The deterioration of concrete over time is the result of various mechanical, physical, chemical and biological processes, with the corrosion of reinforcement being the most serious problem of durability of reinforced concrete structures. Over the last 50 years, a tremendous effort has been spent by the international scientific community with laboratory research and experimental field studies in order to increase the resistance of concrete over corrosion. This paper presents an experimental study of the corrosion behaviour of reinforced concrete beams with simultaneous sustained flexural loading. For this purpose, 40 reinforced concrete beams of 5 different compositions were constructed and exposed in simulated harmful environmental conditions in 3 different stress ratios for a total period of 42 months. Their behavior against corrosion was determined via regular measurements of the electrical resistance of concrete (according to ASTM G57) and the corrosion potential of the steel-reinforced bars with the use of copper sulphate (CSE) as reference electrode (according to ASTM C876). A theoretical calculation of the corrosion rate was conducted based on the electrochemical measurements of the beams. The results indicate that the corrosion potential of steel decreased in time and more rapidly after the initiation of the corrosion process; the electrical resistance firstly increased, remained stable for a short period and then decreased with the corrosion development, as expected. An inversely proportional relationship of the water/cement ratio of a composition with its corrosion behaviour as well as an analogous relationship between the cement content of a composition and its corrosion behaviour was observed. Also, the corrosion rate of steel is increased gradually with increasing load.
Martín-Pérez, Zibara, H., Hooton, R.D. and Thomas, M.D.A. (2000) Study of the Effect of Chloride Binding on Service Life Predictions. Cement and Concrete Research, 30, 1215-1223. https://doi.org/10.1016/S0008-8846(00)00339-2
Val, D.V. and Stewart, M.G. (2003) Life-Cycle Cost Analysis of Reinforced Concrete Structures in Marine Environments. Structural Safety, 25, 343-362. https://doi.org/10.1016/S0167-4730(03)00014-6
Poupard, O., L’Hostis, V., Catinaud, S. and Petre-Lazar, I. (2006) Corrosion Damage Diagnosis of a Reinforced Concrete Beam after 40 Years Natural Exposure in Marine Environment. Cement and Concrete Research, 36, 504-520. https://doi.org/10.1016/j.cemconres.2005.11.004
Berke, N.S. and Hicks, M.C. (1992) Estimating the Life Cycle of Reinforced Concrete Decks and Marine Piles Using Laboratory Diffusion and Corrosion Data. Symposium on Corrosion Forms and Control for Infrastructure, San Diego, 3-4 November 1991, 207-231.
Ouglova, A., Berthaud, Y., Foct, F., François, M., Ragueneau, F. and Petre-Lazar, I. (2008) The Influence of Corrosion on Bond Properties between Concrete and Reinforcement in Concrete Structures. Materials and Structures, 41, 969-980. https://doi.org/10.1617/s11527-007-9298-x
Tee, K.F. and Li, C.Q. (2011) A Numerical Study of Maintenance Strategy for Concrete Structures in Marine Environment. 11th International Conference on Applications of Statistics and Probability in Civil Engineering, Zurich, 1-4 August 2011, 618-625. https://doi.org/10.1201/b11332-94
Angst, U.M., Elsener, B., Larsen, C.K. and Vennesland, Ø. (2011) Chloride Induced Reinforcement Corrosion: Electrochemical Monitoring of Initiation Stage and Chloride Threshold Values. Corrosion Science, 53, 1451-1464. https://doi.org/10.1016/j.corsci.2011.01.025
Montemor, M., Simoes, A. and Ferreira, M. (2003) Chloride-Induced Corrosion on Reinforcing Steel: From the Fundamentals to the Monitoring Techniques. Cement and Concrete Composites, 25, 491-502. https://doi.org/10.1016/S0958-9465(02)00089-6
Cao, C., Cheung, M.M. and Chan, B.Y. (2013) Modelling of Interaction between Corrosion-Induced Concrete Cover Crack and Steel Corrosion Rate. Corrosion Science, 69, 97-109. https://doi.org/10.1016/j.corsci.2012.11.028
Zhang, F., Pan, J.S. and Lin, C.J. (2009) Localized Corrosion Behaviour of Reinforcement Steel in Simulated Concrete Pore Solution. Corrosion Science, 51, 2130-2138. https://doi.org/10.1016/j.corsci.2009.05.044
Alvarez, S., Bautista, A. and Velasco, F. (2011) Corrosion Behaviour of Corrugated Lean Duplex Stainless Steels in Simulated Concrete Pore Solutions. Corrosion Science, 53, 1748-1755. https://doi.org/10.1016/j.corsci.2011.01.050
Shi, J.J., Sun, W., Jiang, J.Y. and Zhang, Y.M. (2016) Influence of Chloride Concentration and Pre-Passivation on the Pitting Corrosion Resistance of Low-Alloy Reinforcing Steel in Simulated Concrete Pore Solution. Construction and Building Materials, 111, 805-813. https://doi.org/10.1016/j.conbuildmat.2016.02.107
Duffo, G., Morris, W., Raspini, I. and Saragovi, C. (2004) A Study of Steel Rebars Embedded in Concrete during 65 Years. Corrosion Science, 46, 2143-2157. https://doi.org/10.1016/j.corsci.2004.01.006
Zhao, Y.X., Yu, J. and Jin, W.L. (2011) Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion. Corrosion Science, 53, 3388-3397. https://doi.org/10.1016/j.corsci.2011.06.018
Wang, J.J., Basheer, P.A.M., Nanukuttan, S.V., Long, A.E. and Bai, Y. (2016) Influence of Service Loading and the Resulting Micro-Cracks on Chloride Resistance of Concrete. Construction and Building Materials, 108, 56-66. https://doi.org/10.1016/j.conbuildmat.2016.01.005
Poursaee, A. and Hansson, C.M. (2008) The Influence of Longitudinal Cracks on the Corrosion Protection Afforded Reinforcing Steel in High Performance Concrete. Cement and Concrete Research, 8, 1098-1105. https://doi.org/10.1016/j.cemconres.2008.03.018
Ababneh, A. and Sheban, M. (2011) Impact of Mechanical Loading on the Corrosion of Steel Reinforcement in Concrete Structures. Materials and Structures, 44, 1123-1137. https://doi.org/10.1617/s11527-010-9688-3
Shi, J.J. and Sun, W. (2010) Evaluation of Steel Corrosion in Concrete under Simultaneous Flexural Load and Chloride Attacks. Journal of the Chinese Ceramic Society, 38, 1201-1208.
Hariche, L., Ballim, Y., Bouhicha, M. and Kenai, S. (2012) Effects of Reinforcement Configuration and Sustained Load on the Behaviour of Reinforced Concrete Beams Affected by Reinforcing Steel Corrosion. Cement and Concrete Composites, 34, 1202-1209. https://doi.org/10.1016/j.cemconcomp.2012.07.010
Li, C.Q. (2000) Corrosion Initiation of Reinforcing Steel in Concrete under Natural Salt Spray and Service Loading-Results and Analysis. ACI Materials Journal, 97, 690-697. https://doi.org/10.14359/9983
Feng, X.G., Tang, Y.M. and Zuo, Y. (2011) Influence of Stress on Passive Behaviour of Steel Bars in Concrete Pore Solution. Corrosion Science, 53, 1304-1311. https://doi.org/10.1016/j.corsci.2010.12.030
Feng, X.G., Zuo, Y., Tang, Y.M., Zhao, X.H. and Lu, X.Y. (2011) The Degradation of Passive Film on Carbon Steel in Concrete Pore Solution under Compressive and Tensile Stresses. Electrochimica Acta, 58, 258-263. https://doi.org/10.1016/j.electacta.2011.09.035
Li, G.P., Hu, F.J. and Wu, Y.X. (2011) Chloride Ion Penetration in Stressed Concrete. Journal of Materials in Civil Engineering, 23, 1145-1153. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000281
Wang, H.L., Lu, C.H., Jin, W.L. and Bai, Y. (2011) Effect of External Loads on Chloride Transport in Concrete. Journal of Materials in Civil Engineering, 23, 1043-1049. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000265
Wang, Z.D., Yao, Y. and Wang, L. (2011) Corrosion Behavior of Steel Bar Embedded in Concrete Subject to Freeze-Thaw Cycles-Chloride Attack-Flexural Load. Journal of the Chinese Ceramic Society, 39, 1022-1027.
Jaffer, S. and Hansson, C. (2008) The Influence of Cracks on Chloride-Induced Corrosion of Steel in Ordinary Portland Cement and High Performance Concretes Subjected to Different Loading Conditions. Corrosion Science, 50, 3343-3355. https://doi.org/10.1016/j.corsci.2008.09.018
Jaffer, S.J. and Hansson, C.M. (2009) Chloride-Induced Corrosion Products of Steel in Cracked-Concrete Subjected to Different Loading Conditions. Cement and Concrete Research, 39, 116-125. https://doi.org/10.1016/j.cemconres.2008.11.001