Patterning Technology of Ferrite and Insulating Material in a Single Layer of the Multilayer Ceramic Device
- 1 College of Science and Technology, Nihon University, Chiba, Japan.
- 2 College of Science and Technology, Nihon University, Chiba, Japan.
- 3 College of Science and Technology, Nihon University, Chiba, Japan.
- 4 College of Science and Technology, Nihon University, Chiba, Japan.
- 5 College of Science and Technology, Nihon University, Chiba, Japan.
Abstract
Patterning technology of ferrite and insulating material in multilayer ceramic devices is proposed. In the conventional technology, the different ceramic materials such as the ferrite and the insulating material have been prepared in the form of the each different green sheet, and then they have been stacked each other. Otherwise the different material has filled cavities that were formed by a mechanical punching in advanced. In our proposing technology, arbitrary patterning of the different ceramic material inside the same green sheet is possible. In this process, the arbitrary shape of the through pattern is formed in the green sheet of the base material by making use of photo resist films as sacrifice patterns, and then the base material is masked by the patterned photo resist film. After filling the slurry of the different material into the through pattern of the base material passing the resist mask, the pattern of the different ceramic material in the green sheet is achieved. In the present paper, the ferrite magnetic material and the alumina-glass composite material are used. The patterned structure inside the green sheet is obtained. The slurry preparation, the thickness of the mask resist film, and the obtained structure of the green sheet are discussed.
- A. J. Blodgett, “A Multilayer Ceramic Multi-Chip Module,” IEEE Transaction on Components, Hybrids, and Manufacturing Technology, Vol. 3, No. 4, 1980, pp. 634637. doi:10.1109/TCHMT.1980.1135663
- T. Takahashi and M. Takaya, “Laminated Electronics Parts and Process for Making the Same,” US Patent No. 4322698, 1982.
- Y. Shimada, K. Utsumi, M. Suzuki, H. Takamizawa, M. Nitta and T. Watari, “Low Firing Temperature Multilayer Glass-Ceramic Substrate,” IEEE Transaction on Components, Hybrids, and Manufacturing Technology, Vol. 6, No. 4, 1983, pp. 382-388.doi:10.1109/TCHMT.1983.1136194
- T. Tamura, A. Dohya and T. Inoue, “Combination of Thick-Film Dielectric/Thin Film Conductor for Fine Pattern Formation of Multilayer Substrate,” Electro Component Science and Technology, Vol. 8, No. 3-4, 1981, pp. 235-239. doi:10.1155/APEC.8.235
- H. Mandai, K. Sugoh, K. Tsukamoto, H. Tani and M. Murata, “A Low Temperature Cofired Multilayer Ceramic Substrate Containing Copper Conductors,” Proceedings of the 4th International Microelectronics Conference, Kobe, 28-30 May 1986, pp. 61-64.
- F. Uchikoba and K. Yamashita, “A New Fine Patterning Method for LTCC Electrode Used with Photo-Patterned Dry Film,” Proceedings of the International Conference on Electronics Packaging, Tokyo, 19-21 April 2006, pp. 376-380.
- Y. Akagi, N. Ota, K. Urata and F. Uchikoba, “A Forming Method of Cavity Structure with LTCC Substrate Using Photo Resist Film,” Proceedings of International Conference on Electronics Packaging, Kyoto, 14-16 April 2009, pp. 734739.
- L. Chen, C. His, S. Fu and J. Lin, “Cosintering of NiZn-Cu Ferrite with Low-Temperature Cofired Ceramic Substrate,” Japanese Journal of Applied Physics, Vol. 39, No. 1, 2000, pp.150-154. doi:10.1143/JJAP.39.150
- J. Jao, P. Li and S. Wang, “Characterization of Inductor with Ni-Zn-Cu Ferrite Embedded in B2O3-SiO2 Glass,” Japanese Journal of Applied Physics, Vol. 46, No. 9, 2007, pp. 5792-5796. doi:10.1143/JJAP.46.5792