Development of a LDIE Prediction Theory in the Condition of Magnetite Formation on Secondary Side Piping in Nuclear Power Plants
- 1 Power Engineering Research Institute, Gimcheon, South Korea
- 2 Power Engineering Research Institute, Gimcheon, South Korea
- 3 Power Engineering Research Institute, Gimcheon, South Korea
- 4 Seoul National University, Seoul, South Korea
Abstract
It has been thought that wall thinning on the secondary side piping in nu-clear power plants is mostly caused by Flow-Accelerated Corrosion (FAC). Recently, it has been seen that wall thinning on the secondary side piping carrying two-phase flow is caused by not only FAC but also Liquid Droplet Impingement Erosion (LDIE). Moreover, it turns out that LDIE in nuclear power plants does not result from a single degradation mechanism but also from the simultaneous happenings of LDIE and FAC. This paper presents a comparison of the mass loss rate of the tested materials between carbon steel (A106 B) and low alloy steel (A335 P22) resulting from degradation effect. An experimental facility was set up to develop a prediction model for clarifying multiple degradation mechanisms that occur together. The experimental facility allows examining liquid droplet impingement erosion in the same conditions as the secondary side piping in nuclear power plants by generating the magnetite on the surface of the test materials. The magnetite is formed by controlling the water chemistry and the temperature of fluid inside the facility. In the initial stage of the experiments, the mass loss rate of A106 B was greater than that of A335 P22. However, after a certain period of time, the mass loss rate of A335 P22 became greater than that of A106 B. It is presumed that the results are caused by the different yield strengths of the test materials and the different degrees of buffer action of the magnetite deposited on their surfaces. The layer of magnetite on the surface of A106 is thicker than that of A335 P22, due to the different amount of chrome content. In nuclear power plants, carbon steel piping having experienced wall thinning degradation is generally replaced with low-alloy steel piping. However, the materials of pipes carrying two-phase flow should be selected considering their susceptibility to LDIE.
- Hwang, K.M. and Lee, D.Y. (2012) A Numerical Analysis Study to Identify the Leak Cause of Feedwater Vent Pipe in CANDU Plant. 24th Nuclear Simulation Symposium, Ottawa, 14-16 October 2012.
- Hwang, K.M., Lee, C.G., Bhang, K.J. and Yim, Y.S. (2011) A Study on the Design of a Pipe Affected by Liquid Droplet Impingement Erosion. Journal of Mechanical Sci-ence and Technology, B, 35, 1097-1103.
- Keck, R.G. and Griffith, P. (1987) Prediction and Mitigation of Erosive-Corrosive Wear in Secondary Piping Systems of Nuclear Power Plants. Massachusetts Institute of Technology, NUREG/CR-5007, 1-15.
- Heymann, F.J. (1969) High-Speed Impact between a Liquid Drop and a Solid Surface. Journal of Applied Physics, 40, 5113-5122. https://doi.org/10.1063/1.1657361
- Li, R., Ninokata, H. and Mori, M. (2011) Parametric Investigation on the Effect Factors for Liquid Droplet Impingement Erosion. Proceedings of ASME-JSME-KSME Joint Conference, Hamamatsu, 24-29 July 2011, AJK2011-03034. https://doi.org/10.1115/ajk2011-03034
- Morita, R. and Uchiyama, Y. (2012) Development of a Wall Thinning Rate Model for Liquid Droplet Impingement Erosion. Proceedings of ASME-JSME-KSME Joint Conference, Toronto, 15-19 July 2012, PVP2012-78443.
- Heymann, F.J. (1992) Liquid Impingement Erosion. ASM Handbook, 18, 221-232.
- Field, J.E., Dear, J.P. and Ogren J.E. (1989) The Effects of Target Compliance on Liquid Drop Impact. Journal of Applied Physics, 65, 533-540. https://doi.org/10.1063/1.343136
- ASTM G32-09 (1982) Standard Test Method for Liquid Impingement Erosion Using Rotating Apparatus.
- ASTM E1180-08 (2008) Standard Practice for Preparing Sulfur Prints for Macro-Structural Evaluation.