., Singh, N. and Sarkar, R. (2005) Shrinkage and Strength Behaviour of Quartzitic and Kaolinitic Clays in Wall Tile Composition. Applied Clay Science, 29, 137-143. https://doi.org/10.1016/j.clay.2004.10.002
Vu, D.H., Wang, K.S., Chen, J.H. and Bac, B.X. (2012) Glass-Ceramic from Mixtures of Bottom Ash and Fly Ash. Waste Management, 32, 2306-2314. https://doi.org/10.1016/j.wasman.2012.05.040
Kamseu, E., Bakop, T., Djangang, C., Melo, U.C., Hanuskova, M. and Leonelli, C. (2013) Porcelain Stoneware with Pegmatite and Nepheline Syenite Solid Solutions: Pore Size Distribution and Descriptive Microstructure. Journal of the European Ceramic Society, 33, 2775-2784. https://doi.org/10.1016/j.jeurceramsoc.2013.03.028
Njindam, O.R., Njoya, D., Mache, J.R., Mouafon, M., Messan, A. and Njopwouo, D. (2018) Effect of Glass Powder on the Technological Properties and Microstructure of Clay Mixture for Porcelain Stoneware Tiles Manufacture. Construction and Building Materials, 170, 512-519. https://doi.org/10.1016/j.conbuildmat.2018.03.069
Slavova, G. (2017) Global and Domestic Bulgarian Production of Cocoa and Chocolate Articles for the Period 2013-2016. Trakia Journal of Sciences, 15, 10-17. https://doi.org/10.15547/tjs.2017.s.01.003
Fallo, J. (1999) Séminaire d’information sur les sous-produits du cacao. Fiche d’information, Ministère de la Recherche Scientifique et de l’Innovation. IRAD, Yaoundé.
GretbagMacbeth (2000) Munsell Soil Color Charts. GretbagMacbeth, New Windsor.
ASTM C 326-03. Standard Test Method for Drying and Firing Shrinkage of Ceramic Whiteware Clays. PA 19428-2959, United States. 1-2.
ISO 10545-3 Carreaux et dalles céramiques. Partie 3: Détermination de l’absorption d’eau, de la porosité ouverte, de la densité relative apparente et de la masse volumique globale. 1-3.
ISO 10545-4 Carreaux et dalles céramiques. Partie 4: Détermination de la résistance à la flexion et de la force de rupture 1-4.
Pialy, P., Nkoumbou, C., Villiéras, F., Razafitianamaharavo, A., Barrès, O., Pelletier, M., Llivier, G., Bihannic, I., Njopwouo, D., Yvon, J. and Bonnet, J.P. (2008) Characterization for Industrial Applications of Clays from Lembo Deposit, Mount Bana (Cameroon). Clay Minerals, 43, 415-435. https://doi.org/10.1180/claymin.2008.043.3.07
Nkoumbuo, C., Njoya, A., Njoya, D., Grobois, C., Njopwwouo, D., Coutin-Nomade, A., Yvon, J. and Martin, F. (2009) Kaolin from Mayouom (Western Cameroon): Industrial Suitability Evaluation. Applied Clay Science, 43, 118-124. https://doi.org/10.1016/j.clay.2008.07.019
Nzeukou, A.N., Flagel, N., Njoya, A., Kamgang, V.B., Medjo, R.E. and Melo, U.C. (2013) Mineralogy and Physic Chemical Properties of Alluvial Clays from Sanaga Valley (Center, Cameroon): Suitability for Ceramics Application. Applied Clay Science, 83-84, 238 243. https://doi.org/10.1016/j.clay.2013.08.038
Konan, K.L., Sei, J., Soro, N.S., Oyetola, S., Gaillard, J.M., Bonnet, J.P. and Kra, G. (2006) Caractérisation de matériaux argileux du site d’Azaguie Blida (Anyama, Côte d’Ivoire) et détermination des propriétés mécaniques des produits céramiques. Journal de la Société Ouest-Africaine de Chimie, 21, 35-43.
Rozenstrauha, I., Bajare, D., Cimdins, R., Berzina, L., Bossert, J. and Boccaccini, A.R. (2006) The Influence of Various Additions on Glass-Ceramic Matrix Composition Based on Industrial Waste. Ceramics International, 32, 115-119. https://doi.org/10.1016/j.ceramint.2005.01.006
Lecomte, G., Pateyron, B. and Blanchart, P. (2004) Experimental Study and Simulation of a Vertical Section Mullite-Ternary Eutectic (985°C) in the SiO 2 -Al 2 O 3 -K 2 O System. Materials Research Bulletin, 39, 1469-1478. https://doi.org/10.1016/j.materresbull.2004.04.024
Lecomte, G.L., Bonnet, J.P. and Blanchart, P. (2007) A Study of the Influence of Muscovite on the Thermal Transformations of Kaolinite from Room Temperature up to 1100°C. Journal of Materials Science, 42, 8745-8752. https://doi.org/10.1007/s10853-006-0192-7
Lecomte, G.L., Bonnet, J.P. and Soro, N. (2013) Influence of Iron into the Structural Reorganization Process during the Sintering of Kaolins. Journal of the European Ceramic Society, 4, 661-668. https://doi.org/10.1016/j.jeurceramsoc.2012.10.024
Kamseu, E., Rizzuti, A., Leonelli, C. and Perera, D. (2010) Enhanced Thermal Stability in K 2 O-Metakaolin-Based Geopolymer Concretes by Al 2 O 3 and SiO 2 Fillers Addition. Journal of Materials Science, 45, 1715-1724. https://doi.org/10.1007/s10853-009-4108-1
Traore, K., Kabre, T.S. and Banchart, P. (2001) Sintering of Clay from Burkina Faso by Dilatometry, Influence of the Applied Load and the Pre-Sintering Heating Rate. Ceramics International, 27, 875-822. https://doi.org/10.1016/S0272-8842(01)00043-8
Seynou, M., Millogo, Y., Ouedraogo, R., Traoré, K. and Tirlocq, J. (2011) Firing Transformations and Properties of Tiles from a Clay from Burkina Faso. Applied Clay Science, 51, 499-502. https://doi.org/10.1016/j.clay.2011.01.002
Aliprandi, G. (1979) Matériaux réfractaires et céramiques techniques. Septima, Paris.
Elimbi, A. and Njopwwouo, D. (2002) Firing Characteristics of Ceramics from the Bomkoul Kaolinite Clay Deposit (Cameroon). Tile & Brick International, 18, 364-369.
Brindley, G.W. and Brown, G. (1980) Crystal Structures of Clay Minerals and Their X-Ray Identification. Mineralogical Society Monograph No. 5, London, Chapter 6. https://doi.org/10.1180/mono-5
Trindade, M.J., Dias, M.I., Coroado, J. and Rocha, F. (2008) Mineralogical Transformations of Calcareous Rich Clays with Firing: A Comparative Study between Calcite and Dolomite Rich Clays from Algarve, Portugal. Applied Clay Science, 42, 345-355. https://doi.org/10.1016/j.clay.2008.02.008
Vassileva, C. and Vassilev, S. (2004) Some Environmental Aspects Related to Sulphuremissions during Combustion of Bulgarian Coals. Comptes rendus de l’Academie Bulgare des Sciences, 57, 29-32.
Deniel, S. (2010) Elaboration et caractérisation de céramiques texturées de mullite à partir de phyllosilicates. PhD Dissertation, Université de Limoges, Limoges.
Sokolar, R. (2010) Effect of Calcite on the Brick Body Closing. Interceram, 59, 57-62.
Sokolar, R., Vodova, L., Grygarova, S., Stubna, I. and Sın, P. (2012) Mechanical Properties of Ceramic Bodies Based on Calcite Waste. Ceramics International, 38, 6607-6612. https://doi.org/10.1016/j.ceramint.2012.05.046
Elimbi, A., Dika, J.M. and Djangang, C.N. (2014) Effects of Alkaline Additives on the Thermal Behavior and Properties of Cameroonian Poorly Fluxing Clay Ceramics. Journal of Minerals and Materials Characterization and Engineering, 2, 484-501. https://doi.org/10.4236/jmmce.2014.25049
Dondi, M., Raimondo, M. and Zanelli, C. (2014) Clays and Bodies for Ceramic Tiles: Reappraisal and Technological Classification. Applied Clay Science, 96, 91-109. https://doi.org/10.1016/j.clay.2014.01.013