A zirconium modified MCM-48 mesoporous material was synthesized by surfactant-templated method. Surface grafting Zr-MCM-48 with tungstophosphoric acid led to a great enhancement of both the number of the Br?nsted acid sites and acidity strength in comparison with the bare support. At 100°C, the 30 wt% H 3 PW 12 O 40 /Zr-MCM-48 contained 174 μmol/g Br?nsted acid sites which were 14.5 times greater than that of Zr-MCM-48. The Keggin structure of the grafted heteropolyacid was rather stable after calcination at 400°C for 2 h, approximately 93.3% of Keggin structure in the dispersed heteropolyacid were remained without destruction but slightly distorted in some degree, as evidenced by FTIR characterization and 31 P NMR-MAS analysis. This H 3 PW 12 O 40 /Zr-MCM-48 solid with three dimensional mesoporous system, large surface area and very strong Br?nsted acidity will be a promising catalyst for acid catalytic reactions.
J. S. Beck, J. C. Vartuli, W. J. Roth, M. E. Leonowics, C. T. Kresge, K. D. Schmitt, C. T. –W. Chu, D. H. Olson, E. W. Sheppard, S. B. McCullen, J. B. Higgins and J. L. Schlenker, A new family of mesoporous molecular sieves prepared with liquid crystal templates, J. Am. Chem. Soc. 114 (1992)10834–10843. doi:10.1021/ja00053a020
A. Corma, From Microporous to Mesoporous Molecular Sieve Materials and Their Use in Catalysis, Chem. Rev. 97 (1997) 2373–2420. doi:10.1021/cr960406n
K. M. Reddy, C. Song, From Microporous to Mesoporous Molecular Sieve Materials and Their Use in Catalysis, Catal. Today 31 (1996)137–144. doi:10.1016/0920-5861(96)00030-2
P. Serrano, J. Aguado, J. M. Escola, Catalytic Cracking of a Polyolefin Mixture over Different Acid Solid Catalysts, Ind. Eng. Chem. Res. 39 (2000)1177–1184. doi:10.1021/ie9906363
Ghanbari-Siahkali, A. Philippou, J. Dwyer, M. W. Anderson, The acidity and catalytic activity of heteropoly acid on MCM-41 investigated by MAS NMR, FTIR and catalytic tests, Appl. Catal. A: General 192 (2000) 57-69. doi:10.1016/S0926-860X(99)00333-6
Y. Zhao, S.L. Qiu, Y. Tang, C. Z. Yu (editors), Recent Progress in Mesostuctured Materials, Stud. Surf. Sci. & Catal. Vol. 165 (2007) 1–920.
V. Alfredsson and M. W. Anderson, Structure of MCM-48 Revealed by Transmission Electron Microscopy, Chem. Mater. 8 (1996) 1141–1146. doi:10.1021/cm950568k
Timothy J.V. Yates, John Meurig Thomas, Jose-Jesus Fernandez, Osamu Terasaki, Ryong Ryoo, Paul A. Midgley, Three-dimensional realspace crystallography of MCM-48 mesoporous silica revealed by scanning transmission electron tomography， Chemical Physics Letters 418 (2006) 540–543.
i Man Kim, Seong Kyun Kim and Ryong Ryoo, Synthesis of MCM-48 single crystals，Chem. Commun. (1998) 259–560.
Tingshun Jiang, Duolin Wu, Jiannan Song, Xuping Zhou, Qian Zhao, Meiru Ji, Hengbo Yin, Synthesis and Characterization of Zr- MCM-48 with good thermal and hydrothermal stability, Powder Technology 207 (2011) 422–427. doi:10.1016/j.powtec.2010.11.030
W.C. Zhan, Y.L. Guo, Y.Q. Wang, X.H. Liu, Y. Guo, Y.S. Wang, Z.G, Zhang, G.Z. Lu, Synthesis of Lanthanum–Doped MCM–48 Molecular Sieves and Its Catalytic Performance for the Oxidation of Styrene, The Journal of Physical Chemistry B 111 (42) (2007) 12103–12110. doi:10.1021/jp074521l
Y.F. Shao, L.Z. Wang, J.L. Zhang, M. Anpo, Synthesis of Hydrothermally Stable and Long-Range Ordered Ce–MCM–48 and Fe–MCM–48 Materials, The Journal of Physical Chemistry B 109 (44) (2005) 20835–20841. doi:10.1021/jp054024+
S. Gómez, O. Giraldo, L.J. Garcés, J. Villegas, S.L. Suib, New Synthetic Route for the Incorporation of Manganese Species into the Pores of MCM–48, Chemistry of Materials 16 (2004) 2411–2417.
S. Yuan, L.Y. Shi, K. Mori, H. Yamashita, Synthesis of Ticontaining MCM–48 by using TiF4 as titanium source, Materials Letters 62 (2008) 3028–3030. doi:10.1016/j.matlet.2008.01.100
U.S. Taralkar, P. Kalita, R. Kumar, P.N. Joshi, Synthesis, characterization and catalytic performance of Sn–MCM–48 in solvent–free Mukaiyama–type aldol condensationreactions, Applied Catalysis A: General 358 (2009) 88–94. doi:10.1016/j.apcata.2009.02.001
X.L. Yang, W.L. Dai, R.H. Gao, H. Chen, H.X. Li, Y. Cao, K.N. Fan, Synthesis, characterization and catalytic application of mesoporous W–MCM–48 for the selective oxidation of cyclopentene to glutaraldehyde, Journal of Molecular Catalysis A: Chemical 241 (2005) 205-214. doi:10.1016/j.molcata.2005.07.025
M.L. Pe?a, A. Dejoz, V. Fornés, F. Rey, M. I. Vázquez, J. M. López Nieto, Vcontaining MCM-41 and MCM-48 catalysts for the selective oxidation of propane in gas phase, Applied Catalysis A: General 209 (2001) 155-164. doi:10.1016/S0926-860X(00)00761-4
M. Hartmann, S. Racouchot, C. Bischof, M. Hartmann, S. Racouchot, C. Bischof, Characterization of copper and zinc containing MCM–41 and MCM–48 mesoporous molecular sieves by temperature programmed reduction and carbon monoxide adsorption, Microporous and Mesoporous Materials 27 (1999) 309-320. doi:10.1016/S1387-1811(98)00264-9
M.L. Guzmán-Castillo, H. Armendáriz-Herrera, A. Tobón-Cervantes, D.R. Acosta, P. Salas-Castillo, A. [20] [20] Montoya de la Funte, A. Vázquez-Rodriguez, The effect of sulfate ion on the synthesis and stability of mesoporous materials, Stud. Surf. Sci. Catal. 142 (2002) 1039-1046. doi:10.1016/S0167-2991(02)80261-0
S. Choi, Y. Wang, Z. Nie, J. Liu, C.H.F. Peden, Cssubstituted tungstophosphoric acid salt supported on mesoporous silica, Catal. Today 55 (2000) 117-124. doi:10.1016/S0920-5861(99)00231-X
P. Salas, L. F. Chen, J.A. Wang, H. Armendáriz, M.L. Guzman, J.A. Montoya, D. R. Acosta, Thermal Stability and Surface Acidity of Mesoporous Silica Doubly Doped by Incorporation of Sulfate and Zirconium Ions, Applied Surface Science 252 (2005) 1124-1132. doi:10.1016/j.apsusc.2005.02.032
J. A. Wang, L. F. Chen, L. E. Nore?a, J. Navarrete, M. E. Llanos, J. L. Contreras, O. Novaro. Mesoporous structure, surface acidity and catalytic properties of the Pt/Zr-MCM-41 catalysts promoted by 12-tungstophosphoric acid, Microporous and Mesoporous Materials 112 (2008) 61-76. doi:10.1016/j.micromeso.2007.09.015
C.A. Emeis, Determination of Integrated Molar Extinction Coefficients for Infrared Absorption Bands of Pyridine Adsorbed on Solid Acid Catalysts, J. Catal. 141 (1993) 347-354. doi:10.1006/jcat.1993.1145
T. Barzzetti, E. Selli, D. Moscotti, L. Forni, Pyridine and ammonia as probes for FTIR analysis of solid acid catalysts, J. Chem. Soc. Faraday Trans. 92 (1996) 1401-1407. doi:10.1039/ft9969201401
A.V. Ivanov, T.V. Vasina, V.D. Nissenbaum, L.M. Kustov, M.N. Timofeeva, J.I. Houzvicka, Isomerization of n-hexane on the Pt-promoted Keggin and Dawson tungstophosphoric heteropoly acids supported on zirconia, Appl. Catal. A: Gen. 259 (2004) 65-72. doi:10.1016/j.apcata.2003.09.011
L.R. Pizzio, C.V. Cáceres, M.N. Blanco, Acid catalysts prepared by impregnation of tungstophosphoric acid solutions on different supports, Appl. Catal. A: Gen. 167 (1998) 283-294. doi:10.1016/S0926-860X(97)00328-1
J.C. Edwards, C.Y. Thiel, B. Nenac, J.F. Knifton, Solidstate NMR and FT-IR investigation of 12-tungstophosphoric acid on TiO2, Catal. Lett. 51 (1998) 77-83. doi:10.1023/A:1019045319788
L.F. Chen, J.A. Wang, L.E. Noren, J. Aguilar, J. Navarrete, P. Salas, J.A. Montoya, P. Del Angel, Synthesis and physicochemical properties of Zr-MCM-41 mesoporous molecular sieves and Pt/H3PW12O40/Zr-MCM-41 catalysts, Journal of Solid State Chemistry 180 (2007) 2958-2972.
D. Srinivas, R. Srivastava, P. Ratnasamy, Transesterifications over titanosilicate molecular sieves, Catal. Today 96 (2004) 127-133.
A. Sakthivel, S.E. Dapurkar, N.M. Gupta, S.K. Kulshreshtha, P. Selvam, The influence of aluminium sources on the acidic behaviour as well as on the catalytic activity of mesoporous H-AlMCM-41 molecular sieves, Micropor. Mesopor. Mater. 65 (2003) 177-187. doi:10.1016/j.micromeso.2003.08.004
T. López, J. Navarrete, R. Gómez, O. Novaro, F. Figueras, H. Armentáriz, Preparation of solgel sulfated ZrO2-SiO2 and characterization of its surface acidity, Appl. Catal. 125 (1999) 217-232.
J.A. Anderson, C. Fergusson, I. Rodriguez-Ramos, A. Guerrero-Ruiz, Influence of Si/Zr ratio on the formation of surface acidity in silicazirconia aerogels, J. Catal. 192 (2000) 344-354. doi:10.1006/jcat.2000.2850