Study on Corrosion Resistance of N36 Zirconium Alloy in LiOH Aqueous Solution
- 1 Science and Technology on Reactor Fuel and Materials Laboratory, Nuclear Power Institute of China, Chengdu, China
- 2 Science and Technology on Reactor Fuel and Materials Laboratory, Nuclear Power Institute of China, Chengdu, China
- 3 Science and Technology on Reactor Fuel and Materials Laboratory, Nuclear Power Institute of China, Chengdu, China
Abstract
Zr-Sn-Nb-Fe alloys are one of the important directions for continuous improvement of zirconium alloys for high burn-up fuel assemblies. The corrosion resistance of Zr-Sn-Nb-Fe alloys is closely related to the alloying element and water chemical condition. To better understand the effect of Sn on corrosion resistance of Zr-Sn-Nb-Fe alloy, the normal N36 (Zr-1Sn-1Nb-0.3Fe) and low-tin N36 (Zr-0.8Sn-1Nb-0.3Fe) alloy sheets were prepared and tested in static autoclave in both of 0.01 mol/L LiOH and 0.03 mol/L LiOH aqueous solution at 360 ° C and 18.6 MPa. The characteristics of the microstructure and oxide film of alloys were analyzed by TEM and SEM respectively. It was shown that that the corrosion transition of the normal N36 appears earlier and the weight gain is higher than the low-tin N36 in two corrosive mediums. The cracks paralleling to the interface of oxide/metal are formed in the fracture surface of the oxide film and the micrographs at the oxide film/substrate interface appear uneven morphology. With the increasing of corrosion gain, there are more parallel cracks in oxide film and the uneven morphology at the oxide film/substrate interface is more obvious.
- Zhao, W.J., Liu, Y.Z., Jiang, H.M., et al. (2008) Effect of Heat Treatment and Nb and H Contents on the Phase Transformation of N18 and N36 Zirconium Alloys. Journal of Alloys and Compounds, 462, 103-108. https://doi.org/10.1016/j.jallcom.2007.08.047
- Zhang, X., Yao, M.Y., Li, Z.K., et al. (2013) Corrosion Resistance of Zr-0.80Sn-0.4Nb-0.4Fe-0.10Cr-xCu Alloys in Super-Heated Steam at 400°C. Rare Metal Materials and Engineering, 42, 1210-1214.
- Comstock, A.M., Pan, R.J., Garde, G., et al. (2010) Advanced Zirconium Alloys for PWR Application. Journal of ASTM International, 7, 1546.
- Yang, Z.B., Zhao, W.J., Miao, Z., et al. (2015) Corrosion Behavior of Zr-XSn-1Nb-0.3Fe Alloys. Rare Metal Materials and Engineering, 44, 1129-1133.
- Zhang, J.L., Xie, X.F., Yao, M.Y., et al. (2013) Study on the Corrosion Resistance of Zr-1Nb-0.7Sn-0.03Fe-xGe Alloy in Lithiated Water at 360°C. Acta Metallurgica Sinica, 49, 443-450. https://doi.org/10.3724/SP.J.1037.2012.00638
- Park, J.Y., Yoo, S.J., Choi, B.K., et al. (2008) Corrosion and Oxide Characteristics of Zr-1.5Nb-0.4Sn-0.2Fe-0.1Cr Alloy in 360°C Pure Aqueous and LiOH Solution. Journal of Nuclear Materials, 37, 343-350. https://doi.org/10.1016/j.jnucmat.2007.06.015
- Yao, M.Y., Zhou, B.X., Li, Q., et al. (2008) A Superior Corrosion Behavior of Zircaloy-4 in Lithiated Aqueous at 360°C/18.6 MPa by β-Quenching. Journal of Nuclear Materials, 374, 197-203. https://doi.org/10.1016/j.jnucmat.2007.08.002
- Zhang, H.X., Fruchart, D., Hlil, E.K., et al. (2010) Crystal Structure, Corrosion Kinetics of New Zirconium Alloys and Residual Stress Analysis of Oxide Films. Journal of Nuclear Materials, 396, 65-70. https://doi.org/10.1016/j.jnucmat.2009.10.055
- Takeda, K. and Anada, H. (2000) Mechanism of Corrosion Rate Degradation due to Tin. Journal of ASTM International, 5, 592.
- Yilmazbayhan, A., Breval, E., Motta, A.T., et al. (2006) Transmission Electron Microscopy Examination of Oxide Layers Formed on Zr Alloys. Journal of Nuclear Materials, 34, 265-281. https://doi.org/10.1016/j.jnucmat.2005.10.012
- Zhang, J.L., Tu, L.M., Xie, X.F., et al. (2014) Corrosion Resistance of Zr-1Nb-xGe Alloys in Superheated Steam at 400°C. Journal of the Chinese Society of Corrosion and Protection, 34, 171-177.
- Gholinia, G.A., Frankel, P., et al. (2014) The Microstructure and Microtexture of Zirconium Oxide Films Studied by Transmission Electron Backscatter Diffraction and Automated Crystal Orientation Mapping with Transmission Electron Microscopy. Acta Materialia, 80, 159-171. https://doi.org/10.1016/j.actamat.2014.07.062