Using Colloidal Nano Silica to Enhance the Performance of Cementitious Mortars
- 1 Faculty of Engineering, Department of Architectural Engineering, The Pennsylvania State University, Pennsylvania, USA
- 2 Faculty of Engineering, Department of Architectural Engineering, The Pennsylvania State University, Pennsylvania, USA
Abstract
Nanomaterials have been widely used in the past few decades due to their proven capacity to enhance the mechanical properties of materials. While many studies have sought to improve the understanding of how nanomaterials affect the behavior of concrete, additional research is needed in order to achieve the full potential of the material, especially in the presence of supplementary cementitious materials. This study aims to investigate the mechanical properties of cement mortars incorporating both nano-silica (NS) and class F fly ash (FA). Furthermore, mercury intrusion porosimetry (MIP) was performed to study its effect on pore characteristics, and thermogravimetric analysis (TGA) was performed to measure the calcium hydroxide Ca(OH) 2 content in the mixtures. It was found that using nano-silica enhances the compressive strength, reduces the total porosity and accelerates the pozzolanic reaction.
- Sahmaran, M., Yaman, I.O. and Tokyay, M. (2009) Transport and Mechanical Properties of Self Consolidating Concrete with High Volume Fly Ash. Cement and Concrete Composites, 31, 99-106. https://doi.org/10.1016/j.cemconcomp.2008.12.003
- Bentz, D.P., Barrett, T., De, I. and Weiss, W.J. (2012) Relating Compressive Strength to Heat Release in Mortars. Advances in Civil Engineering Materials, 1, 14 p. https://doi.org/10.1520/ACEM20120002
- Lam, L., Wong, Y.L. and Poon, C.S. (2000) Degree of Hydration and Gel/Space Ratio of High-Volume Fly Ash/Cement Systems. Cement and Concrete Research, 30, 747-756. https://doi.org/10.1016/S0008-8846(00)00213-1
- Qing, Y., Zenan, Z., Deyu, K. and Rongshen, C. (2007) Influence of Nano-SiO2 Addition on Properties of Hardened Cement Paste as Compared with Silica Fume. Construction and Building Materials, 21, 539-545. https://doi.org/10.1016/j.conbuildmat.2005.09.001
- Li, H., Xiao, H., Yuan, J. and Ou, J. (2004) Microstructure of Cement Mortar with Nano-Particles. Composites Part B: Engineering, 35, 185-189. | https://doi.org/10.1016/S1359-8368(03)00052-0
- Schoepfer, J. and Maji, A. (2009) An Investigation into the Effect of Silicon Dioxide Particle Size on the Strength of Concrete. Special Publication, 267, 45-58.
- Said, A.M., Zeidan, M.S., Bassuoni, M.T. and Tian, Y. (2012) Properties of Concrete Incorporating Nano-Silica. Construction and Building Materials, 36, 838-844. https://doi.org/10.1016/j.conbuildmat.2012.06.044
- Kong, D., Du, X., Wei, S., Zhang, H., Yang, Y. and Shah, S.P. (2012) Influence of Nano-Silica Agglomeration on Microstructure and Properties of the Hardened Cement-Based Materials. Construction and Building Materials, 37, 707-715. https://doi.org/10.1016/j.conbuildmat.2012.08.006
- ASTM Standard C618 (2017) Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete. ASTM International, West Conshohocken, PA. https://www.astm.org/
- ASTM C109/C109M (2016) Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens). ASTM International, West Conshohocken, PA. https://www.astm.org/
- Pane, I. and Hansen, W. (2005) Investigation of Blended Cement Hydration by Isothermal Calorimetry and Thermal Analysis. Cement and Concrete Research, 35, 1155-1164. https://doi.org/10.1016/j.cemconres.2004.10.027
- Lothenbach, B., Scrivener, K. and Hooton, R.D. (2011) Supplementary Cementitious Materials. Cement and Concrete Research, 41, 1244-1256. https://doi.org/10.1016/j.cemconres.2010.12.001