Abstract
The design temperature of high plutonium concentration ZPPR fuel plates is 600°C. Cladding integrity of the 304 L stainless steel cladding is a significant concern with this fuel since even small holes can lead to substantial fuel degradation. Since the fuel has a higher coefficient of thermal expansion than the cladding, an investigation of the stress induced in the cladding due to the differential thermal expansion of fuel and cladding up to the design temperature was conducted. Small holes in the cladding envelope would be expected to lead to the fuel hydriding and oxidizing into a powder over a long period of time. This is the same type of chemical reaction chain that exists in the degradation of the high uranium concentration ZPPR fuel. Unfortunately, the uranium fuel was designed with vents which allowed this degradation to occur. The Pu cladding is sealed so only fuel with damaged cladding would be subject to this damage. The thermal stresses that can be developed in the fuel cladding have been calculated in this paper and compared to the ultimate tensile stress of the cladding. The conclusion is drawn that thermal stresses cannot induce holes in the cladding even for the highest storage temperatures predicted in calculations (292°C). In fact, thermal stress cannot cause cladding failure as long as the fuel temperatures are below the design limit of 600°C (1112°F).
- Solbrig, C.W., Krsul, J.R. and Olsen, D.N. (1994) Pyrophoricity of Uranium in Long Term Storage Environments. Proceedings of DOE Spent Nuclear Fuel: Challenges and Initiatives, ANS Topical Meeting, Salt Lake City, 13-16 December 1994, 89-93.
- Solbrig, C.W., Pope, C.L. and Andrus, J.P. (2013) Analysis of Possible Damage of ZPPR Pu Fuel in Storage. ECAR 2121, Idaho National Laboratory, Idaho Falls.
- TEV-1473 (2012) Summary of ZPPR Pu Plate and Pin Inspection and Operation Records. Rev. 0.
- Hecker, S.S. and Stevens, M.F. (2000) Mechanical Behavior of Plutonium and Its Alloys. Los Alamos Science, Los Alamos.
- Till, C.E., Chang, Y.I. and Hannum, W.H. (1997) The Integral Fast Reactor—An Overview. Progress in Nuclear Energy, 31, 3-11. http://dx.doi.org/10.1016/0149-1970(96)00001-7
- Johnson, M.L. (1965) The Description of Fuel and Other Core Materials Procured for SEFOR Critical Experiments in ZPR-III. GEAP 5133, AEC Research and Development Report, General Electric Co., San Jose.
- Steel, A.K. (2007) 304/304l Stainless Steel. Product Data Bulletin.
- PF-1600 (1967) Specification for U-Pu-Mo Alloy ZPPR Fuel Elements. Drawings on Pages 42 to 45 Inclusive, Argonne National Laboratory, Chicago.
- Lawson, A.C., et al. (2004) Invar Model for δ-phase Pu: Thermal Expansion, Elastic, and Magnetic Properties. LA UR 04-6008, Los Alamos National Laboratory, Los Alamos.
- ANL-7471 (1972) Final Safety Analysis Report of the Zero Power Plutonium Facility.
- Klann, R.T., Austin, B.D., Aumeier, S.E. andOlsen, D.N. (2001) Inventory of Special Nuclear Material from the Zero Power Physics Reactor. Argonne National Laboratory-West.
- Anonymous (2013) Engineering Toolbox. http://www.engineeringtoolbox.com/surface-roughness-ventilation-ducts-d_209.html
- Blandford, R.K., Morton, D.K., Snow, S.D. and Rahl, T.E. (2007) Tensile Stress-Strain Results for 304L and 316L Stainless Steel Plate at Temperature. INL/CON-06-11962, ASME Pressure Vessels and Piping Division Conference, July 2007, 1-12.